Formula and preparation method of lead-carbon colloid battery electrode plate lead paste

A colloidal battery and lead paste technology, which is applied to battery electrodes, lead-acid batteries, circuits, etc., can solve the problems of weak adsorption, unfavorable charging and discharging, low porosity of lead paste, and low capacity, so as to improve fast charging ability, Effects of prolonging cycle life and improving power density

Active Publication Date: 2016-11-30
HUBEI RUNYANG NEW ENERGY
View PDF5 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The disadvantages of this paste process include: low porosity of lead paste, weak ability to absorb acid and maintain acid solution, low capacity, and low utilization rate of act

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] (1) Configure polyanionic cellulose solution. Proceed as follows:

[0044] First, add polyanionic cellulose into pure water in an amount of 10% by weight, stir well until it is completely dissolved, store it for 2 hours and use it;

[0045] Secondly, the polyanionic cellulose mother liquor prepared in the first step is diluted according to the mass ratio of pure water: polyanionic cellulose mother liquor = 100:1 to obtain a polyanionic cellulose solution.

[0046] (2) Measure the components of the positive plate lead paste formula.

[0047] Lead oxide powder: 100kg;

[0048] 1.20g / cm 3 Dilute sulfuric acid: 7kg;

[0049] Short polyester: 0.08kg;

[0050] Cypbrid carbon: 0.1kg;

[0051] Silica with a particle size of 1-9nm: 0.1 kg;

[0052] Polyanionic cellulose solution: 0.07kg;

[0053] Pure water: 7kg.

[0054] (3) Measure the components of the negative plate lead paste formula.

[0055] Lead oxide powder: 100kg;

[0056] 1.20g / cm 3 Dilute sulfuric acid: 7...

Embodiment 2

[0073] (1) Configure polyanionic cellulose solution. Proceed as follows:

[0074] First, add polyanionic cellulose into pure water in an amount of 18% by weight, stir well until it is completely dissolved, store it for 2 hours and use it;

[0075] Secondly, the polyanionic cellulose mother liquor prepared in the first step is diluted according to the mass ratio of pure water:polyanionic cellulose mother liquor=100:2.5 to obtain a polyanionic cellulose solution.

[0076] (2) Measure the components of the positive plate lead paste formula.

[0077] Lead oxide powder: 100kg;

[0078] 1.40g / cm 3 Dilute sulfuric acid: 8.5kg;

[0079] Short acrylic: 0.14kg;

[0080] Cypbrid Carbon: 0.15kg;

[0081] Silica with a particle size of 1-9nm: 0.3kg;

[0082] Polyanionic cellulose solution: 0.3kg;

[0083] Pure water: 8.5kg.

[0084] (3) Measure the components of the negative plate lead paste formula.

[0085] Lead oxide powder: 100kg;

[0086] 1.40g / cm 3 Dilute sulfuric acid: 9...

Embodiment 3

[0103] (1) Configure polyanionic cellulose solution. Proceed as follows:

[0104] First, add polyanionic cellulose into pure water in an amount of 25% by weight, stir well until it is completely dissolved, store it for 2 hours and use it;

[0105] Secondly, the polyanionic cellulose mother liquor prepared in the first step is diluted according to the mass ratio of pure water: polyanionic cellulose mother liquor = 100:5 to obtain a polyanionic cellulose solution.

[0106] (2) Measure the components of the positive plate lead paste formula.

[0107] Lead oxide powder: 100kg;

[0108] 1.60g / cm 3 Dilute sulfuric acid: 10kg;

[0109] Short spandex: 0.2kg;

[0110] Cypbrid carbon: 0.2kg;

[0111] 0.5kg of silicon dioxide with a particle size of 1-9nm;

[0112] Polyanionic cellulose solution: 0.5kg;

[0113] Pure water: 10kg.

[0114] (3) Measure the components of the negative plate lead paste formula.

[0115] Lead oxide powder: 100kg;

[0116] 1.60g / cm 3 Dilute sulfuric...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Densityaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention provides a formula and a preparation method of a lead-carbon colloid battery electrode plate lead paste. According to the present invention, partial lead is replaced by Cypbrid carbon, such that the battery has characteristics of the lead acid battery and the capacitor with the adding of the Cypbrid carbon so as to easily improve the rapid charging capacity of the battery, increase the power density of the battery and prolong the cycle life, and the Cypbrid carbon occupies the partial electrode space so as to cause the reducing of the energy density and increase the gassing amount of the electrode; SiO2 and polyanionic cellulose are added, such that the electrode plate porosity is increased, the adsorption of sulfuric acid is increased, and the protection effect is provided for the active substance attached on the surface of the electrode plate; the colloid exists in the dry paste of the electrode plate so as to increase the sulfuric acid and water retention capacity and provide the excellent charge and discharge characteristics, and can be matched with the colloidal electrolyte, such that the colloid content in the acid injection liquid can be reduced, the uniform distribution of the filled colloid is easily achieved, and the electrolyte in the separation plate and the colloid can be organically combined in the electrode plate.

Description

technical field [0001] The invention relates to lead-carbon colloidal battery pole plate technology, in particular to a lead-carbon colloidal battery pole plate lead paste formula and a preparation method thereof. Background technique [0002] Traditional lead-acid batteries have the characteristics of short cycle life and low specific energy. In order to improve the cycle life of the battery, it will be mixed with colloid to make a colloidal battery when injecting acid. In this way, the amount of glue added is large, the perfusion is difficult, and it is easy to mix unevenly. [0003] The manufacturing process of conventional lead-acid battery plates is as follows: First, mix lead oxide powder and other incoming materials for paste, smear the obtained lead paste on the grid, and then pour acid on the surface of the smeared plate, quickly Drying, curing, and finally polishing the green plates. Wherein, the process of mixing the paste is as follows: put the lead oxide powde...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): H01M4/36H01M4/56H01M4/587H01M4/62H01M10/06
CPCH01M4/364H01M4/56H01M4/587H01M4/62H01M10/06Y02E60/10
Inventor 罗旭陈健刘克宇程先清徐进
Owner HUBEI RUNYANG NEW ENERGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap