A Processing Technology of Small Diameter High Pressure Oil Pipe

A high-pressure oil pipe and processing technology, applied in the field of high-pressure oil pipes, can solve the problems of easy fracture and poor toughness, and achieve the effects of strong heat resistance, reduction of strains or cracks, and improvement of cold forming performance.

Active Publication Date: 2016-11-09
ZHANGJIAGANG CITY SHENGDINGYUAN PIPE MAKING
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The seamless steel pipe has a hollow cross-section and is widely used as a pipe for conveying fluids. The seamless steel pipe is made of a steel ingot or a solid tube blank through perforation to make a capillary tube, and then hot-rolled, cold-rolled or cold-drawn. Steel pipes generally use small-diameter high-pressure oil pipes, and they must also withstand high pressure during use. The high-pressure oil pipes used today are generally less than 18mm in outer diameter and more than 4mm in diameter. Most of the existing products have poor toughness and are easy to break

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] A small-diameter high-pressure oil pipe described in this embodiment uses 27SiMn steel as a raw material, and the 27SiMn steel includes the following components in percentage content: C: 0.14%, Si: 0.35%, Mn: 1.42%, P: 0.015% , S: 0.005%, V: 0.06%, Ni: 0.25%, Cr: 0.08%, Nb: 0.5%, the outer diameter of the high-pressure oil pipe is 10mm, and the inner diameter is 4mm.

[0034] The processing technology of a small-diameter high-pressure oil pipe described in this embodiment includes the following steps:

[0035] (1) Select the tube blank, and select the following percentage components C: 0.14%, Si: 0.35%, Mn: 1.42%, P: 0.015%, S: 0.005%, V: 0.06%, Ni: 0.25%, Cr : 0.08%, Nb: 0.5% smelted tube blank made of 27SiMn steel;

[0036] (2) Carry out physical, chemical and mechanical inspection of the tube blank;

[0037] (3) Clean and remove rust after passing the inspection. The cleaning is to use sulfuric acid to clean, the concentration of sulfuric acid solution is controlle...

Embodiment 2

[0055] A small-diameter high-pressure oil pipe described in this embodiment uses 27SiMn steel as a raw material, and the 27SiMn steel includes the following components in percentage content: C: 0.12%, Si: 0.50%, Mn: 1.35%, P: 0.02% , S: 0.01%, V: 0.07%, Ni: 0.12%, Cr: 0.12%, Nb: 0.3%, the outer diameter of the high-pressure oil pipe is 18mm, and the inner diameter is 10mm.

[0056] The processing technology of a small-diameter high-pressure oil pipe described in this embodiment includes the following steps:

[0057] (1) Select the tube blank, and select the following percentage components C: 0.12%, Si: 0.50%, Mn: 1.35%, P: 0.02%, S: 0.01%, V: 0.07%, Ni: 0.12%, Cr : 0.12%, Nb: 0.3% smelted tube blank made of 27SiMn steel;

[0058] (2) Carry out physical, chemical and mechanical inspection of the tube blank;

[0059] (3) Clean and remove rust after passing the inspection. The cleaning is to use sulfuric acid to clean, the concentration of sulfuric acid solution is controlled a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
yield ratioaaaaaaaaaa
elongationaaaaaaaaaa
Login to view more

Abstract

The invention discloses a small-caliber high-pressure oil pipe machining process. 27 SiMn steel is used as a raw material and comprises, 0.12%-0.16% of C, 0.15%-0.50% of Si, 1.35%-1.55% of Mn, less than 0.02% of P, less than 0.01% of S, 0.04%-0.07% of V, 0.12%-0.35% of Ni, 0.05%-0.12% of Cr and 0.3%-0.6% of Nb, the outer diameter of a high-pressure oil pipe is 4-18 mm, and the inner diameter of the high-pressure oil pipe is 1.5-10 mm. The small-caliber high-pressure oil pipe machining process adopts a scientific machining method, precise cold rolling is performed, then annealing, precise cold drawing and normalization are performed to eliminate texture defects, enable texture to be thin and uniform and improve the plasticity and toughness of the steel pipe, a middle-temperature zinc-series phosphating and saponification are adopted, and higher deformation degree and deformation speed can be obtained with smaller pressure. The small-caliber high-pressure oil pipe produced by means of the small-caliber high-pressure oil pipe machining process has higher strength, toughness, plasticity and ductility, all indexes completely meet the requirements, and the oil pipe can bear large pressure, is free of cracks and can meet the oil supply demand of an automobile.

Description

technical field [0001] The invention belongs to the technical field of high-pressure oil pipes, and in particular relates to a processing technology of small-diameter high-pressure oil pipes. Background technique [0002] The seamless steel pipe has a hollow cross-section and is widely used as a pipe for conveying fluids. The seamless steel pipe is made of a steel ingot or a solid tube blank through perforation to make a capillary tube, and then hot-rolled, cold-rolled or cold-drawn. Steel pipes generally use small-diameter high-pressure oil pipes, and they must also withstand high pressure during use. The high-pressure oil pipes used today are generally less than 18mm in outer diameter and more than 4mm in diameter. Most of the existing products have poor toughness and are easy to break. Contents of the invention [0003] In order to solve the above problems, the invention discloses a processing technology of a small-diameter high-pressure oil pipe. The produced high-pres...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/58C22C38/48B21C37/06C21D8/10
Inventor 陈惠明
Owner ZHANGJIAGANG CITY SHENGDINGYUAN PIPE MAKING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap