Anti-mildew paperboard and preparation method thereof

A technology for anti-mildew and cardboard, which is applied in the direction of paper, papermaking, paper coating, etc., can solve the problems of easy mildew, unusable cartons, and waste of cost

Inactive Publication Date: 2016-11-09
铜陵锋帆彩色印务有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In view of the above-mentioned prior art, the purpose of the present invention is to overcome the conventional cartons in the prior art that are often affected by the surrounding environment during storage and placement, especially in humid and cold environments. Problems such as mildew occur, thereby making the cartons unusable, and causing a large cost waste, thereby providing an anti-mildew that can effectively prevent mildew, greatly reduce the use cost of the produced cartons, and reduce storage costs. Cardboard and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0013] The present invention provides a kind of preparation method of anti-mildew cardboard, wherein, described preparation method comprises:

[0014] 1) After mixing and melting styrene-acrylic emulsion, nano-titanium dioxide, ferric oxide, carboxymethyl cellulose, polyvinyl alcohol, talcum powder and water, the mixture M1 is obtained;

[0015] 2) Coating the mixture M1 prepared in step 1) on the cardboard to obtain mildew-resistant cardboard; wherein,

[0016] With respect to 100 parts by weight of the styrene-acrylic emulsion, the amount of nano-titanium dioxide is 0.5-3 parts by weight, the amount of ferric oxide is 3-8 parts by weight, and the content of carboxymethyl cellulose is 3-10 parts by weight, the amount of polyvinyl alcohol used is 1-5 parts by weight, the amount of talcum powder used is 5-20 parts by weight, and the amount of water used is 10-30 parts by weight.

[0017] The above design mixes styrene-acrylic emulsion, nano-titanium dioxide, ferric oxide, carb...

Embodiment 1

[0027] 1) After mixing 100g of styrene-acrylic emulsion, 1g of nano-titanium dioxide, 5g of ferric oxide, 5g of carboxymethyl cellulose, 2g of polyvinyl alcohol, 10g of talcum powder and 15g of water and melting it at a temperature of 200°C, Preparation of mixture M1;

[0028] 2) Coating the mixture M1 prepared in step 1) on the cardboard to obtain mildew-resistant cardboard A1.

Embodiment 2

[0030] 1) After mixing 100g of styrene-acrylic emulsion, 2g of nano-titanium dioxide, 7g of ferric oxide, 8g of carboxymethyl cellulose, 4g of polyvinyl alcohol, 15g of talcum powder and 25g of water and melting it at a temperature of 350°C, Preparation of mixture M1;

[0031] 2) Coating the mixture M1 prepared in step 1) on the cardboard to obtain mildew-resistant cardboard A2.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Viscosityaaaaaaaaaa
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses an anti-mildew paperboard and a preparation method thereof. The preparation method comprises the steps that 1, styrene-acrylic emulsion, nanometer titania, iron sesquioxide, carboxymethylcellulose, polyvinyl alcohol, talcum powder and water are mixed and molten, and a mixture M1 is prepared; 2, a paperboard is coated with the mixture M1 prepared in the step 1, and the anti-mildew paperboard is prepared, wherein the mixture M1 is prepared from 100 parts by weight of styrene-acrylic emulsion, 0.5-3 parts by weight of nanometer titania, 3-8 parts by weight of iron sesquioxide, 3-10 parts by weight of carboxymethylcellulose, 1-5 parts by weight of polyvinyl alcohol, 5-20 parts by weight of talcum powder and 10-30 parts by weight of water. By means of the design, the effects that mildewing can be effectively prevented, the use cost of the prepared paperboard is greatly reduced, and the preservation cost is reduced are achieved.

Description

technical field [0001] The invention relates to the field of production and preparation of cardboard, in particular to mildew-resistant cardboard and a preparation method thereof. Background technique [0002] As the production material of cartons, the properties of cardboard greatly affect the properties of the produced cartons. During the use of cartons, their wide application range often makes them placed in a wide range of environments. However, conventional cartons are often affected by the surrounding environment during storage and placement, especially in humid and cold environments. If the cartons are placed for a long time, they are prone to mildew and other problems, which makes the cartons unusable and causes serious damage. Big cost waste. [0003] Therefore, it is an urgent problem to be solved in the present invention to provide a mildew-resistant cardboard that can effectively prevent mildew, greatly reduce the use cost of the manufactured carton, and reduce ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D21H19/58D21H19/60D21H19/52D21H19/64D21H21/36
CPCD21H19/58D21H19/52D21H19/60D21H19/64D21H21/36
Inventor 解和锋沐磊
Owner 铜陵锋帆彩色印务有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products