Bismuth magnesium niobate modified potassium sodium niobate transparent ferroelectric ceramic material and preparation method thereof adopting low purity raw materials

A technology of potassium sodium niobate and ferroelectric ceramics, which is applied in the field of materials, can solve problems such as ecological and environmental hazards, and achieve the effects of excellent performance, simple preparation method, and strong practicability

Inactive Publication Date: 2016-08-03
SHAANXI NORMAL UNIV
View PDF1 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, since lead-based transparent ferroelectric ceramics contain more than 70% lead, which has brought serious harm to human beings and the ecological environment, many countries such as the European Union, the United States, Japan, and China have formulated multiple laws and regulations to stipulate that all newly produced electronic products should be lead-free

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Bismuth magnesium niobate modified potassium sodium niobate transparent ferroelectric ceramic material and preparation method thereof adopting low purity raw materials
  • Bismuth magnesium niobate modified potassium sodium niobate transparent ferroelectric ceramic material and preparation method thereof adopting low purity raw materials
  • Bismuth magnesium niobate modified potassium sodium niobate transparent ferroelectric ceramic material and preparation method thereof adopting low purity raw materials

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] 1. Ingredients

[0031] According to 0.93(K 0.5 Na 0.5 )NbO 3 -0.07Bi(Mg 1 / 3 Nb 2 / 3 )O 3 The stoichiometry was weighed separately for Na with a purity of 99.0%. 2 CO 3 3.6069g of K with a purity of 99.8% 2 CO 3 4.7414g Nb with a purity of 99.5% 2 o 5 19.0564g of Bi with a purity of 97% 2 o 3 2.4560g, purity are 98.5% MgO0.1395g, mix homogeneously, raw material mixture is packed in the nylon jar, be ball milling medium with zirconium ball, dehydrated alcohol, the mass ratio of dehydrated alcohol and raw material mixture is 1: 1.2, use a ball mill at 401 rpm for 16 hours, separate the zirconium balls, place the raw material mixture in a drying oven at 80°C for 10 hours, grind with a mortar for 30 minutes, and pass through an 80-mesh sieve.

[0032] 2. Pre-burning

[0033] Place the raw material mixture after step 1 through an 80-mesh sieve in an alumina crucible, and compact it with an agate rod so that its compacted density is 1.5g / cm 3 , cover it, place i...

Embodiment 2

[0045] In the batching step 1 of the present embodiment, according to 0.97 (K 0.5 Na 0.5 )NbO 3 -0.03Bi(Mg 1 / 3 Nb 2 / 3 )O 3 The stoichiometry was weighed separately for Na with a purity of 99.0%. 2 CO 3 3.8736g of K with a purity of 99.8% 2 CO 3 5.0919g of Nb with a purity of 99.5% 2 o 5 19.8892g of Bi with a purity of 97.0% 2 o 3 1.0838g, 0.0615g of MgO with a purity of 98.5%, and the other steps were the same as in Example 1 to prepare a potassium sodium niobate transparent ferroelectric ceramic material modified by bismuth magnesium niobate.

Embodiment 3

[0047] In the batching step 1 of the present embodiment, according to 0.95 (K 0.5 Na 0.5 )NbO 3 -0.05Bi(Mg 1 / 3 Nb 2 / 3 )O 3 The stoichiometry was weighed separately for Na with a purity of 99.0%. 2 CO 3 3.7383g of K with a purity of 99.8% 2 CO 3 4.9141g of Nb with a purity of 99.5% 2 o 5 19.4667g of Bi with a purity of 97.0% 2 o 3 1.7799g, 0.1011g of MgO with a purity of 98.5%, the other steps were the same as in Example 1, and a potassium sodium niobate transparent ferroelectric ceramic material modified by bismuth magnesium niobate was prepared.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
remanent polarizationaaaaaaaaaa
transmittivityaaaaaaaaaa
dielectric lossaaaaaaaaaa
Login to View More

Abstract

The invention discloses a bismuth magnesium niobate modified potassium sodium niobate transparent ferroelectric ceramic material and a preparation method thereof adopting low purity raw materials. The formula of the ceramic material is (1-x)(K<0.5>Na<0.5>)Nb<3-x>Bi(Mg<1 / 3>Nb<2 / 3>)O3, wherein x represents the mole number of Bi(Mg<1 / 3>Nb<2 / 3>)O3 and is in a range of 0.03 to 0.09. Low purity raw materials are used, the preparation method comprises steps of preparing raw materials, pre-burning, ball-milling, granulating, pressing, rubber discharging, pressure-free sealed sintering, polishing, and silver ink firing; the ceramic material has the advantages of high light transmission, optical isotropy, strong practicality, and easy production, moreover, the preparation method is simple, the repeatability is good, and the yield is high. The test results show that when x is equal to 0.07, the optical transmission rate of the ceramic material is 70% or more in the visible light and infrared areas, at the same time, the ceramic material has good electric properties: the maximal dielectric constant is 3337, the dielectric loss is less than 3%, the remnant polarization is 1.5 [mu]C / cm2, and the coercive field is 7.0 kV / cm.

Description

technical field [0001] The invention belongs to the technical field of materials, and in particular relates to a potassium sodium niobate transparent ferroelectric ceramic material modified by bismuth magnesium niobate and a method for preparing the ceramic material by using low-purity raw materials. Background technique [0002] Transparent ferroelectric ceramics are a class of materials that can achieve optical intensity and voltage controllability due to the nonlinear change of their refractive index under the action of an electric field, which causes optical path differences in different crystallographic directions. Lithium niobate (LiNbO 3 ) crystal is the de facto industry standard because of its large nonlinear optical coefficient and high response speed. [0003] With the development of information technology, LiNbO 3 Due to the disadvantages of low electro-optic coefficient, high temperature dependence and high cost, crystal can no longer meet the requirements of ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/495
CPCC04B35/495C04B2235/3201C04B2235/3206C04B2235/3251C04B2235/3298C04B2235/9653
Inventor 杨祖培张小帅晁小练魏灵灵
Owner SHAANXI NORMAL UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com