Production formula and process for real stone paint

A production formula and technology of real stone paint, applied in the direction of coating, etc., can solve the problems of incomplete drying, long drying time, hollowing, etc., and achieve the effect of fast drying speed, low cost and simple production process

Inactive Publication Date: 2016-01-06
赵彬
View PDF4 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, ordinary real stone paint takes a long time to dry, and it dries from the surface to the inside. It looks dry on the outside, but the inside is not completely dry. It often appears hollowing in rainy weather.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A production formula and process of real stone paint, the production formula is (parts by weight)

[0019] Bentonite 1, Hydroxyethyl Cellulose 1, Ethylene Glycol 8, Film Forming Aid 6, Regulator ANP-951, Silicone Acrylic Emulsion RC-301140, Thickener 1.5, Preservative 1, Color Sand 700, Water 140.

[0020] In the further optimized technical scheme of the present invention, the colored sand includes (in parts by weight) 80-120 mesh colored sand 340, 40-80 mesh colored sand 180, and 20-40 mesh colored sand 180 .

[0021] In a further optimized technical solution of the present invention, the hydroxyethyl cellulose has a viscosity of 30,000.

[0022] A production formula and process of real stone paint, and its production process is:

[0023] 1) First add water to the mixer according to the above formula ratio;

[0024] 2) Start the mixer, slowly add the hydroxyethyl cellulose and bentonite to the mixer and stir, then add the regulator and continue to stir until a white viscous emul...

Embodiment 2

[0028] A production formula and process of real stone paint, the production formula is (parts by weight)

[0029] Bentonite 1.5, hydroxyethyl cellulose 1.5, ethylene glycol 10, film forming aid 7, regulator ANP-951.5, silicone acrylic emulsion RC-301150, thickener 2.0, preservative 1.5, colored sand (80-120 mesh ) 350, colored sand (40-80 mesh) 200, colored sand (20-40 mesh) 200, water 150.

[0030] Preferably, the hydroxyethyl cellulose has a viscosity of 30,000.

[0031] A production formula and process of real stone paint, and its production process is:

[0032] 1) First add water to the mixer according to the above formula ratio;

[0033] 2) Start the mixer, slowly add the hydroxyethyl cellulose and bentonite to the mixer and stir, then add the regulator and continue to stir until the white viscous emulsion is stirred;

[0034] 3) Add silicone acrylic emulsion, ethylene glycol, film forming aids, preservatives, and colored sand to the white viscous emulsion in sequence, and stir whi...

Embodiment 3

[0037] A production formula and process of real stone paint, the production formula is (parts by weight)

[0038] Bentonite 2, Hydroxyethyl Cellulose 2, Ethylene Glycol 12, Film Forming Aid 8, Regulator ANP-952, Silicone Acrylic Emulsion RC-301160, Thickener 12.5, Preservative 2, Colored Sand 800, Water 1160.

[0039] In this embodiment, the colored sand includes (in parts by weight) colored sand 360 with a particle size of 80-120 mesh, colored sand 220 with a particle size of 40-80 mesh, and colored sand 220 with a particle size of 20-40 mesh.

[0040] Preferably, the hydroxyethyl cellulose has a viscosity of 30,000.

[0041] A production formula and process of real stone paint, and its production process is:

[0042] 1) First add water to the mixer according to the above formula ratio;

[0043] 2) Start the mixer, slowly add the hydroxyethyl cellulose and bentonite to the mixer and stir, then add the regulator and continue to stir until the white viscous emulsion is stirred;

[0044] 3)...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a production formula and process for a real stone paint. The production process comprises the following steps: (1) adding water into a stirring machine according to proportions of the formula at first; (2) starting the stirring machine, slowly adding hydroxyethyl cellulose and bentonite into the stirring machine, stirring, then adding a conditioning agent, and further stirring until white viscous emulsion is stirred out; (3) sequentially adding silicone acrylic emulsion, glycol, a coalescing agent, a preservative and color sand into the white viscous emulsion while stirring; and (4) after stirring the materials in the step (3) uniformly, adding a thickening agent, and stirring uniformly to obtain a finished product. The produced product is relatively strong in cohesive force and relatively high in minimum film forming temperature, thereby fundamentally solving the problems of too soft coating layers and the like; and the product is simple in production process, low in cost and excellent in performance, cannot fall off easily, does not have potential safety hazards, is strong in decorativeness and wide in applicable range, is aqueous and environment-friendly, is good in pollution resistance and long in service life, and is economical and cost-effective.

Description

Technical field [0001] The invention relates to the technical field of building materials, in particular to a production formula and process of real stone paint. Background technique [0002] Real stone paint is mainly made of high molecular polymer, natural colored stone sand and related additives, and it is as hard as stone after drying and curing. Real stone paint has the advantages of fireproof, waterproof, acid and alkali resistance, pollution resistance, non-toxic, odorless, strong adhesion, and never fade. It can effectively prevent the external harsh environment from corroding the building and prolong the life of the building. It has good adhesion and freeze-thaw resistance, so it is especially suitable for use in cold areas. However, ordinary real stone paint takes a long time to dry, and it dries from the surface to the inside. It looks dry on the outside, but the inside is not completely dry. Usually, it will appear empty in rainy weather. Summary of the invention [...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/04C09D7/12
Inventor 赵彬
Owner 赵彬
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com