High-strength-toughness and high-temperature hot rolled steel plate and preparation method thereof

A high-strength toughness, hot-rolled steel plate technology, applied in the field of steel products, can solve the problems that the matrix structure of hot-rolled steel plates cannot be directly refined, and achieve the effect of flexible cooling process requirements, small grain size, and high strength

Inactive Publication Date: 2016-04-27
NORTHEASTERN UNIV
View PDF19 Cites 24 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition, the uniform distribution of fine inclusions formed by Ti or composite deoxidation with other elements in the steel also has the ability to promote the formation of intragranular ferrite, but the existing technology usually uses such inclusions to improve the welding heat-affected zone. However, the matrix structure of the hot-rolled steel plate cannot be directly refined, and the traditional controlled rolling, controlled cooling and heat treatment processes are still required to improve the properties of the steel plate

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-strength-toughness and high-temperature hot rolled steel plate and preparation method thereof
  • High-strength-toughness and high-temperature hot rolled steel plate and preparation method thereof
  • High-strength-toughness and high-temperature hot rolled steel plate and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0022] The chemical composition of the high-strength toughness high-temperature hot-rolled steel sheet of the present invention includes: C0.04-0.15%, Si0.05-0.35%, Mn0.5-2.5%, Ti0.005-0.025%, Cr≤1.0 %, Mo≤0.5%, Ni≤1.0%, Cu≤0.5%, B≤0.003%, P≤0.02%, S≤0.01%, N≤0.007%, O0.001-0.006%, Al, Zr, Mg, The total content of Ca and rare earth elements is ≤0.03%, and the balance is Fe and unavoidable impurity elements.

[0023]The content of C, Si, and Mn elements in the composition of the steel plate of the present invention is the same as that of conventional low-carbon low-alloy high-strength steel, and no special adjustment is required, so the content ranges are respectively C0.04-0.15%, Si0.05-0.35%, Mn0 .5-2.5%. Since Ti is used for final deoxidation, and fine inclusions rich in titanium oxide are required to promote the formation of intragranular ferrite during post-rolling cooling, a certain amount of inclusions is required in the steel, that is, a certain amount of titanium and ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
yield strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-strength-toughness and high-temperature hot rolled steel plate and a preparation method thereof. The high-strength-toughness and high-temperature hot rolled steel plate is prepared from the following chemical components in percentage by weight: 0.04-0.15 percent of C, 0.05-0.35 percent of Si, 0.5-2.5 percent of Mn, 0.005-0.025 percent of Ti, smaller than or equal to 1.0 percent of Cr, smaller than or equal to 0.5 percent of Mo, smaller than or equal to 1.0 percent of Ni, smaller than or equal to 0.5 percent of Cu, smaller than or equal to 0.003 percent of B, smaller than or equal to 0.02 percent of P, smaller than or equal to 0.01 percent of S, smaller than or equal to 0.007 percent of N, 0.001-0.006 percent of O, smaller than or equal to 0.03 percent of the total content of elements including Al, Zr, Mg, Ca and rare earth and the balance of Fe and inevitable impurity elements. The preparation method of the steel plate comprises the following steps: smelting and casting according to the components, carrying out high-temperature continuous rolling by adopting an austenite, carrying out accelerated cooling by watering the steel plate after being rolled, and then air cooling to room temperature, wherein the heating temperature of a steel billet is 1150-1260 DEG, the cooling temperature is larger than or equal to 5 DEG C / s. and the finish cooling temperature is 550-650 DEG C . As a microscopic structure of the steel plate is a fined acicular ferrite type structure, the steel plate is good in strength and toughness properties. The preparation method of the steel plate is flexible in process and simple in operation, saves the cost and improves the production efficiency.

Description

technical field [0001] The invention relates to the technical field of steel products, in particular to a high-strength toughness high-temperature hot-rolled steel plate and a preparation method thereof. Background technique [0002] Controlled rolling and controlled cooling technology is an important means to improve the comprehensive mechanical properties of hot-rolled steel. The traditional controlled rolling process includes two-stage rolling in the austenite recrystallization zone and non-recrystallization zone. First, through the rolling deformation in the recrystallization zone, the coarsened austenite grains are repeatedly recrystallized during the heating process and the size is refined, and then enter the austenite non-recrystallization zone when the temperature is high, and after sufficient deformation accumulation, the austenite is effective The grain size is significantly refined and the work-hardened state is maintained. Therefore, in the subsequent controlle...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/04C22C38/14C22C38/02C22C38/18C22C38/16C22C38/12C22C38/08C21D8/02
CPCC22C38/04C21D8/0226C21D2211/005C22C38/005C22C38/02C22C38/08C22C38/12C22C38/14C22C38/16C22C38/18
Inventor 王超王昭东王国栋
Owner NORTHEASTERN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products