A modified asphalt, reactive technology, used in textiles and papermaking, building components, building insulation materials, etc., can solve the problems of high price, slow decomposition, and the product price is not close to the people, and achieves long service life, easy construction, and elimination of The effect of fire hazards

Inactive Publication Date: 2016-01-13
卢桂才
View PDF6 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the price of polymethylethoxysilane raw materials is relatively high, resulting in a product price that is not close to the people. The price of the product obtain

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0014] Example 1

[0015] Add 40 parts of No. 70 petroleum pitch to the reactor, add 8 parts of SBS rubber modifier, heat up to 110~115℃, stir for 30min, then heat up to 180~185℃, continue to stir and react for 1h, add 0.5 part of aluminum zirconate Ester waterproof bridging agent, stir for 30min, and cool to 120~130℃ to obtain reactive modified asphalt, which is smeared on non-woven fabric to make waterproof membrane.

Example Embodiment

[0016] Example 2

[0017] Add 60 parts of No. 90 petroleum pitch into the reactor, add 12 parts of SBR rubber modifier, heat up to 115~120℃, stir for 30min, then heat up to 185~190℃, continue to stir and react for 1.5h, add 2 parts of chlorinated Trioctyltin, stirred for 30 minutes, and cooled to 120-130°C, the reactive modified asphalt is obtained, which is smeared on the non-woven fabric to make a waterproof membrane.

Example Embodiment

[0018] Example 3

[0019] Add 66 parts of No. 90 petroleum asphalt into the reactor, add 4 parts of SBS rubber modifier and 12 parts of SBR rubber modifier, heat up to 115~120℃, stir for 30min, then heat up to 185~190℃, continue to stir the reaction Add 3 parts of di-n-butyl ethyl phosphate for 1.5 hours, stir for 30 minutes, and cool to 120-130°C to obtain reactive modified asphalt, which is smeared on the non-woven fabric to make a waterproof membrane.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The present invention aims to provide reactive type modified asphalt and a production method therefor, and particularly relates to reactive viscosity modified asphalt that can perform chemical cross-linking and physical tenon connection with concrete. The reactive type viscosity modified asphalt is prepared by raw materials comprising asphalt, a rubber modifier, and a waterproof bridging agent. The modified asphalt provided by the present invention can be used as an adhesive layer of a waterproof roll or directly used as a waterproof material to build a waterproof bridge, and generates very strong adhesion force with a cement base surface.

Description

technical field [0001] The invention relates to a reactive modified asphalt, which is a modified asphalt capable of chemically reacting with cement concrete to produce chemical crosslinking and physical mortise and tenon effects, and discloses a production method of the modified asphalt. Background technique [0002] Modified asphalt is to add rubber, resin, high molecular polymer, ground rubber powder or other fillers and other external additives (modifiers) to asphalt, or take measures such as mild oxidation of asphalt to make asphalt low temperature It is not easy to be brittle, and it is not easy to flow at high temperature. There are two mechanisms for modifying asphalt, one is to change the chemical composition of asphalt, and the other is to make the modifier evenly distributed in the asphalt to form a certain spatial network structure. The modified asphalt currently on the market mainly includes: 1. Rubber and thermoplastic elastomer modified asphalt: including: nat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L95/00C08L53/02C08L9/06C08L9/00C08L97/00C08K5/10C08K5/57C08K5/521C08K5/098
CPCC08L97/005C08H6/00D06N5/003C08L95/005C08L9/06
Inventor 卢桂才朱方伍伍盛江郭文雄赵晓岚陆善庆
Owner 卢桂才
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap