Chinlon DTY oiling agent with efficient permeability and splashing prevention property and preparation method of oiling agent

A technology of anti-splash agent and manufacturing method, which is applied in textiles, papermaking, fiber processing, etc., can solve the problems of not being able to adapt to the high-speed texturizing process, sticking to the machine table and the ground, and unstable fiber quality, etc. Good spinnability, less broken ends, and high rate of high-quality products

Inactive Publication Date: 2015-10-14
TAICANG LONGFANG OIL CO LTD
View PDF5 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, due to the rapid development of my country's nylon DTY fiber technology, in order to increase production, the speed of nylon DTY fiber texturing continues to increase. The previously used nylon DTY oil can no longer adapt to

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Chinlon DTY oiling agent with efficient permeability and splashing prevention property and preparation method of oiling agent
  • Chinlon DTY oiling agent with efficient permeability and splashing prevention property and preparation method of oiling agent

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A high-permeability, anti-splash nylon DTY oil is mainly composed of emulsifier, bundling agent, antistatic agent, high-efficiency penetrant, anti-splash agent and smoothing agent. The weight percentage of each component is as follows:

[0030] The emulsifier is 6%, which is polyoxyethylene oleate;

[0031] The sizing agent 3% is sorbitan oleate polyoxyethylene ether;

[0032] Antistatic agent 2%, which is dodecanol polyoxyethylene phosphate methyl salt;

[0033] 88% of the smoothing agent is one-time hydrogenated mineral oil;

[0034] High penetration agent 0.5%, dimethyl cyclosiloxane;

[0035] The anti-splashing agent is 0.5%, which is polyisobutylene with a molecular weight of 1.5 million.

Embodiment 2

[0037] A high-permeability, anti-splash nylon DTY oil is mainly composed of emulsifier, bundling agent, antistatic agent, high-efficiency penetrant, anti-splash agent and smoothing agent. The weight percentage of each component is as follows:

[0038] Emulsifier 12%, including polyoxyethylene oleate 5%, castor oil polyoxyethylene ether 2%, trimethylolpropane polyoxyethylene ether 3%, and lauryl polyoxyethylene ether 2%;

[0039] Sizing agent 8%, of which sorbitan oleate polyoxyethylene ether 3%, lauryl lauric acid diethanolamine salt 2%, and laureth polyoxyethylene ether sulfate triethanolamine salt 3%;

[0040] Antistatic agent 5%, of which dodecanol polyoxyethylene phosphate methyl salt 2%, cetyl sulfate methyl salt 2%, and stearyl dihydroxyethyl betaine 1%;

[0041] Smoothing agent 72%, including 50% hydrogenated mineral oil once, 10% national standard mechanical oil, 12% dioctyl sebacate;

[0042] High penetration agent 1.5%, of which dimethylcyclosiloxane 0.5%, hexamethyldisiloxane...

Embodiment 3

[0045] A high-permeability, anti-splash nylon DTY oil is mainly composed of emulsifier, bundling agent, antistatic agent, high-efficiency penetrant, anti-splash agent and smoothing agent. The weight percentage of each component is as follows:

[0046] Emulsifier 8%, of which polyoxyethylene oleate 5%, trimethylolpropane polyoxyethylene ether 3%;

[0047] Binder 6%, of which sorbitan oleate polyoxyethylene ether 4%, lauryl lauric acid diethanolamine salt 2%;

[0048] Antistatic agent 3.5%, of which cetyl sulfate methyl salt 2%, stearyl dihydroxyethyl betaine 1.5%;

[0049] Smoothing agent 80%, including 70% of one-time hydrogenated mineral oil and 10% of national standard mechanical oil;

[0050] High penetration agent 1.5%, including 1% hexamethyldisiloxane and 0.5% low-viscosity dimethicone;

[0051] 1% of anti-splashing agent is polyisobutylene with a molecular weight of 1.5 million.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a chinlon DTY oiling agent with efficient permeability and splashing prevention property. The oiling agent is prepared from the following components according to weight percent: 6-12% of emulsifier, 3-8% of collecting agent, 2-5% of antistatic agent, 0.5-1.5% of efficient penetrant, 0.5-1.5% of splashing prevention agent and 72-88% of smoothing agent. The chinlon DTY oiling agent with efficient permeability and splashing prevention property, provided by the invention, is transparent, steady, and good in spinnability; the surface tension of the oiling agent is small, the spreadability is good, the permeability is strong, and oiling is quick and uniform; intermolecular attraction of the oiling agent is strong, so that the oiling agent cannot be thrown away by a machine running at high speed and splash; since the oiling amount of the fiber surface is ensured, high speed elasticity enhancement is facilitated, and the quality of fiber is guaranteed.

Description

Technical field [0001] The present invention relates to the technical field of nylon DTY fiber processing, and more specifically to a nylon DTY oil agent with high permeability and splash resistance and a manufacturing method thereof. Background technique [0002] At present, due to the rapid development of nylon DTY fiber technology in my country, the speed of nylon DTY fiber texturing is continuously increasing in order to increase production. The previously used nylon DTY oil can no longer adapt to the high-speed texturing process, and it often appears that it is not oiled or oiled. Unevenness or oil on the fiber will often be thrown out by high-speed operation and stick to the machine and the ground, resulting in unstable fiber quality and environmental pollution. Summary of the invention [0003] In view of the above problems in the prior art, the purpose of the present invention is to provide a nylon DTY finish and its manufacturing method that can meet the following requirem...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D06M13/02D06M15/53D06M13/513D06M15/227D06M13/368D06M15/643D06M13/224D06M13/262D06M13/463D06M101/34
CPCD06M13/02D06M13/224D06M13/368D06M13/513D06M15/227D06M15/53D06M15/643
Inventor 赵国良朱坚毅陆蕴菊
Owner TAICANG LONGFANG OIL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap