Extrusion type lamination process for preparing composite film

A composite process and composite film technology, applied in the direction of lamination device, lamination auxiliary operation, lamination, etc., can solve the problem of low fastness of composite film, improve the coloring effect, shorten the time used, and strengthen the firmness. Effect

Inactive Publication Date: 2016-05-18
SICHUAN HUILI IND
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the present invention is to provide an extrusion compounding process for preparing a composite film, so as to solve the problem that the existing composite film preparation process easily leads to low fastness of the composite film

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] The extrusion composite process for preparing composite film comprises the following steps:

[0037] 1) Preparation of film: Mix the raw materials for film preparation in proportion and then make film by blowing film, pressing film and trimming;

[0038] 2) Extrusion compounding: the film A is coated with adhesive under the action of the pressure roller, dried and solidified, the thermoplastic is melted in the extruder, and flows out in the form of a film from the flat die, and is placed on the rubber roller The film-like material that is continuously conveyed between the cooling metal roller and the film A and film B is pressed and solidified to form a composite film; the adhesive is composed of the following components in weight percentage: 40% solid content, and the balance is deionized water, the adhesive is an isocyanate adhesive; the drying temperature is 160°C; the curing temperature is 60°C;

[0039] 3) Printing of the composite film: the composite film is prin...

Embodiment 2

[0047] The extrusion composite process for preparing composite film comprises the following steps:

[0048] 1) Preparation of film: Mix the raw materials for film preparation in proportion and then make film by blowing film, pressing film and trimming;

[0049] 2) Extrusion compounding: the film A is coated with adhesive under the action of the pressure roller, dried and solidified, the thermoplastic is melted in the extruder, and flows out in the form of a film from the flat die, and is placed on the rubber roller The film-like material that is continuously conveyed between the cooling metal roller and the film A and film B is pressed and solidified to form a composite film; the adhesive is composed of the following components in weight percentage: 50% solid content, and the balance is deionized water, the adhesive is an isocyanate adhesive; the drying temperature is 200°C; the curing temperature is 100°C;

[0050] 3) Printing of the composite film: the composite film is pri...

Embodiment 3

[0058] The extrusion composite process for preparing composite film comprises the following steps:

[0059] 1) Preparation of film: Mix the raw materials for film preparation in proportion and then make film by blowing film, pressing film and trimming;

[0060] 2) Extrusion compounding: the film A is coated with adhesive under the action of the pressure roller, dried and solidified, the thermoplastic is melted in the extruder, and flows out in the form of a film from the flat die, and is placed on the rubber roller The film-like material continuously conveyed between the cooling metal roller and the film A and film B is pressed and solidified to form a composite film; the adhesive is composed of the following components in weight percentage: 45% solid content, and the balance is deionized water, the adhesive is an isocyanate adhesive; the drying temperature is 180°C; the curing temperature is 80°C;

[0061] 3) Printing of the composite film: the composite film is printed with p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an extrusion type lamination process for preparing a composite film, which comprises the following steps of: (1) film preparation; (2) dry lamination: coating a film A with an adhesive under the action of a roller, drying, curing, and forming a composite film with a film B under the action of the roller; (3) composite film printing: printing print ink on the composite film through a printing machine; (4) irradiating the print ink with ultraviolet rays emitted by a first group of ultraviolet lamps of the printing machine to have crosslinking reaction between the print ink and a printing layer; (5) irradiating the print ink with ultraviolet rays emitted by a second group of ultraviolet lamps of the printing machine to cure the printing layer on the composite film; (6) drying the printing layer with an infrared ray dryer arranged on the printing machine; and (7) carrying out UV glazing on the dried printing layer with an UV glazing device arranged on the printing machine. By adopting the extrusion type lamination process, the problem that the composite film prepared by adopting the existing composite film preparation process is low in fastness is solved.

Description

technical field [0001] The invention relates to the technical field of pharmaceutical packaging, in particular to an extrusion composite process for preparing composite films. Background technique [0002] In the pharmaceutical industry, it involves packaging the prepared medicines. The packaging mainly includes bags and aluminum foil boards. No matter what kind of packaging is used, it involves the preparation of composite films and the printing process. [0003] The preparation of the composite film is to compound and solidify the single-layer film through the printing process and then through the dry composite process or the extrusion composite process to form a composite film. [0004] The printing process is to print some product information on the composite film used for packaging to facilitate the identification and use of pharmaceuticals. The equipment used in the printing process mainly includes the printing machine, the winding device, and the ink that cooperates ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B32B37/15B32B38/00B32B38/16B32B37/10B32B37/08B32B38/14
CPCB32B37/153B32B37/08B32B37/10B32B38/00B32B38/14B32B38/145B32B38/164B32B2038/0076
Inventor 彭启源肖世才
Owner SICHUAN HUILI IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com