High-performance polyurethane-modified butyronitrile latex gloves and preparation method thereof

A technology of polyurethane modification and polyurethane latex, applied in gloves, clothing, protective clothing, etc., can solve few problems, achieve good chemical protection and increase chemical resistance

Active Publication Date: 2016-11-09
中红普林(北京)医疗用品高新技术研究院有限公司
View PDF9 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The combination of the two has good compatibility, and can play a strong combined effect in terms of perfor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-performance polyurethane-modified butyronitrile latex gloves and preparation method thereof
  • High-performance polyurethane-modified butyronitrile latex gloves and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0024] Table 1 Nitrile Latex Formula

[0025] raw material

Nitrile Latex

sulfur

Accelerator

Zinc oxide

Titanium dioxide

Dispersant

pure water

Dosage (number of servings)

86.4

1.55

0.94

0.93

1.94

0.04

167.4

[0026] Polyurethane emulsion is synthesized as follows:

[0027] First get 33 parts of polytetrahydrofuran glycol (PTMG) and add in the reaction kettle, under the situation of stirring, add 22 parts of isophorone diisocyanate (IPDI), then weigh 2.5 parts of dimethylol propionic acid (DMPA) and 3 Add 20 parts of diethylene glycol into the kettle, stir well, then add 20 parts of acetone and 0.02 parts of catalyst dibutyltin dilaurate in sequence. At 60-80°C, start timing and react for 3 hours. Then 1.6 parts of trimethylolpropane (TMP) and 25 parts of acetone were added, and the reaction was timed for 3 hours. After the reaction was completed, the temperature was lowered to below 50° C., and 33 parts of...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a pair of high-performance polyurethane-modified butyronitrile latex gloves and a preparation method thereof. According to the method, the chemical resistance of carboxyl butyronitrile latex can be enhanced by adopting a method of blending polyether urethane emulsion with butyronitrile latex. The butyronitrile gloves produced by adopting the impregnation forming technology of blended latex have the double characteristics of butyronitrile latex and polyurethane, as well as good chemical protection capability, and glove products can be produced on the existing butyronitrile latex glove production line.

Description

technical field [0001] The invention relates to a high-performance polyurethane-modified nitrile latex and a preparation method thereof, which belongs to the field of polymer materials. Background technique [0002] In recent years, with the improvement of enterprises' awareness of labor protection, enterprises have invested more and more in labor protection. The most obvious is the change of glove varieties, from traditional labor protection products (thread gloves) to synthetic chemical labor protection products (Latex gloves), the protective performance is gradually enhanced, the types of gloves are becoming more and more abundant, and the protection is becoming more and more targeted. At present, in many industries such as medical treatment, food, electronics, and photovoltaics, the protection of gloves is becoming more and more important. The main types of gloves include polyvinyl chloride gloves, natural rubber gloves, and nitrile gloves, among which nitrile gloves do ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L9/04C08L75/08C08K13/02C08K3/06C08K3/22C08G18/75C08G18/66C08G18/48C08G18/34C08G18/32C08G18/12A41D19/015
CPCA41D19/015C08G18/0823C08G18/12C08G18/4854C08G18/6674C08G18/6692C08G18/755C08L9/04C08L75/08C08K13/02C08K3/06C08K2003/2296C08K2003/2241C08G18/3206
Inventor 李成文赵世图李民刚
Owner 中红普林(北京)医疗用品高新技术研究院有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap