A warp knitting spacer fabric composite sole

A warp knitting spacer fabric and composite sole technology, applied in warp knitting, shoe sole, knitting and other directions, can solve the problems of difficult to control pores, poor uniformity, low production efficiency, etc., and achieve the effect of reducing the viscosity increase efficiency

Active Publication Date: 2016-11-16
FUJIAN JINJIANG HUAYU WEAVING
View PDF4 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in order to improve the properties of elasticity, moisture absorption and breathability, the current materials for shoe soles are prepared by foaming solid materials, the prepared pores are difficult to control, and the uniformity is poor; and a certain forming mold is required for reverse molding production, resulting in low production efficiency. Especially because the bonding of the sole and the upper material requires the use of adhesives, etc., causing a large number of environmental protection problems and bringing a large amount of environmental pollution to the enterprise; and the new environmental protection sole material is firstly environmentally friendly, and secondly has a certain degree of elasticity and is also environmentally friendly. Need to have a certain degree of ventilation, but also hope to have the characteristics of light weight

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A warp knitting spacer fabric composite sole
  • A warp knitting spacer fabric composite sole
  • A warp knitting spacer fabric composite sole

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] A kind of production method of warp-knitted spacer fabric composite shoe sole, its specific steps are:

[0036] Using conventional polyester monofilament and high-strength polyester monofilament as raw materials, the warp knitting method of the integrally formed three-dimensional mesh fabric is warp knitting with a double needle bed warp knitting machine, warping, warp knitting, and finishing to prepare warp knitting Spacer fabric composite sole;

[0037] The conventional polyester monofilament is 40-400D polyester monofilament, and the specification of high-strength polyester monofilament is 60-500D denier.

[0038] The warp tension of the warp-knitted spacer fabric composite shoe sole is 15g during the warp-knitting process, and the warp-knitted shape of the warp-knitted spacer fabric composite shoe sole is any shoe sole shape, and the mesh pattern of the mesh cloth can be set arbitrarily; specifically For triangles, crosses, crosses, etc.

[0039] Its main process ...

Embodiment 2

[0057] A kind of production method of warp-knitted spacer fabric composite shoe sole, its specific steps are:

[0058] Using conventional polyester monofilament and high-strength polyester monofilament as raw materials, the warp knitting method of the integrally formed three-dimensional mesh fabric is warp knitting with a double needle bed warp knitting machine, warping, warp knitting, and finishing to prepare warp knitting Spacer fabric composite sole;

[0059] The conventional polyester monofilament is 40-400D polyester monofilament, and the specification of high-strength polyester monofilament is 60-500D denier.

[0060] The warp tension of the warp-knitted spacer fabric composite shoe sole is 30g during the warp-knitting process, and the warp-knitted shape of the warp-knitted spacer fabric composite shoe sole is any shoe sole shape, and the mesh pattern of the mesh cloth can be set arbitrarily; specifically For triangles, crosses, crosses, etc.;

[0061] Its main process...

Embodiment 3

[0079] A kind of production method of warp-knitted spacer fabric composite shoe sole, its specific steps are:

[0080] Using conventional polyester monofilament and high-strength polyester monofilament as raw materials, the warp knitting method of the integrally formed three-dimensional mesh fabric is warp knitting with a double needle bed warp knitting machine, warping, warp knitting, and finishing to prepare warp knitting Spacer fabric composite sole;

[0081] The conventional polyester monofilament is 40-400D polyester monofilament, and the specification of high-strength polyester monofilament is 60-500D denier.

[0082] The warp tension of the warp-knitted spacer fabric composite shoe sole is 45g during the warp-knitting process, and the warp-knitted shape of the warp-knitted spacer fabric composite shoe sole is any shoe sole shape, and the mesh pattern of the mesh cloth can be set arbitrarily; specifically For triangles, crosses, crosses, etc.;

[0083] Its main process...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a warp knitting spacer fabric composite sole. A production method of the sole is characterized by performing, with general polyester monofilaments and high-tenacity polyester monofilaments as raw materials, warp knitting by using a two-needle bar warp knitting machine based on a three-dimensional screen cloth warp knitting method to prepare elastic screen cloth through warping, warp knitting and after-finishing. Based on the method of three-dimensional warp knitting of warp knitting spacer fabric characterized by integral forming, a sole has excellent structural strength, elasticity and light weight; the warp knitting spacer fabric composite sole has excellent moisture conductivity and breathability performance of three-dimensional fabric; the polyester filaments with an antibacterial function and high tenacity are used as the screen cloth materials for the sole, so that the sole has the functions of bacteria resistance and bacteriostasis; a multi-step chain extension and tackifying process can be performed by using a tackifying chain extender with epoxy functional groups, so that the problems that conventional powdery tackifying is low in efficiency and micro-molecules are hard to remove in a tackifying process are solved. The prepared warp knitting spacer fabric composite sole has a broad application prospect in the field of shoe materials.

Description

technical field [0001] The invention relates to the technical field of textile production, in particular to a warp-knitted spacer fabric composite shoe sole. Background technique [0002] There are many types of sole materials, which can be divided into natural base materials and synthetic base materials. Natural bottom materials include natural bottom leather, bamboo, wood, etc., and synthetic bottom materials include rubber, plastic, rubber-plastic composite materials, recycled leather, elastic cardboard, etc. However, in order to improve the properties of elasticity, moisture absorption and breathability, the current materials for shoe soles are prepared by foaming solid materials, the prepared pores are difficult to control, and the uniformity is poor; and a certain forming mold is required for reverse molding production, resulting in low production efficiency. Especially because the bonding of the sole and the upper material requires the use of adhesives, etc., causing...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D04B21/00D01D5/12D01D5/092A43B1/04A43B13/02C08G63/91D01F6/62
CPCA43B1/04A43B13/02C08G63/91D01D5/092D01D5/12D01F6/62D04B21/00D10B2331/04
Inventor 苏成喻柯文新陈志鹏石建良杨孝清
Owner FUJIAN JINJIANG HUAYU WEAVING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products