A kind of alumina ceramics, processing technology, applied in chemical instruments and methods, cleaning methods and utensils, cleaning methods using liquids, etc. Firmness and other problems, to achieve the effect of strong surface adsorption, light weight, and prolong the service life of the equipment

Inactive Publication Date: 2016-05-04
孙英
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The hardness of the ceramic patch is ≥ HRA85, second only to the hardness of diamond, and the surface is smooth, the friction coefficient is small, and the wear resistance is very ideal, especially in the high temperature oxidizing medium or corrosive medium, the material of the ceramic patch has better performance than other metal materials. It is much superior. Ordinary ceramic sheets and rubber cannot be bonded together. After using glue, the bond is not firm, and the ceramic sheets need to be processed.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A process for treating alumina ceramic sheets, the steps are as follows:

[0023] (1) Cleaning with distilled water: Place the ceramic piece in 100% pure water for cleaning and drying;

[0024] (2) Ketone washing: Soak the cleaned ceramic sheet in 80% acetone for half an hour and dry it;

[0025] (3) Alkaline cleaning: Soak the ketone-washed ceramic sheet in 10% sodium carbonate solution for half an hour and dry it.

Embodiment 2

[0027] A process for treating alumina ceramic sheets, the steps are as follows:

[0028] (1) Cleaning with distilled water: Place the ceramic piece in 100% pure water for cleaning and drying;

[0029] (2) Ketone washing: Soak the cleaned ceramic sheet in 85% acetone for half an hour and dry it;

[0030] (3) Alkaline cleaning: Soak the ketone-washed ceramic sheet in 15% sodium carbonate solution for half an hour and dry it.

Embodiment 3

[0032] A process for treating alumina ceramic sheets, the steps are as follows:

[0033] (1) Cleaning with distilled water: Place the ceramic piece in 100% pure water for cleaning and drying;

[0034] (2) Ketone washing: Soak the cleaned ceramic sheet in 90% acetone for half an hour and dry it;

[0035] (3) Alkaline cleaning: Soak the ketone-washed ceramic sheet in 20% sodium carbonate solution for half an hour and dry it.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

A treatment process of alumina ceramic wafers comprises the following steps of (1) washing with distilled water: washing ceramic wafers with 100% pure water, and drying; (2) washing with acetone: soaking the washed ceramic wafers in 80-90% acetone, and drying; (3) alkali washing: soaking the ceramic wafers washed with the acetone in 10-20% sodium carbonate solution, and drying. The treatment process of the alumina ceramic wafers has the beneficial effects of being large in hardness, excellent in wear resistance, light in weight, strong in surface adhesive force (10-20 times of that of the untreated ceramic wafers), and firm and durable after being combined with rubber through glue.

Description

technical field [0001] The invention relates to the technical field of alumina ceramic sheet processing, in particular to an alumina ceramic sheet processing process. Background technique [0002] Alumina ceramics: high alumina content, relatively dense structure, and special properties, so it is called special ceramics. Al2O3. The ceramic material is a close-packed hexagonal structure composed of oxygen ions, and aluminum ions fill two-thirds of the octahedral gaps. This is the same stable α-Al2O3 structure as natural corundum, so the ceramic has a high melting point and high Hardness, with excellent wear resistance. The hardness of the ceramic patch is ≥ HRA85, second only to the hardness of diamond, and the surface is smooth, the friction coefficient is small, and the wear resistance is very ideal, especially in the high temperature oxidizing medium or corrosive medium, the material of the ceramic patch has better performance than other metal materials. It is much super...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B41/80B08B3/04B08B3/08
CPCC04B41/00B08B3/04B08B3/08C04B41/009C04B41/80C04B35/10
Inventor 孙英
Owner 孙英
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap