Wear-resisting antioxidant alloy spring steel and heat treatment process thereof

A spring steel and anti-oxidation technology, which is applied in the field of alloy spring steel, can solve the problems of inability to effectively meet the hardness requirements of high-level wear-resistant and anti-oxidation alloy spring steel and low hardness, and achieve high cost performance and overcome low hardness and high hardness. The effect of yield strength

Inactive Publication Date: 2016-12-07
ANHUI HONGQIAO METAL MFG
View PDF2 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, because it does not contain or contain a very small amount of carbide-forming alloying elements such as Cr, Mo, V, etc., the hardness is low, and it cannot effectively meet the hardness requirements of high-level wear-resistant and anti-oxidation alloy spring steel.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A wear-resistant and anti-oxidation alloy spring steel, the composition percentage of the alloy spring steel is: C: 0.380%, Cu: 0.280%, Mn: 0.160%, Si: 0.800-%, Cr: 0.900%, P: 0.040% , S: 0.030%, Ni: 0.300%, Al: 0.010%, V: 0.040%, B: 0.020-1.100%, and the balance is Fe and unavoidable impurities.

[0024] In the heat treatment process of wear-resistant and anti-oxidation alloy spring steel, the tempering temperature is 760°C, the holding time is 8h, and air-cooled; the quenching temperature is 800°C, the holding time is 50min, and water-cooling.

Embodiment 2

[0026] A wear-resistant and anti-oxidation alloy spring steel, the composition percentage of the alloy spring steel is: C: 0.360%, Cu: 0.260%, Mn: 0.150%, Si: 0.800%, Cr: 0.700%, P: 0.030%, S: 0.030%, Ni: 0.300%, Al: 0.008%, V: 0.020%, B: 0.080%, Be: 0.060%, and the balance is Fe and unavoidable impurities.

[0027] In the heat treatment process of wear-resistant and anti-oxidation alloy spring steel, the tempering temperature is 750°C, the holding time is 7h, and air-cooled; the quenching temperature is 820°C, the holding time is 80min, and water-cooling.

Embodiment 3

[0029] A wear-resistant and anti-oxidation alloy spring steel, the composition percentage of the alloy spring steel is: C: 0.550%, Cu: 0.450%, Mn: 2.200%, Si: 5.420%, Cr: 3.800%, P: 0.080%, S: 0.050%, Ni: 0.500%, Al: 0.050%, V: 0.100%, Mo: 0.050%, Sr: 0.031%, and the balance is Fe and unavoidable impurities.

[0030] In the heat treatment process of wear-resistant and anti-oxidation alloy spring steel, the tempering temperature is 740°C, the holding time is 8h, and air-cooled; the quenching temperature is 830°C, the holding time is 80min, and water-cooling.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses wear-resisting antioxidant alloy spring steel and a heat treatment process thereof. The spring steel comprises 0.360-0.550% of C, 0.260-0.450 % of Cu, 0.150-2.20% of Mn, 0.800-5.420% of Si, 0.700-3.800% of Cr, 0.030-0.080% of P, 0.030-0.050% of S, 0.300-0.500% of Ni, 0.008-0.050% of Al, 0.020-0.100% of V, and the balance Fe and inevitable impurities. According to the heat treatment process, the tempering temperature is 750+ / -10 DEG C, the temperature holding time is 6-8 h, and then air cooling is carried out; and the quenching temperature is 800-830 DEG C, the temperature holding time is 80-150 min, and then water cooling is carried out. Through the heat treatment process, the excellent wear-resisting antioxidant properties of the wear-resisting antioxidant alloy spring steel are realized, consumption of materials is reduced, and the production efficiency is improved.

Description

technical field [0001] The invention relates to an alloy spring steel, in particular to a wear-resistant and anti-oxidation alloy spring steel and its heat treatment process. Background technique [0002] A spring is a mechanical part that uses elasticity to work. Parts made of elastic materials are deformed under the action of external force, and return to their original shape after the external force is removed. Also known as "spring". Spring is an important component of mechanization and automation, and is widely used in aerospace, machinery manufacturing, transportation, instrumentation and other industries, and is generally made of spring steel. [0003] According to the GB / T standard, spring steel is divided into non-alloy spring steel (carbon spring steel) and alloy spring steel according to its chemical composition. Among them, alloy spring steel has a wide application prospect because the addition of alloy elements significantly improves the relaxation resistance...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/02C22C38/04C22C38/18C22C38/16C22C38/08C22C38/06C22C38/12C22C38/60C21D1/18
CPCC22C38/02C21D1/18C22C38/002C22C38/008C22C38/04C22C38/06C22C38/08C22C38/12C22C38/16C22C38/18C22C38/32C22C38/60
Inventor 余昌国余志强
Owner ANHUI HONGQIAO METAL MFG
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products