Cellulose and liquid crystal composition and preparation method thereof

A liquid crystal composition, cellulose technology, applied in liquid crystal materials, chemical instruments and methods, etc., to achieve the effect of good fluidity

Active Publication Date: 2017-01-25
TIANJIN POLYTECHNIC UNIV
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In addition, there are also reports on the research of some liquid crystal compounds (for example, CN1632056A, CN1179153A, CN101863875A, CN10487311A), but these liquid crystal compounds are not applied in the field of cellulose liquid crystal

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Cellulose and liquid crystal composition and preparation method thereof
  • Cellulose and liquid crystal composition and preparation method thereof
  • Cellulose and liquid crystal composition and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0041] The present invention also provides a preparation method of the above-mentioned composition, comprising the steps of:

[0042] (1) mixing mesogen and cellulose with an ionic liquid to form a transparent solution;

[0043] (2) Keeping the transparent solution at 54-83° C. for more than 15 minutes to obtain a cellulose liquid crystal composition.

[0044] The types and compositions of the mesogen, cellulose, and ionic liquid of the present invention are as described above, and will not be repeated here.

[0045] In step (1), the mixing can be carried out at 70-100°C, preferably at 80-90°C. The mixing can be mixing mesogen and cellulose, and then mixing with ionic liquid; it can also be mixing mesogen and ionic liquid, and then mixing with cellulose; it can also be mixing cellulose and ionic liquid Mix and then mix with the mesogen. Preferably, the mesogen and the ionic liquid are mixed and then mixed with the cellulose. This facilitates the formation of mesogens. Acc...

preparation example 1

[0051] Put 31mmol of p-cyanobiphenol, 58mmol of 1,6-dibromohexane and 35mmol of potassium carbonate in acetone, heat to reflux at 60°C for 12h, remove acetone, add chloroform and water to the mixture, let stand to separate the liquid, and The chloroform in the organic phase was removed, and then recrystallized with ethyl acetate and petroleum ether (8:15 by volume) to obtain an intermediate. Intermediate 1 H NMR (DMSO, ppm): 7.91, 7.81, 7.70, 6.99 (phenyl, 8H), 4.02 (OCH 2 ,2H),3.50(BrCH 2 ,2H),2.0-1.3(CH 2 ,8H).

[0052] Put the intermediate and excess N-methylimidazole in acetonitrile, react at 80°C for 48 hours, remove the acetonitrile, add ether to remove the excess N-methylimidazole, and obtain the white product shown in the following formula—Mesogen A1 . Its purity is 98%, 1 HNMR (DMSO, ppm) is: 8.0-7.6 (phenyl, 8H), 9.15, 7.07, 6.99 (imidazolyl, 3H), 4.20 (OCH 2 ,2H),4.05(NCH 2 ,2H),3.85(CH 3 ,3H), 1.9-1.3(CH2,8H).

[0053]

preparation example 2

[0055] Put 31mmol of p-cyanobiphenol, 58mmol of 1,5-dibromopentane and 35mmol of potassium carbonate in acetone, heat to reflux at 65°C for 12h, remove acetone, add chloroform and water to the mixture, let stand to separate the liquid, and The chloroform in the organic phase was removed, and then recrystallized with ethyl acetate and petroleum ether (8:15 by volume) to obtain an intermediate. Intermediate 1 H NMR (DMSO, ppm): 7.91, 7.81, 7.70, 6.99 (phenyl, 8H), 4.02 (OCH 2 ,2H),3.50(BrCH 2 ,2H),2.0-1.3(CH 2 ,6H).

[0056] The intermediate and excess N-methylimidazole were placed in acetonitrile, reacted at 85°C for 48 hours, the acetonitrile was removed, and ether was added to remove excess N-methylimidazole, and the white product shown below—Mesogen A2 was obtained. Its purity is 98%, 1 H NMR (DMSO, ppm): 8.0-7.6 (phenyl, 8H), 9.15, 7.07, 6.99 (imidazolyl, 3H), 4.20 (OCH 2 ,2H),4.05(NCH 2 ,2H),3.85(CH 3 ,3H),1.9-1.3(CH 2 ,6H).

[0057]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
degree of polymerizationaaaaaaaaaa
Login to View More

Abstract

The invention discloses a cellulose and liquid crystal composition and a preparation method thereof. The cellulose and liquid crystal composition comprises ionic liquid, liquid crystal units and cellulose. The cellulose and liquid crystal composition is prepared by mixing the specific liquid crystal units with the cellulose in the ionic liquid and then conducting hydrogen-bonded self-assembly. The cellulose and liquid crystal composition is good in fluidity without changing an original structure of the cellulose.

Description

technical field [0001] The invention relates to a cellulose liquid crystal composition and a preparation method thereof. Background technique [0002] In recent years, with the deterioration of environmental pollution and the gradual depletion of non-renewable resources such as oil and natural gas, environmentally friendly and renewable resources have attracted increasing attention from society. Cellulose is the most abundant renewable resource on earth. It has the advantages of low price, good biocompatibility, degradability and no pollution to the environment. Therefore, the development and utilization of cellulose has become a hot topic in recent years. [0003] Due to its own structural characteristics, cellulose is difficult to melt and dissolve. Although the cellulose fiber produced by the traditional viscose method is very mature, it is still accompanied by problems such as high pollution and high energy consumption. As a good solvent for cellulose, ionic liquid ha...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09K19/34C09K19/52C09K19/54
CPCC09K19/348C09K19/52C09K19/542C09K2019/525
Inventor 宋俊刘芳程博闻韩扬扬王乐军
Owner TIANJIN POLYTECHNIC UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com