Production technology for resin buttons

A production process and button technology, applied to buttons, fasteners, clothing, etc., can solve the problems of single color effect, easy to break, and brittle buttons, and achieve the effect of simple preparation method, reduced manufacturing cost, and bright colors

Inactive Publication Date: 2016-07-13
嘉善天路达工贸有限公司
View PDF0 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the lack of luster of resin buttons made of traditional materials, and the color effect is relatively simple, it cannot meet the aesthetic needs of modern society.
[0003] And in order to meet the inspection standard of the industry, existing resin buttons mostly adopt m-benzene resin to produce, and the cost of m-benzene resin is higher, so the cost is also high, and the buttons produced by m-benzene resin are more brittle and easily broken

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0014] The preparation process of the resin button of the present invention is as follows: a, raw material mixing, after mixing all the raw materials in the formula, form glue at a temperature of 200-300°C;

[0015] For sheet b, pour the fully mixed glue into a centrifuge bucket, gel at 35°C-40°C for 2-3 minutes, and then let it dry for 20-30 minutes to form a soft gel. The jelly is cut into slices, and then placed on the blanking machine to punch blanks;

[0016] c. Submerge the billet formed by punching in brine, wherein the mass of salt and water is 1:30-40, keep the temperature at 85°C-95°C, and bathe in water for 4-5 hours to make the billet completely react Afterwards, the hard embryo-like germ kernel;

[0017] D, the germ grain that is hard embryo shape is processed into button with button machine in the step c;

[0018] e. Put the buttons made in step d into the water mill barrel, which mainly contains water and lime powder. After polishing for 10-15 hours, clean the...

Embodiment 1

[0020] Example 1: After mixing 88% o-phthalic resin, 10% isophthalic resin, 0.5% accelerator, 0.5% and 1.0% curing agent, at a temperature of 20°C, a glue is formed slurry; Pour the fully mixed slurry into a centrifuge bucket, gel at 35°C for 2 minutes, then let it air for 20 minutes to form a soft jelly, cut the soft jelly into slices, Then put it on the punching machine to punch the blank; immerse the blank formed by the blank in brine, wherein the mass of salt and water is 1:30, keep the temperature at 85°C, and bathe in water for 4 hours to make the blank completely react Finally, it is a hard embryo-like germ grain; the hard embryo-like germ grain is processed into a button with a button machine; the button is put into a water mill bucket, and the water mill bucket mainly contains water and lime powder. After grinding for 10 hours, Then clean the polished buttons, and then use ultrasonic cleaning, add an organic solvent cleaning agent to the ultrasonic cleaning machine, a...

Embodiment 2

[0021] Embodiment 2: After mixing the ortho-phthalic resin with a mass fraction of 85%, the iso-phthalic resin of 13%, the accelerator of 0.5%, the curing agent of 0.5% and 1.0%, at a temperature of 25°C, a glue is formed slurry; Pour the fully mixed slurry into a centrifuge bucket, gel at 38°C for 3 minutes, and then let it air for 25 minutes to form a soft jelly, cut the soft jelly into slices, Then put it on the punching machine to punch the blank; immerse the blank formed by the blank in brine, wherein the mass of salt and water is 1:35, keep the temperature at 88°C, and bathe in water for 5 hours to make the blank completely react Finally, it is a hard embryo-like germ grain; the hard embryo-like germ grain is processed into a button with a button machine; the button is put into a water mill bucket, and the water mill bucket mainly contains water and lime powder. After grinding for 12 hours, Then clean the polished buttons, and then use ultrasonic cleaning, add an organic...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a production technology for resin buttons and relates to the technical field of preparing resin buttons.The resin buttons are mainly prepared from a main material and an auxiliary material, wherein the main material is prepared from, by mass, 85-90% of orthophthalic resin and 5-10% of m-benzene resin, and the auxiliary material is prepared from, by mass, 0.5-0.8% of an accelerant, 0.5-1.0% of a mill base and 0.8-1.5% of a curing agent.The production technology comprises the steps that the raw materials are mixed; a sheet is formed, wherein a blank material formed by stamping a blank is steeped in salt water after stamping, and thus the blank material becomes hard blank particles; the hard blank particles are processed into buttons with a button machine; the buttons are put into a water mill barrel for polishing, surface hardening treatment is carried out after ultrasonic washing, and the buttons are coated with coatings with a colorful effect through a coating machine.The orthophthalic resin is added and serves as the main material, so that the production cost of the buttons is reduced, and the produced buttons are firm and not likely to break; the produced buttons are then subjected to coating treatment, and thus the demand of people for fashion is met.

Description

Technical field: [0001] The invention relates to a production process of a resin button, belonging to the technical field of resin button preparation. Background technique: [0002] Buttons can not only connect clothes to make them tightly insulated, but also make people neat and tidy. The chic buttons will also embellish the clothes. Therefore, it is an indispensable part of the clothing structure. With the development of the times, buttons are becoming more and more colorful and beautiful in terms of material, shape and production process. Resin buttons are a major category of buttons. It has been favored by the public. Unanimous praise, with the rapid development of the clothing industry, it requires more changes in the button surface, especially in terms of gloss and color, to meet the needs of different special clothing. Due to the lack of luster of resin buttons made of traditional materials, and the color effect is relatively single, it cannot meet the aesthetic nee...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): A44B1/02
CPCA44B1/02
Inventor 俞善锋
Owner 嘉善天路达工贸有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com