Anti-glare film

A technology of anti-glare film and anti-glare layer, which is applied in the direction of optics, instruments, optical components, etc., can solve the problems of anti-glare performance reduction, and achieve excellent anti-glare performance, suppress whitening and glare effects

Inactive Publication Date: 2016-05-25
SUMITOMO CHEM CO LTD
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, for the anti-glare film disclosed in Patent Document 1, if the haze is further reduced (reduced haze), there is a possibility that when the display surface of the image display device on which the anti-glare film is arranged is viewed from an oblique direction, reduced anti-glare
Therefore, the antiglare film disclosed in Patent Document 1 still has room for improvement in terms of antiglare properties at wide viewing angles.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anti-glare film
  • Anti-glare film
  • Anti-glare film

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0228] (Preparation of molds for anti-glare film production)

[0229] A material obtained by performing ballard copper plating on the surface of an aluminum roll (A6063 based on JIS) with a diameter of 200 mm was prepared. Ballard copper plating includes copper plating / thin silver plating / surface copper plating, and the overall thickness of the plating is set to about 200 μm. The copper-plated surface was mirror-polished, and a photosensitive resin was applied and dried on the polished copper-plated surface to form a photosensitive resin film. Next, using the laser will be Figure 9 The pattern in which the pattern A shown above was repeatedly arranged was exposed on the photosensitive resin film, and it developed. Exposure and development were performed by laser using Laser Stream FX (manufactured by Think Laboratory). As the photosensitive resin film, a resin film containing a positive photosensitive resin was used. Here, pattern A is made by passing a pattern with rando...

Embodiment 2

[0239] Mold B was produced in the same manner as that of Mold A in Example 1 except that the etching amount in the second etching process was set to 12 μm, and an anti-glare film was produced in the same manner as in Example 1 except that Mold A was replaced with Mold B. . This antiglare film was referred to as antiglare film B.

Embodiment 3

[0241] Mold C was produced in the same manner as that of Mold A in Example 1 except that the etching amount in the second etching process was set to 13 μm, and an anti-glare film was produced in the same manner as in Example 1 except that Mold A was replaced with Mold C. . Let this antiglare film be antiglare film C.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Root mean square roughnessaaaaaaaaaa
Root mean square roughnessaaaaaaaaaa
Root mean square roughnessaaaaaaaaaa
Login to View More

Abstract

Provided is an anti-glare film which exhibits excellent anti-glare properties at a wide observation angle even when the haze is low, and which can sufficiently inhibit glare and color fading from occurring when disposed on an image display device. Provided is the anti-glare film having a transparent support body, and an anti-glare layer formed thereon and having minute irregularities, wherein: the total haze is between 0.1% and 3%, inclusive; the surface haze is between 0.1% and 2%, inclusive; the root-mean-square roughness is within a predetermined range when measured at a predetermined cut-off length, for example, the root-mean-square roughness (Rq) (0.08) is between 0.01 and 0.05 mum, inclusive, when measured at a cut-off length of 0.08 mm; the shape of the surface irregularities on the aforementioned anti-glare layer has an average tilt angle value of 0.2 degree to 1.2 degrees, inclusive; and the standard deviation of the tilt angle is between 0.1 degree and 0.8 degree, inclusive.

Description

technical field [0001] The present invention relates to an antiglare film excellent in antiglare properties. Background technique [0002] For image display devices such as liquid crystal displays, plasma display panels, Braun tube (cathode ray tube: CRT) displays, and organic electroluminescent (EL) displays, in order to avoid In order to prevent deterioration of visibility, an anti-glare film is arranged on the display surface. [0003] As an anti-glare film, a transparent film having a surface unevenness has been mainly considered. Such an anti-glare film exhibits anti-glare properties by reducing the reflection of external light by scattering and reflecting external light (external light scattered light) by using the uneven shape of the surface. However, when the scattered light from external light is strong, the entire display surface of the image display device may be whitish or the so-called "whitening" such as cloudy displayed colors may occur. In addition, the pi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): G02B5/02
CPCG02B5/0268G02B5/0215
Inventor 古谷勉
Owner SUMITOMO CHEM CO LTD
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com