Photochromic ceramic ink with leather effect and preparation method thereof

A photochromic, ceramic ink technology, applied in the field of ceramics

Inactive Publication Date: 2016-12-07
FOSHAN GAOMING HAIDI CERAMIC RAW MATERIAL CO LTD
View PDF10 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are few reports about functional dermatoglyph effect ceramic inks at present, so the technology needs to be improved, and there is an urgent need to develop

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Photochromic ceramic ink with leather effect and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0039] Example 1

[0040] A photochromic ceramic ink with dermatoglyphic effect and a preparation method thereof. The preparation method includes the following steps:

[0041] Step A. Preparation of dermatoglyph: 35% SiO2, 10% Al2O3, 3% (K2O+Na2O), 8% (CaO+MgO), 7%B2O3, 15%ZrO2, 12%V2O5 are mixed and sanded evenly; 5% antibacterial compound and sand evenly; add 1% deodorant and sand evenly; then add 4% photochromic compound and sand evenly to make a mixture; spread the mixture into a refractory sagger , Conduct high-temperature melting at 1400°C to obtain a molten slurry; quench the slurry with water and break it into granules to obtain a skin glaze;

[0042] Step B. Weigh 20% dermatoglyph, 8% Solsperse 24000, 5% Span-80, 0.3% BYK052, 3% polystyrene resin and 63.7% environmentally friendly hydrocarbon solvent, add them to a high-speed mixer for dispersion for 60 minutes; disperse The good mixture is put into a sand mill and sanded for 10 hours to obtain a semi-finished ink with a p...

Example Embodiment

[0054] Example 2

[0055] A photochromic ceramic ink with dermatoglyphic effect and a preparation method thereof. The preparation method includes the following steps:

[0056] Step A. Preparation of skin texture glaze: mix 38% SiO2, 9% Al2O3, 2% (K2O+Na2O), 10% (CaO+MgO), 8% B2O3, 12% ZrO2, 12% V2O5 and sand and grind uniformly; 3.5% antibacterial compound and sand evenly; add 3% deodorant and sand evenly; then add 2.5% photochromic compound and sand evenly to make a mixture; spread the mixture into a refractory sagger , Conduct high-temperature melting at 1400°C to obtain a molten slurry; quench the slurry with water and break it into granules to obtain a skin glaze;

[0057] Step B. Weigh 30% skin texture glaze, 5% Solsperse 24000, 3% Span-80, 0.5% BYK052, 2% polystyrene resin and 59.5% environmentally friendly hydrocarbon solvent, and add it to a high-speed mixer for dispersion for 60 minutes; disperse The good mixture is put into a sand mill and sanded for 10 hours to obtain a ...

Example Embodiment

[0069] Example 3

[0070] A photochromic ceramic ink with dermatoglyphic effect and a preparation method thereof. The preparation method includes the following steps:

[0071] Step A. Preparation of dermatoglyph: 40% SiO2, 8% Al2O3, 1% (K2O+Na2O), 12% (CaO+MgO), 9% B2O3, 10% ZrO2, 13% V2O5 are mixed and sanded evenly; 0.5% antibacterial compound and sand evenly; add 5% deodorant and sand evenly; then add 1.5% photochromic compound and sand evenly to make a mixture; spread the mixture into a refractory sagger , Conduct high-temperature melting at 1400°C to obtain a molten slurry; quench the slurry with water and break it into granules to obtain a skin glaze;

[0072] Step B. Weigh 35% dermatoglyph, 3% Solsperse 24000, 2% Span-80, 0.8% BYK052, 1% polystyrene resin and 58.2% environmentally friendly hydrocarbon solvent, add them to a high-speed mixer for dispersion for 60 minutes; disperse The good mixture is put into a sand mill and sanded for 10 hours to obtain a semi-finished ink w...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Viscosityaaaaaaaaaa
Surface tensionaaaaaaaaaa
Login to view more

Abstract

The invention discloses photochromic ceramic ink with a leather effect and a preparation method thereof. The preparation method comprises the following steps that 1, leather glaze is prepared; 2, the leather glaze, a dispersion agent, a surface additive, an antifoaming agent and a binding agent are weighed in proportion, the balance is a solvent, and grinding is carried out to obtain a semi-finished product; 3, filtering is carried out to obtain the finished ink. Compared with ceramic ink with the leather effect in the prior art, the accessories are scientific, preparation is reasonable, the quality stability is good, the ink is used in cooperation with ceramic ink-jet printing pigment ink, the concave-convex vivid texture of a leather ceramic tile can be shown more fully and visually, the stereoscopic sense is high, the decoration effect of the ceramic tile is further improved, and the ink can also be widely applied to the fields of ceramic tiles, archaized bricks and the like. A photochromic compound, a deodorant and an antibacterial composite are reasonably matched, so that the ceramic ink has excellent bacterium resisting and antifouling functions, an excellent air purifying function and an excellent photochromic function, and the application range of the ceramic ink capable of sinking is widened.

Description

technical field [0001] The invention relates to the technical field of ceramics, in particular to a photochromic ceramic ink with skin texture effect and a preparation method thereof. Background technique [0002] Bacteria and mold, as pathogenic bacteria, are very harmful to humans, animals and plants, affecting people's health and even life-threatening, and bringing significant economic losses. Therefore, the research on antibacterial materials and their products has attracted people's attention day by day, and the demand for antibacterial products will constitute a huge market. [0003] Photochromism refers to photochromism caused by different light sources and color changes caused by physical phenomena such as reflection, refraction and interference. Photochromic materials are divided into organic photochromic materials and inorganic photochromic materials, among which inorganic photochromic materials are less studied, mainly including transition metal oxides, metal hal...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D11/50C09D11/30C09D11/38
CPCC09D11/50C09D11/30C09D11/38
Inventor 于庆九邱杰华
Owner FOSHAN GAOMING HAIDI CERAMIC RAW MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap