Low-emission high-performance long glass fiber reinforced PP composite and preparation method thereof

A composite material and long glass fiber technology, which is applied in the field of materials, can solve the problems of reduced impact resistance, less addition, and affecting the performance of composite materials.

Inactive Publication Date: 2016-04-06
HUIZHOU CHANGYI TECH
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

These additives are often added in small amounts and are generally solid. Their use will seriously affect the performance of composite materials and reduce their impact resistance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] This embodiment provides a kind of low emission, high-performance long glass fiber reinforced PP composite material, and its raw material comprises by weight:

[0025] 35 parts of long glass fiber;

[0026] PP85 copies

[0027] 0.9 parts of compatibilizer;

[0028] 0.4 part of antioxidant;

[0029] 2 parts of flame retardant;

[0030] The raw materials of the compatibilizer include 6 parts by weight of hydroxyethyl cellulose, 0.2 part of propylene glycol, 0.04 part of magnesium chlorate, and 6 parts of potassium nitrate.

[0031] The long glass fiber is an alkali-free continuous glass fiber with a length of 10 mm and a diameter of 13 μm.

[0032] In the present embodiment, its preparation method of the long glass fiber is:

[0033] (1) Soaking treatment in n-heptane: immerse the long glass fiber in n-heptane for swelling treatment, the treatment time is 20h;

[0034] (2) Washing with acetone: Wash the swollen long glass fiber with ultrasonic vibration, and then dr...

Embodiment 2

[0041] This embodiment provides a kind of low emission, high-performance long glass fiber reinforced PP composite material, and its raw material comprises by weight:

[0042] 40 parts of long glass fiber;

[0043] PP80 copies

[0044] 2 parts of compatibilizer;

[0045] Antioxidant 0.1 part;

[0046] 3 parts of flame retardant;

[0047] The raw materials of the compatibilizer include 5 parts by weight of hydroxyethyl cellulose, 0.5 part of propylene glycol, 0.01 part of magnesium chlorate, and 8 parts of potassium nitrate.

[0048] The long glass fiber is an alkali-free continuous glass fiber, and the diameter of the alkali-free continuous glass fiber is 20 μm.

[0049] The composite material of this embodiment is prepared into a plate-shaped part of 1000mm×1000mm×20mm by using the rapid prototyping material of the prior art, and its performance is tested by using the ASTM standard, and the results are shown in Table 2.

[0050] Table 2.

[0051] project

Embodiment 3

[0053] This embodiment provides a kind of low emission, high-performance long glass fiber reinforced PP composite material, and its raw material comprises by weight:

[0054] 30 parts of long glass fiber;

[0055] PP90 copies

[0056] 0.3 parts of compatibilizer;

[0057] 0.7 part of antioxidant;

[0058] 1 part of flame retardant;

[0059]The raw materials of the compatibilizer include 7 parts by weight of hydroxyethyl cellulose, 0.1 part of propylene glycol, 0.07 parts of magnesium chlorate, and 3 parts of potassium nitrate.

[0060] The composite material of this embodiment is prepared into a 1000mm×1000mm×20mm plate-shaped part using the rapid prototyping material of the prior art, and its performance is tested using ASTM standards, and the results are shown in Table 3.

[0061] table 3.

[0062] project

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Lengthaaaaaaaaaa
Diameteraaaaaaaaaa
Tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a low-emission high-performance long glass fiber reinforced PP composite and a preparation method thereof. Magnesium chlorate, potassium nitrate and propylene glycol are selected and synergistically interacted, the emission of the long glass fiber reinforced PP composite is effectively reduced, micromolecules of a product prepared from the long glass fiber reinforced PP composite are not prone to emitting due to the luminous effect and thermal effect, the stability of the composite is maintained, and meanwhile the mechanical property of the prepared PP composite can be effectively maintained. The PP composite has the excellent impact resistant property and low-emission property, the surface is smooth and free of floating fiber, and the PP composite is specially suitable for preparing products such as automobile parts, electronic product elements, instrument parts and aeronautical equipment parts.

Description

technical field [0001] The invention relates to the technical field of materials, in particular to a low-emission, high-performance long glass fiber reinforced PP composite material and a preparation method thereof. Background technique [0002] Long glass fiber reinforced PP composite materials have the characteristics of light weight, high strength, good impact resistance, and good dimensional stability. They can be used to replace traditional reinforced engineering plastics and even metal materials such as steel in practical applications. In recent years, with the progress of automobile lightweight, long glass fiber reinforced PP composite materials are more and more widely used in the automobile industry as the main material for replacing steel with plastic due to their cost-effective advantages. Long glass fiber reinforced polypropylene materials are used The performance of making auto parts is equivalent to that of steel parts, but the weight is reduced by 40% or more,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L23/12C08L1/28C08K13/06C08K9/04C08K7/14C08K5/053C08K3/24C08K3/28
CPCC08L23/12C08K2201/003
Inventor 杜崇铭林湖彬刘勋
Owner HUIZHOU CHANGYI TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com