Preparation method capable of lowering production cost of Nixing ceramics

A technology of production cost and Nixing pottery, which is applied in the field of pottery manufacturing, can solve the problems of restricting the development of Nixing pottery, and achieve the effect of improving the market competitiveness of enterprises, high strength and high porosity

Inactive Publication Date: 2016-02-03
QINZHOU CITY HUAXIA TAIJIQUAN NINGXING POTTERY
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the preparation process of Nixing pottery has been studied in many aspects and some achievements have been made, the research on reducing the production cost by reducing the firing temperature of Nixing pottery is still very limited, which limits the production of Nixing pottery to a large extent. Xingtao's development

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A preparation method for reducing the production cost of Nixing pottery, comprising the steps of:

[0028] 1) Preparation of blank: The blank is made of the following raw materials in proportion by weight: 52 parts of Dongni, 32 parts of Ximu, 1.5 parts of bentonite, 2 parts of wollastonite, 0.7 part of red clay, 0.3 part of powdered quartz, alumina 2 parts, and use ball mill to mix: first, according to the above raw materials: zirconia ball: water = 1:4:2, add in the ratio, ball mill for 8 hours; secondly, pass through a 60-mesh sieve, and dry; then according to the dried raw material: oxidation Zirconium balls: add water in a ratio of 1:3:2, ball mill for 11 hours; then pass through a 120-mesh sieve; finally pass through sedimentation, pressure filtration, vacuum mud refining, and get the billet after aging;

[0029] 2) Body forming: making the blank into a flowerpot body;

[0030] 3) Body trimming: trim the flowerpot body to meet the design requirements;

[0031] 4...

Embodiment 2

[0036] A preparation method for reducing the production cost of Nixing pottery, comprising the steps of:

[0037] 1) Preparation of blank: The blank is made of the following raw materials in proportion by weight: 45 parts of Dongni, 25 parts of Ximu, 1 part of bentonite, 1 part of wollastonite, 0.6 part of red clay, 0.2 part of powdered quartz, alumina 1 part, and use ball mill to mix: first, according to the above raw materials: zirconia ball: water = 1:4:2, add in the ratio, ball mill for 7 hours; secondly pass through a 50-mesh sieve, and dry; then according to the dried raw material: oxidation Zirconium balls: add water in a ratio of 1:3:2, ball mill for 10 hours; then pass through a 110-mesh sieve; finally pass through precipitation, pressure filtration, vacuum mud refining, and get the billet after aging;

[0038] 2) Body forming: making the blank into a flowerpot body;

[0039] 3) Body trimming: trim the flowerpot body to meet the design requirements;

[0040] 4) Drying...

Embodiment 3

[0045] A preparation method for reducing the production cost of Nixing pottery, comprising the steps of:

[0046] 1) Preparation of blank: The blank is made of the following raw materials in proportion by weight: 60 parts of Dongni, 40 parts of Ximu, 2 parts of bentonite, 3 parts of wollastonite, 0.8 part of red clay, 0.4 part of powdered quartz, alumina 3 parts, and use ball mill to mix: first, according to the above raw materials: zirconia ball: water = 1:4:2, add in the ratio, ball mill for 9 hours; secondly, pass through a 70-mesh sieve, and dry; then according to the dried raw material: oxidation Zirconium balls: add water at a ratio of 1:3:2, ball mill for 12 hours; then pass through a 130-mesh sieve; finally pass through precipitation, pressure filtration, vacuum mud refining, and get the billet after aging;

[0047] 2) Body forming: making the blank into a flowerpot body;

[0048] 3) Body trimming: trim the flowerpot body to meet the design requirements;

[0049] 4) ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method capable of lowering the production cost of Nixing ceramics. A blank is prepared from the following raw materials in parts by weight: 45-60 parts of east clay, 25-50 parts of west clay, 1-2 parts of bentonite, 1-3 parts of wollastonite, 0.6-0.8 part of red clay, 0.2-0.4 part of konilite and 1-3 parts of aluminum oxide. The preparation method comprises the following steps: sintering: (a) heating to 75-90 DEG C at a speed of 35 DEG C / h-50 DEG C / h, and maintaining the temperature for 6-8 hours; (b) heating to 125-140 DEG C at a speed of 45 DEG C / h-60 DEG C / h, and maintaining the temperature for 2-4 hours; (c) heating to 500-550 DEG C at a speed of 65 DEG C / h-80 DEG C / h, and maintaining the temperature for 0.2-0.4 hour; (d) heating to 800-850 DEG C at a speed of 65 DEG C / h-80 DEG C / h, and maintaining the temperature for 0.1-0.3 hour; and (e) heating to 1020-1040 DEG C at a speed of 85 DEG C / h-100 DEG C / h, and maintaining the temperature for 0.6-0.8 hour.

Description

technical field [0001] The invention relates to a preparation method for reducing the production cost of Nixing pottery, belonging to the technical field of pottery manufacture. Background technique [0002] Nixing pottery, scientific name Zini pottery, is a pottery with a long history and Qinzhou characteristics. It is also known as the four famous pottery in China together with Yixing pottery in Jiangsu, Jianshui pottery in Yunnan, and Rongchang pottery in Sichuan. The biggest feature of Nixing pottery in Qinzhou is its non-glazed finish. The burnt and polished pottery presents an endless variety of "kiln-changing" colors. The artistic taste is extremely high, and it is known as "a must in China". [0003] Although Nixing pottery is well-known overseas, its development is slow compared to the development of my country's pottery industry. This is because Nixing pottery is mainly based on ornamental and collection value to expand the market, and it is difficult to form a lar...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B33/13C04B33/32C04B33/34
Inventor 黄涛默
Owner QINZHOU CITY HUAXIA TAIJIQUAN NINGXING POTTERY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com