Wear-resistant nylon composite material and preparation method therefor

A nylon composite material, nylon technology, applied in the field of wear-resistant and high-temperature resistant nylon composite materials and its preparation, can solve the problems of composite material loss of mechanical properties, poor compatibility, and restrictions on the promotion and application of composite materials, and achieve stable product quality. Improved wear resistance and high continuous production efficiency

Inactive Publication Date: 2016-06-08
HEFEI GENIUS NEW MATERIALS
View PDF2 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although in the prior art, high-temperature-resistant nylon is modified by adding wear-resistant agents to increase its wear resistance, but the mechanical properties of the composite material are poor due to the poor compatibility between the added components. Severe losses limit the popularization and application of composite materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0025] The content of the present invention is further illustrated below in conjunction with specific examples, but the content of the present invention is not limited only to the following examples.

[0026] The preparation method of wear-resistant nylon composite material of the present invention, adopts following steps:

[0027] (1) Add 5kg of molybdenum disulfide to 5L of dilute sulfuric acid solution with a concentration of 17wt%, heat to 70-80°C, stir for 1-2 hours, filter, and wash with deionized water until neutral; wash the Add molybdenum disulfide to 5L of 17wt% sodium hydroxide solution, stir at 50-80°C for 1-2 hours, filter, wash with deionized water until neutral, and dry;

[0028] (2) Add the dried molybdenum disulfide into toluene diisocyanate, soak for 30-60 minutes, filter and dry to obtain pretreated molybdenum disulfide.

[0029] (3) Put the high-temperature-resistant nylon and pretreated molybdenum disulfide in a high-mixer, stir for 5 minutes at 80°C and ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a wear-resistant nylon composite material. The wear-resistant nylon composite material is prepared from the following ingredients in parts by weight: 65-95 parts of high-temperature resistant nylon, 1-15 parts of pretreated molybdenum disulfide, 0.1-1.0 part of antioxidant and 0.2-1.0 part of lubricant. The invention also discloses a preparation method for the wear-resistant nylon composite material. According to the wear-resistant nylon composite material and the preparation method therefor, the pretreated molybdenum disulfide is added as a wear resistance modifier, and proper processing aids are added, so that the wear resistance and heat resistance of high-temperature nylon are improved, the use value is higher, the field of employment is widened, and the wear-resistant nylon composite material can be extensively applied to the fields of electronic electrical appliances, automobiles, war industry and the like; the composite material disclosed by the invention is simple in extruded preparation process, high in continuous production efficiency and stable in product quality; and the high-temperature nylon and the pretreated molybdenum disulfide are pre-mixed firstly, so that the dispersity of the pretreated molybdenum disulfide in the composite material is greatly improved, and the wear resistance of the composite material is improved.

Description

technical field [0001] The invention belongs to the technical field of polymer materials, and in particular relates to a wear-resistant and high-temperature-resistant nylon composite material and a preparation method thereof. Background technique [0002] High temperature resistant nylon is a kind of aromatic polyamide, which is a polyamide resin prepared by polycondensation reaction of diamine or dicarboxylic acid with aromatic ring and aliphatic dicarboxylic acid or diamine. Due to the introduction of aromatic rings into the main chain of polyamide molecules, its heat resistance and mechanical properties are improved, water absorption is reduced, and it has a more suitable performance / price ratio. Therefore, high-temperature-resistant nylon is a high-heat-resistant resin between general-purpose engineering plastic nylon and high-temperature-resistant engineering plastic polyether ether ketone (PEEK), and is increasingly used in machinery, electronics and other fields. H...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L77/06C08K13/06C08K9/04C08K9/02C08K3/30C08K5/134C08K5/526C08K5/098
Inventor 杨桂生方永炜
Owner HEFEI GENIUS NEW MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products