High-toughness silica gel strip used for windscreen wipers, and manufacturing method thereof
A technology for silicone strips and wipers, applied in the field of auto parts, can solve the problems of short service life, poor toughness, poor shape and corrosion resistance, and reduced product strength, and achieve long service life, strong corrosion resistance and good softness. Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0015] Silicone strips for high tenacity wipers, composed of 60% silica gel, 12% white carbon black, 6% silicone oil, 5% polytetrafluoroethylene, 5% diisooctyl phthalate, 3% Diisooctyl adipate, 3% tributyl (1-ethoxyethylene) tin, 3% carbon black, 3% dicumyl peroxide.
[0016] A method for manufacturing a silicone strip for a high-toughness windshield wiper, comprising the following steps:
[0017] Step 1: Mixing raw materials: Stir silica gel, white carbon black, silicone oil, polytetrafluoroethylene, diisooctyl phthalate, carbon black, and dicumyl peroxide evenly, then continue stirring, adding Diisooctyl adipate, then add tributyl (1-ethoxyethylene) tin, stir evenly to form a silica gel strip blank;
[0018] Step 2: extruding the silica gel strip blank in step 1;
[0019] Step 3: Put the silica gel strip blank extruded in step 2 into a drying box, dry and shape at a high temperature of 500-600 degrees, and the product is finished.
[0020] The use of silica gel makes the ...
Embodiment 2
[0022] Silicone strips for high tenacity wipers, composed of 65% silica gel, 10% white carbon black, 5% silicone oil, 6% polytetrafluoroethylene, 6% diisooctyl phthalate, 2% Diisooctyl adipate, 3% tributyl (1-ethoxyethylene) tin, 1% carbon black, 2% dicumyl peroxide.
[0023] Compared with Example 1, the amount of silica gel is increased, the softness is increased, and the glass is easier to scrape clean.
Embodiment 3
[0025] High-toughness silicone strip for wiper, said high-toughness silicone strip is composed of 70% silica gel, 8% white carbon black, 4% silicone oil, 5% polytetrafluoroethylene, 5% phthalate Diisooctyl formate, 2% diisooctyl adipate, 2% tributyl (1-ethoxyethylene) tin, 2% carbon black, 2% dicumyl peroxide.
[0026] Compared with the above two embodiments, the amount of silica gel is the largest and the softness is the best.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap