Manufacturing method for anti-ageing and shearing hardening type rubber composite for tires

A composite material and manufacturing method technology, applied in the direction of rolling resistance optimization, road transportation emission reduction, etc., can solve the problems of not being able to dynamically change the contact area between the tire and the ground, reducing tire resistance, unfavorable grip and braking, etc.

Inactive Publication Date: 2017-01-04
任立元
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

During the driving process of the vehicle, the contact area between the tire and the ground is large, which is conducive to gripping and braking, but it is not conducive to reducing the resistance of the tire; on the contrary, if the contact area between the tire and the ground is small, although it is beneficial to reduce the resistance of the tire, it is not conducive to reducing the resistance of the tire. grip and braking
It can be seen that the existing tires ca

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A kind of manufacturing method of aging-resistant and shear-hardened rubber composite material for tires, its specific steps are as follows:

[0020] Step ①: Utilize the existing milling technology to add the rubber mixture to the rubber mill. The formula of the rubber mixture is: 16 parts by weight of EPDM rubber, 18 parts by weight of butadiene rubber, and 18 parts by weight of natural rubber. It is 12 parts, the weight part of auxiliary agent is 23 parts, the weight part of organic / inorganic mixed pigment is 3 parts, and the weight part of flaky nano-carbon black is 10 parts, and the parameter of rubber mill is 500 seconds of mixing time, 145 degrees Celsius of temperature , pressure 0.6 MPa;

[0021] Step ②: Add a rubber foaming agent to the mixture obtained in step ①, the weight portion of the foaming agent is 12 parts, and the resulting mixture is then added to the rubber open mill. The parameters of the rubber open mill are 700 seconds of rubber mixing time, temp...

Embodiment 2

[0031] A kind of manufacturing method of aging-resistant and shear-hardened rubber composite material for tires, its specific steps are as follows:

[0032] Step ①: Utilize the existing milling technology to add the rubber mixture to the rubber mill. The formula of the rubber mixture is: 22 parts by weight of EPDM rubber, 22 parts by weight of butadiene rubber, and 22 parts by weight of natural rubber 10 parts, the weight part of auxiliary agent is 25 parts, the weight part of organic / inorganic mixed pigment is 3 parts, the weight part of flake nano-carbon black is 10 parts, and the parameter of rubber mill is 500 seconds of mixing time, 150 degrees Celsius of temperature , pressure 0.7MPa;

[0033] Step ②: Add a rubber foaming agent to the mixture obtained in step ①, the weight portion of the foaming agent is 15 parts, and the resulting mixture is then added to the rubber open mill. The parameters of the rubber open mill are 600 seconds of rubber mixing time, temperature 110...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Width sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a manufacturing method for an anti-ageing and shearing hardening type rubber composite for tires. The manufacturing method specifically comprises the following steps that firstly, a rubber mixture is added into a rubber open mill with an existing open technology; secondly, a rubber foaming agent is added into the mixture obtained in the first step; thirdly, a shearing thickening material is added into the mixture obtained in the second step; fourthly, the mixture obtained in the third step is extruded with a screw extruder for forming, and the anti-ageing and shearing hardening type rubber composite can be obtained. When tires rotate at a lower speed, the shearing thickening material in the rubber/shearing thickening composite can flow and deform, the rubber/shearing thickening composite is greatly deformed and becomes soft, and thus the group holding force of tires is enlarged; on the contrary, when tires rotate quickly, the rolling resistance of tires can be reduced; by adding flaky nanometer carbon black, the space sealing effect of rubber molecules can be improved, slow corrosion of ozone and ultraviolet can be well blocked, and the anti-ageing performance of rubber can be improved.

Description

technical field [0001] The invention relates to the technical field of production and manufacture of rubber materials, in particular to a method for producing an aging-resistant and shear-hardened rubber composite material for tires. Background technique [0002] At present, the contact area between the tire and the ground is mainly regulated by the air pressure inside the tire. If the air pressure in the tire is high, the contact area between the tire and the ground is small. When the air pressure in the tire decreases, the contact area between the tire and the ground increases. During the driving process of the vehicle, the contact area between the tire and the ground is large, which is conducive to gripping and braking, but it is not conducive to reducing the resistance of the tire; on the contrary, if the contact area between the tire and the ground is small, although it is beneficial to reduce the resistance of the tire, it is not conducive to reducing the resistance of ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L9/00C08L23/16C08L7/00C08L71/02C08K13/04C08K7/00C08K3/04C08K3/36C08K3/22C08K5/09C08K5/06C08J9/10
CPCC08J9/102C08J2203/04C08J2309/00C08J2323/16C08J2409/00C08J2423/16C08K2201/004C08K2201/011C08K2201/014C08L9/00C08L23/16C08L2201/08C08L2203/14C08L2205/025C08L2205/035C08L7/00C08L71/02C08K13/04C08K7/00C08K3/04C08K3/36C08K2003/2296C08K5/09C08K5/06Y02T10/86
Inventor 任立元
Owner 任立元
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka