Unlock instant, AI-driven research and patent intelligence for your innovation.
A kind of scar sunscreen repair silicone gel and its preparation method
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A silicone gel and scar technology, applied in the field of biomedicine, can solve the problem of high cost, achieve the effect of low cost, short production cycle, and lighten the color
Active Publication Date: 2018-07-17
TIANJIN JIASHITANG SCI & TECH
View PDF5 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
This product works well as a sunscreen for scars, but at a higher cost
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 7
[0032] A preparation method for sunscreen repairing silicone gel for scars, comprising the steps of:
[0033] (1) get each raw material by table 1 embodiment 1;
[0034] (2) Dispersing the antioxidant substance in a solvent, heating in a water bath at 85° C., to dissolve the antioxidant substance, and obtain an antioxidant substance solution;
[0035] (3) Continue heating in a water bath at 85°C, and disperse the sunscreen agent in the antioxidant substance solution under stirring;
[0036] (4) Add the mixture obtained in step (3) into polydimethylsiloxane, stir evenly at a stirring speed of 20 rpm, and obtain a homogeneous system which is a scar sunscreen repair silicone gel.
Embodiment 8
[0038] A preparation method for sunscreen repairing silicone gel for scars, comprising the steps of:
[0039] (1) get each raw material by table 1 embodiment 2;
[0040] (2) Dispersing the antioxidant substance in a solvent, heating in a water bath at 80° C. to dissolve the antioxidant substance, and obtain an antioxidant substance solution;
[0041] (3) Continue heating in a water bath at 80°C, and disperse the sunscreen agent in the antioxidant substance solution under stirring;
[0042] (4) Add the mixture obtained in step (3) into polydimethylsiloxane, stir evenly at a stirring speed of 15 rpm, and obtain a homogeneous system that is a scar sunscreen repairing silicone gel.
Embodiment 9
[0044] A preparation method for sunscreen repairing silicone gel for scars, comprising the steps of:
[0045] (1) get each raw material by table 1 embodiment 3;
[0046] (2) Dispersing the antioxidant substance in a solvent, heating in a water bath at 83° C. to dissolve the antioxidant substance, and obtain an antioxidant substance solution;
[0047] (3) Continue heating in a water bath at 83°C, and disperse the sunscreen in the antioxidant solution under stirring;
[0048] (4) Add the mixture obtained in step (3) into polydimethylsiloxane, stir evenly at a stirring speed of 18 rpm, and obtain a homogeneous system that is a scar sunscreen repairing silicone gel.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
PUM
Login to View More
Abstract
The invention discloses a scar sun-screening and repairing silicon gel and a preparation method thereof. The scar sun-screening and repairing silicon gel is prepared from the following raw materials in percentage by weight: 55-90% of polydimethylsiloxane, 1-20% of a sun-screening agent, 0.2-8% of an antioxidant substance and 2-35% of a solvent. Experiments prove that the scar sun-screening and repairing silicon gel disclosed by the invention is good in sun-screening effect and is capable of inhibiting scar hyperplasia; upon clinical tests, the effective rate of repairing scars after sun exposure is more than 90.00%; the silicon gel is conducive to the protection and repairing of scars under a condition of sun exposure, and the silicon gel is capable of diluting chromatosis and taking a significant effect; and the preparation method disclosed by the invention is simple, short in production cycle, simple in prescription and low in cost.
Description
technical field [0001] The invention belongs to the technical field of biomedicine, and in particular relates to a scar sunscreen repair silicone gel which can achieve better healing effect by sunscreen, moisturizing and anti-oxidation for damaged skin. Background technique [0002] As early as 1983, Perkin et al. added a silicone gel film between the elastic band and the scar to prevent direct friction when using the elastic band to compress the scar, and found that the effect was much better than that of the elastic band alone. Thus uncovered the inhibitory effect of silicone gel on scars and has received extensive attention. [0003] Studies have pointed out that silicone gel has the effect of treating scars because silicone gel can form a layer of silicone gel film after being applied to damaged skin, which can slowly and continuously release silicone oil, and silicone oil helps to separate necrotic tissue , Accelerate the proliferation of granulation tissue and the for...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to View More 
Login to View More