A technology for pump bearings and bearing seats, applied in the field of pump bearings and bearing seat cleaning agents, can solve problems such as increasing the risk of rusting of bearings and bearing seats, inability to completely remove grease and other contaminants, and failure to reach them. , to achieve the effect of prolonging the service life, ensuring normal operation and convenient use
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0016] (1) Dissolve 10 parts of hydrogenated rosin in 200 parts of ethanol, add 6 parts of stearic acid and 0.2 part of silane coupling agent, mix well, and then microwave at a microwave frequency of 2450 MHz and a power of 800 W for 10 minutes to obtain material I;
[0017] (2) Add 12 parts of asbestos wool and 4 parts of volcanic ash to 15 parts of ore soil, first heat to 70-80°C and mix for 15 minutes, then add 3 parts of soda powder and 1 part of aluminum powder, and continue heating to 110-120°C to keep warm Mix for 10 minutes to obtain material II;
[0018] (3) Add material II, 8 parts of tea seed powder, 8 parts of soap powder, 3 parts of polyaspartic acid, 3 parts of sodium salicylate and 1 part of borax to material I, mix well and add to the ball mill, and ball mill until The fineness is less than 50μm.
[0019] Preparation of ore soil: Add 6 parts of hydrogenated castor oil and 2 parts of nano-zinc oxide into 5 times the weight of ethanol, stir to form a uniform sol...
Embodiment 2
[0022] (1) Dissolve 15 parts of hydrogenated rosin in 250 parts of ethanol, then add 8 parts of stearic acid and 0.3 part of silane coupling agent, mix well, and microwave at a microwave frequency of 2450 MHz and a power of 800 W for 10 minutes to obtain material I;
[0023] (2) Add 10 parts of asbestos wool and 6 parts of volcanic ash to 20 parts of ore soil, first heat to 70-80 ° C and mix for 15 minutes, then add 3 parts of soda powder and 1 part of aluminum powder, and continue heating to 110-120 ° C to keep the temperature Mix for 10 minutes to obtain material II;
[0024] (3) Add material II, 10 parts of tea seed powder, 6 parts of soap powder, 5 parts of polyaspartic acid, 4 parts of sodium salicylate and 0.5 part of borax to material I, mix well and add in the ball mill, and ball mill until The fineness is less than 50μm.
[0025] Preparation of ore soil: Add 8 parts of hydrogenated castor oil and 3 parts of nano-zinc oxide into 5 times the weight of ethanol, stir to ...
PUM

Abstract
Description
Claims
Application Information

- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com