Normal-temperature impregnating resin for fiber reinforced plastic grids

A technology of impregnating resin and FRP, which is applied in the field of resin impregnating FRP grid at room temperature, which can solve the problems of human injury and volatilization, and achieve the effect of small human injury, high boiling point and safe operation and use

Inactive Publication Date: 2015-11-25
DE RUISEN NANTONG COMPOSITE MATERIAL CO LTD
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Usually, FRP grating is molded by immersing glass fibers in a resin mixture solution, but the heated mixture solution will inevitably volatilize, especially in summer, the volatilized gas of the mixture solution will more or less cause harm to the human body

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0023] The present invention will be further described below in conjunction with embodiment:

[0024] Experimental raw materials:

[0025] 90-100 parts of epoxy resin;

[0026] 30-40 parts of epoxy resin modifier;

[0027] 80-90 parts of room temperature curing agent;

[0028] 5-10 parts of pigment;

[0029] 1-5 parts of release agent.

[0030] Test method: Stir and mix the above materials into the mold, take it out after 40 minutes.

[0031] Heat resistance test: Place the sample in a baking oven, set the temperature at 50°C and 100°C, and bake for 30 minutes respectively.

[0032] Acid resistance test: Place the sample in sulfuric acid for 30 minutes.

[0033] Alkali resistance test: place the sample in sodium hydroxide for 30 minutes.

[0034] Impact resistance test: A 50Kg discus falls freely and impacts downward to observe whether the surface is broken or deformed.

[0035] The experimental data are shown in the table below:

[0036] Table 1

[0037] 　 ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses normal-temperature impregnating resin for fiber reinforced plastic grids. The normal-temperature impregnating resin for the fiber reinforced plastic grids is composed of, by weight, 90-100 parts of epoxy resin, 30-40 parts of epoxy resin modifying agent, 80-90 parts of normal-temperature curing agent, 5-10 parts of pigment and 1-5 parts of release agent. The normal-temperature impregnating resin for the fiber reinforced plastic grids has the advantages of being needless of heating, easy to process, low in toxicity, high in solidifying speed, resistant to corrosion and high temperatures, capable of achieving demolding easily, high in reliability, low in cost and the like.

Description

technical field [0001] The invention relates to a normal-temperature impregnating resin for a glass fiber reinforced plastic grid. Background technique [0002] FRP grating is a reinforced material that uses glass fiber as a matrix and is plasticized by resin. FRP gratings are more and more widely used, so the production and performance of FRP gratings are getting higher and higher. Usually, FRP grating is molded by immersing glass fibers in a resin mixture solution and heating, but the heated mixture solution will inevitably volatilize, especially in summer, the gas volatilized from the mixture solution will more or less cause harm to the human body. Therefore, in practical applications, it is more desirable to reduce the molding temperature of FRP grating to room temperature without affecting the corrosion resistance and heat resistance. Contents of the invention [0003] The purpose of the present invention is to provide a fiberglass grating room temperature impre...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L63/02C08L29/04C08L71/08C08K5/1515C08G59/40
Inventor 周建军
Owner DE RUISEN NANTONG COMPOSITE MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap