Process for producing thermal dye sublimation raw paper

A production process, thermal sublimation technology, applied in papermaking, paper machines, textiles and papermaking, etc., can solve problems such as inability to meet the use requirements of thermal sublimation base paper, poor printing effect, lint and powder loss, etc., and achieve low cost and smooth surface Good degree of paper uniformity

Inactive Publication Date: 2016-09-21
SHANDONG TIANYANG PAPER
View PDF6 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Aiming at the fact that traditional papermaking methods cannot meet the requirements for the use of thermal sublimation base paper, the present invention provides a production process for thermal sublimation base paper, through which the tearing degree, evenness, expansion ratio, tensile strength and Smoothness and other indicators, so as to solve the phenomenon of lint and powder falling, poor printing effect, wrinkling of base paper during printing, and easy paper breakage during printing of the base paper produced by traditional technology.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Process for producing thermal dye sublimation raw paper
  • Process for producing thermal dye sublimation raw paper

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] ① Disintegration: Add plant fiber into the pulper, and decompose it into the pulp tank through the pulper, and add fillers to the pulp tank at the same time, and control the dry pulp concentration of the pulp to 3.6%, of which coniferous wood accounts for 15% of the total mass of plant fibers, hardwood accounts for 85% of the total mass of plant fibers, and fillers account for 30% of the total mass of fillers and plant fibers.

[0040] ② Refining: Use a double-disc refiner to beat the pulp, the beating degree is controlled at 25°SR, and the wet weight is controlled at 4.5g.

[0041] ③ Ingredients: add cationic starch with an amount of 1.0% and a wet strength agent with an amount of 0.5% in the slurry after refining. As a specific implementation, the wet strength agent in this example adopts polyamide epoxy resin .

[0042] ④Dilution and purification: The slurry after batching is diluted to control the concentration of the feedstock, and the concentration of the feedsto...

Embodiment 2

[0048] ① Disintegration: Add plant fiber into the pulper, and decompose it into the pulp tank through the pulper, add fillers to the pulp tank at the same time, and control the dry pulp concentration of the pulp to 4%, of which coniferous wood accounts for 25% of the total mass of plant fibers, hardwood accounts for 75% of the total mass of plant fibers, and fillers account for 20% of the total mass of fillers and plant fibers.

[0049] ② Refining: Use a double-disc refiner to beat the pulp, the beating degree is controlled at 32°SR, and the wet weight is controlled at 5.5g.

[0050] ③Batching: Add cationic starch with an amount of 1.25% and a wet strength agent with an amount of 0.75% to the slurry after refining. As a specific implementation, the wet strength agent in this example adopts polyamide epoxy resin .

[0051] ④Dilution and purification: The slurry after batching is diluted to control the concentration of the feedstock, and the concentration of the feedstock is co...

Embodiment 3

[0057] ① Disintegration: Add plant fiber to the pulper, and decompose it into the pulp tank through the pulper, and add fillers to the pulp tank at the same time, and control the absolute dry pulp concentration of the pulp to 4.2%, of which coniferous wood accounts for 30% of the total mass of plant fibers, hardwood accounts for 70% of the total mass of plant fibers, and filler accounts for 15% of the total mass of fillers and plant fibers.

[0058] ② Refining: use a double-disc refiner to beat the pulp, the beating degree is controlled at 35°SR, and the wet weight is controlled at 6.5g.

[0059] ③Batching: Add cationic starch with an amount of 1.5% and a wet strength agent with an amount of 1.0% to the slurry after refining. As a specific implementation, the wet strength agent in this example adopts polyamide epoxy resin .

[0060] ④Dilution and purification: The slurry after batching is diluted to control the concentration of the feedstock, and the concentration of the feed...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

A production process of sublimation base paper relates to the field of papermaking technology. Firstly, coniferous wood and hardwood with a mass ratio of 15:85 to 30:70 are crushed through a pulper, and then fillers are added, and the mass of plant fibers and fillers is The ratio is 70:30~85:15; then refine the obtained slurry, and control the degree of beating to 25~35°SR, and add cationic starch and wet strength agent to the slurry; then dilute and purify , forming on the net, pressing, and then drying the obtained wet paper for the first time, surface sizing, second drying and third drying to obtain the sublimation base paper. The invention can effectively control the tearing degree, evenness, stretching rate, tensile strength and smoothness of the sublimation base paper, thereby solving the problem of lint and powder falling and poor printing effect of the base paper produced by the traditional process during use. , The base paper is wrinkled during the printing process, and the paper is easy to break during printing.

Description

technical field [0001] The invention relates to the technical field of papermaking, in particular to a production process of thermal sublimation base paper. Background technique [0002] Sublimation transfer printing technology uses inkjet printing to print special printing dyes on paper, and then heats and pressurizes to transfer the dyes to fabrics. Sublimation transfer printing products have the advantages of good printing effect, soft hand feeling, long service life, simple process, less equipment investment, strong flexibility, high authenticity rate, resource saving, and environmental protection. With the continuous development of thermal sublimation transfer printing technology and people's recognition and dependence on thermal sublimation transfer printing products, thermal sublimation transfer printing technology has developed rapidly in my country, and its application fields have become more and more extensive. [0003] Sublimation base paper, as the carrier of su...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D21F9/00D21F5/02D21H21/16D21H21/20D21H21/10
CPCD21F9/00D21F5/02D21H21/10D21H21/16D21H21/20
Inventor 刘洪奎刘洪霞张俊刚祝建国袁保利陈敏
Owner SHANDONG TIANYANG PAPER
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap