Nail polish containing aloe extracts

A technology of aloe vera extract and nail polish, applied in manicure, skin care preparations, medical preparations containing active ingredients, etc., can solve the problems of low odor, high nail and skin irritation, solubility corrosion, etc., to achieve Improved bonding strength and stability, good moisturizing effect, and less irritating effect

Inactive Publication Date: 2016-04-06
JINAN HAOZE ENVIRONMENTAL PROTECTION TECH CO LTD
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But the disadvantages that exist are: 1. It has a pungent smell, and the strong pungent smell will cause physical discomfort after being inhaled; 2. It is more irritating to the nails and skin of the human body after use, and it will cause greater damage if used for a long time; 3. Contact with chemical fiber clothing and general plastics will cause soluble corrosion
This type of formula can be properly formulated to obtain low-odor, low-irritation, high-gloss nail polish that does not dissolve and corrode chemical fiber clothing and plastics. The focus is not good, and there is a big gap compared with ester solvent-based nail polish; 3. The surface of the nail polish will stick back after drying

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] A nail polish added with aloe extract, comprising the following components in parts by weight:

[0048] 10 parts of aloe vera extract;

[0049] 20 parts of acrylic acid copolymer;

[0050] 10 parts of alcohol solvent;

[0051] 5 parts of alcohol solvent film-forming agent;

[0052] 0.5 parts of dispersant;

[0053] 0.1 part of defoamer;

[0054] 2 parts sunscreen

[0055] 0.3 part of antibacterial agent;

[0056] 1 part of paint.

[0057] The acrylic copolymer is a mixture of acrylate monomer copolymer and acrylic acid-acrylate copolymer.

[0058] The alcoholic solvent is isobutanol.

[0059] The alcohol solvent film former is a mixture of alkyd resin and polyvinyl alcohol.

[0060] The antibacterial agent is a mixture of polyene derivatives, acidic compounds and morpholine derivatives.

[0061] The sunscreen is a mixture of 2-phenylbenzimidazole-5-sulfonic acid and octyl methoxycinnamate.

[0062] The defoamer is a high-carbon alcohol fatty acid ester compou...

Embodiment 2

[0064] A nail polish added with aloe extract, comprising the following components in parts by weight:

[0065] 30 parts of aloe extract;

[0066] 40 parts of acrylic acid copolymer;

[0067] 15 parts of alcohol solvent;

[0068] 8 parts of alcohol solvent film former;

[0069] 0.8 parts of dispersant;

[0070] 0.5 part of defoamer;

[0071] 0.6 part of antibacterial agent;

[0072] 4 parts of paint.

[0073]The acrylic acid copolymer is an acrylic acid-acrylate copolymer.

[0074] The alcohol solvent is a mixture of glycerol and isobutanol.

[0075] The alcohol solvent film former is a mixture of polyamide resin, polyvinyl alcohol and nitrocellulose.

[0076] The antibacterial agent is a mixture of polyene derivatives and acidic compounds.

[0077] The sunscreen is a mixture of ethylhexyl salicylate and 2-phenylbenzimidazole-5-sulfonic acid.

[0078] The defoamer is emulsified silicone oil.

Embodiment 3

[0080] A nail polish added with aloe extract, comprising the following components in parts by weight:

[0081] 20 parts of aloe extract;

[0082] 30 parts of acrylic acid copolymer;

[0083] 20 parts of alcohol solvent;

[0084] 10 parts of alcohol solvent film former;

[0085] 1 part of dispersant;

[0086] 0.3 part of defoamer;

[0087] 1 part sunscreen

[0088] 0.8 part of antibacterial agent;

[0089] 2 parts of paint.

[0090] The acrylic acid copolymer is a mixture of acrylic acid and acrylic acid-acrylate copolymers.

[0091] The alcohol solvent is a mixture of glycerol and isobutanol.

[0092] The alcohol solvent film former is a mixture of polyamide resin, polyvinyl alcohol and nitrocellulose.

[0093] The antibacterial agent is a mixture of polyene derivatives, acidic compounds and morpholine derivatives.

[0094] The sunscreen is a mixture of ethylhexyl salicylate, 2-phenylbenzimidazole-5-sulfonic acid and octyl methoxycinnamate.

[0095] The defoamer is ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a nail polish containing aloe extracts. The nail polish is prepared from, by weight, 30 parts of aloe extracts, 40 parts of polyacrylic copolymer, 15 parts of alcohols solvent, 8 parts of alcohol solvent film-forming agent, 0.8 part of dispersing agent, 0.5 part of antifoaming agent, 0.6 part of antibacterial agent and 4 parts of pigment. The nail polish has the advantages that by adding the polyacrylic copolymer, the bonding strength and stability of an adhesive are improved; by adding the aloe extracts, sterilization and inflammation diminishing are achieved; aloe has a light taste, so that the irritation of the nail polish is small; after the aloe extracts are added, the moistening effect of the nail polish is good, glossiness is improved, and the effect is durable.

Description

technical field [0001] The invention relates to the technical field of cosmetics, in particular to a nail polish added with aloe extract. Background technique [0002] Nail polish belongs to a large category of products in the color cosmetic series, which has the function of beautifying and modifying nails. At present, the nail polishes used by people are divided into ester solvent-based nail polish and water-based nail polish. [0003] Ester solvent-based nail polish uses ethyl acetate, butyl acetate and other esters as solvents, ester-soluble film-forming agents, steralnium chloride hectorite and hydrated silica as thickening suspending agents, together with plasticizers and pigments It is made by stirring and mixing with additives such as essence. This type of formulation can be properly formulated to obtain nail polishes with high gloss, strong adhesion and strong water resistance. But the disadvantages that exist are: 1. It has a pungent smell, and the strong pungent ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): A61K8/97A61K8/81A61Q3/02A61Q17/00
CPCA61K8/34A61K8/8147A61K8/8152A61K8/97A61K2800/596A61Q3/02A61Q17/005
Inventor 冉德焕
Owner JINAN HAOZE ENVIRONMENTAL PROTECTION TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com