Environment-friendly abrasion-resistant waterproof leakage repair material and preparation method thereof

A leak trapping and environmental protection technology, applied in anti-corrosion coatings, polyurea/polyurethane coatings, coatings, etc., can solve problems such as leakage, pungent odor, etc., and achieve the effect of saving man-hours, improving tensile strength and excellent performance

Active Publication Date: 2016-07-06
SHENZHEN AIDAKAI WATERPROOF ENG CO LTD
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The most widely used waterproof coatings in the prior art are polyurethane waterproof coatings, which are cheap and have a strong and pungent smell. The main function is benzene compounds. Thinner or gasoline can be diluted for construction. Since thinner is more advantageous in price compared with gasoline, 95% of engineering teams will use thinner to dilute traditional polyurethane waterproof coatings. The main component of thinner is organic solvents containing benzene , and benzene is recognized as a strong carcinogen, using this material for construction waterproofing can only temporarily solve the problem of leakage in a short period of time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] Adopt isocyanate-free hydroxyl water-based polyurethane, calcium carbonate powder, powdery inorganic pigment, defoamer and colorless and transparent water-based polyurethane cross-linking agent, wherein 100 parts by weight of hydroxyl water-based polyurethane, 35 parts by weight of calcium carbonate powder, water-based polyurethane cross-linking agent The joint agent is 20 parts by weight. Among them, hydroxyl water-based polyurethane, calcium carbonate powder, powdered inorganic pigment, and defoamer constitute the first component, and water-based polyurethane crosslinking agent constitutes the second component. When used, these two components can be mixed to obtain environmental protection. Wear-resistant and waterproof leak-trap material.

Embodiment 2

[0018] Adopt hydroxyl water-based polyurethane without isocyanate, calcium carbonate powder, powdery inorganic pigment, defoamer and colorless and transparent water-based polyurethane cross-linking agent, wherein 100 parts by weight of hydroxyl water-based polyurethane, 38 parts by weight of calcium carbonate powder, water-based polyurethane cross-linking agent The joint agent is 22 parts by weight. Among them, hydroxyl water-based polyurethane, calcium carbonate powder, powdered inorganic pigment, and defoamer constitute the first component, and water-based polyurethane crosslinking agent constitutes the second component. When used, these two components can be mixed to obtain environmental protection. Wear-resistant and waterproof leak-trap material.

Embodiment 3

[0020] Adopt hydroxyl water-based polyurethane without isocyanate, calcium carbonate powder, powdery inorganic pigment, defoamer and colorless and transparent water-based polyurethane cross-linking agent, wherein 100 parts by weight of hydroxyl water-based polyurethane, 40 parts by weight of calcium carbonate powder, water-based polyurethane cross-linking agent Joint agent is 25 parts by weight. Among them, hydroxyl water-based polyurethane, calcium carbonate powder, powdered inorganic pigment, and defoamer constitute the first component, and water-based polyurethane crosslinking agent constitutes the second component. When used, these two components can be mixed to obtain environmental protection. Wear-resistant and waterproof leak-trap material.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention provides an environment-friendly abrasion-resistant waterproof leakage repair material and a preparation method thereof.The environment-friendly abrasion-resistant waterproof leakage repair material is prepared from hydroxyl waterborne polyurethane containing isocyanate, calcium carbonate powder, powdery inorganic pigment, a defoaming agent and a colorless transparent waterborne polyurethane cross-linking agent, and the material comprises, by weight, 100 parts of hydroxyl waterborne polyurethane, 35-45 parts of calcium carbonate powder and 20-30 parts of the waterborne polyurethane cross-linking agent.The hydroxyl waterborne polyurethane, the calcium carbonate powder, the powdery inorganic pigment and the defoaming agent form a first component, and the waterborne polyurethane cross-linking agent forms a second component.When the material is used, the two components are mixed so that the environment-friendly abrasion-resistant waterproof leakage repair material can be obtained.the material is free of toxin, environment friendly and stable in performance, and is elastic, high in bonding force and resistant to acid, alkaline and aging after being cured into a film, the service life can be 30 years or above, and the defects that an existing conventional waterproof anti-seeping grouting material is not durable and not environmentally friendly enough can be overcome and made up for.

Description

technical field [0001] The invention relates to the field of waterproof materials, in particular to an environmentally friendly wear-resistant waterproof leak-trapping material and a preparation method thereof. Background technique [0002] The most widely used waterproof coatings in the prior art are polyurethane waterproof coatings, which are cheap and have a strong and pungent smell. The main function is benzene compounds. Thinner or gasoline can be diluted for construction. Since thinner is more advantageous in price compared with gasoline, 95% of engineering teams will use thinner to dilute traditional polyurethane waterproof coatings. The main component of thinner is organic solvents containing benzene , and benzene is recognized as a strong carcinogen, using this material for construction and waterproofing can only temporarily solve the problem of leakage in a short period of time. Contents of the invention [0003] The invention provides an environmentally friendl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/04C09D5/08C09D7/12
CPCC08K3/26C08K2003/265C09D5/08C09D7/40C09D7/61C09D175/04
Inventor 李海军姜虎刘建新
Owner SHENZHEN AIDAKAI WATERPROOF ENG CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com