Anchoring brick

A technology for anchoring bricks and bauxite particles, which is applied in the field of refractory materials, can solve the problems of poor thermal stability of fired products, and achieve the effects of strong load softening temperature, thermal shock resistance and life improvement

Inactive Publication Date: 2016-10-12
JIAOZUO JINXIN HENGTUO REFRACTORIES
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Compared with unfired products and unshaped refractory materials, the thermal stability of fired products is very poor. With the technological progress of new ki

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0009] Example 1

[0010] The components of anchor bricks include main materials and binders. The main materials include aggregates and powders. The aggregates are composed of the following parts by weight: 3-5mm alumina pellets 10 parts, 1-3mm alumina 25 parts of granules, 10 parts of alumina particles of 0-1mm, 15 parts of kyanite of 0.5-1mm; the powder consists of the following parts by weight: combined clay powder 5 parts, bauxite clinker powder 15 Parts, 20 parts of bauxite flour; the binding agent is composed of the following parts by weight: 0.6 parts of calcium lignosulfonate and 0.2 parts of yellow dextrin. Pour the above-mentioned components into the mixer, add 5% clean water, stir evenly, and form after 2 hours of trapping. The finished brick can be obtained after drying and firing steps.

Example Embodiment

[0011] Example 2

[0012] The components of anchoring bricks include main materials and binders. The main materials include aggregates and powders. The aggregates are composed of the following parts by weight: 3-5mm bauxite pellets 15 parts, 1-3mm bauxite 30 parts of particles, 5 parts of 0-1mm alumina particles, 10 parts of 0.5-1mm kyanite; the powder consists of the following parts by weight: combined clay powder 5 parts, bauxite clinker powder 20 Parts, 15 parts of raw bauxite powder; the binding agent is composed of the following parts by weight: 0.4 part of calcium lignosulfonate and 0.1 part of yellow dextrin. Pour the above-mentioned components into the mixer, add 5% clean water, stir evenly, and form after 2 hours of trapping. The finished brick can be obtained after drying and firing steps.

Example Embodiment

[0013] Example 3

[0014] The components of anchor bricks include main materials and binders. The main materials include aggregates and powders. The aggregates are composed of the following parts by weight: 3-5mm alumina pellets 10 parts, 1-3mm alumina 30 parts of granules, 10 parts of alumina particles of 0-1mm, 5 parts of kyanite of 0.5-1mm; the powder consists of the following parts by weight: 10 parts of combined clay powder, 15 parts of bauxite clinker powder Parts, 15 parts of raw bauxite powder; the binding agent is composed of the following parts by weight: 0.5 parts of calcium lignosulfonate and 0.2 parts of yellow dextrin. Pour the above-mentioned components into the mixer, add 5% clean water, stir evenly, and form after 2 hours of trapping. The finished brick can be obtained after drying and firing steps.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an anchoring brick. The anchoring brick comprises a main material and a bonding agent, wherein the main material comprises aggregates and power; the aggregates comprise the following components in parts by weight: 10 to 15 parts of 3 to 5mm alumina granules, 25 to 35 parts of 1 to 3mm alumina granules, 5 to 15 parts of 0 to 1mm alumina granules, and 5 to 15 parts of kyanite; the powder comprises the following components in parts by weight: 5 to 10 parts of combined clay powder, 15 to 25 parts of alumina pulverized clinker, and 15 to 25 parts of alumina raw powder; the bonding agent comprises the following components in parts by weight: 0.3 to 0.8 part of calcium lignosulphonate, and 0.1 to 0.3 part of yellow dextrin. The anchoring brick has the beneficial effects that the anchoring brick produced through the formula has higher refractoriness under load and thermal shock resistance capacity, and ensures that the service life of an industrial furnace is greatly prolonged.

Description

technical field [0001] The invention relates to the technical field of refractory materials, in particular to an anchor brick. Background technique [0002] Compared with unfired products and unshaped refractory materials, the thermal stability of fired products is very poor. With the technological progress of new kilns, the requirements for thermal stability of fired products are very strict. Therefore, thermal stability has become a The bottleneck of the development of fired products. For the anchor brick, it is used as an anchor to connect and fix the working layer and the insulation layer during use, and must maintain a high strength at high temperatures. In addition, the kilns used in most cases work intermittently, and they have to withstand repeated temperature changes during use. Therefore, the traditional production process is improved to improve the thermal stability and thermal shock resistance of the fired anchor bricks, which can significantly prolong the produ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B35/66C04B35/101
CPCC04B35/101C04B2235/349
Inventor 薛鸿雁李强许兴堂武占忠范红刚黄江文刘涛生王小波
Owner JIAOZUO JINXIN HENGTUO REFRACTORIES
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap