Dispersible full-degradable spunlaced nonwoven fabric and preparation method thereof

A spunlace non-woven fabric, fully degradable technology, applied in the direction of non-woven fabrics, textiles and paper making, to achieve the effect of high strength, good flushability and high output

Inactive Publication Date: 2017-02-01
绍兴柯桥天圣无纺有限公司
View PDF7 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the flushability of the spunlace nonwovens currently on the market needs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Dispersible full-degradable spunlaced nonwoven fabric and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A flushable and fully degradable spunlace non-woven fabric is prepared from raw materials of the following weight percentages: 15% viscose fiber, 10% tencel, and the balance is wood pulp.

[0028] Among them, the viscose fiber is a serrated flat viscose fiber with a length of 10mm; Tencel is a special short fiber produced by Lenzing Company with a length of 12mm; the length of wood pulp is 4mm.

[0029] The preparation method of the flushable and fully degradable spunlace nonwoven fabric of the present invention includes the following steps:

[0030] (1) Each raw material is separately dissolved and concentrated according to the feeding ratio;

[0031] (2) The concentrated raw materials are transported to the mixing tube for uniform mixing to form a slurry;

[0032] (3) Sizing;

[0033] (4) Forming, spunlace;

[0034] (5) Drying;

[0035] (6) Slitting.

[0036] Wherein, in step (1), the concentration of viscose fiber after concentration adjustment is 0.7%, the concentration of tencel...

Embodiment 2

[0042] A flushable and fully degradable spunlace non-woven fabric is prepared from the following raw materials in weight percentage: 30% viscose fiber, 5% tencel, and the balance is wood pulp.

[0043] Among them, the viscose fiber is a zigzag flat viscose fiber with a length of 12mm; Tencel is a special short fiber produced by Lenzing Company with a length of 10mm; the length of wood pulp is 2mm.

[0044] The preparation method of the flushable and fully degradable spunlace nonwoven fabric of the present invention includes the following steps:

[0045] (1) Each raw material is separately dissolved and concentrated according to the feeding ratio;

[0046] (2) The concentrated raw materials are transported to the mixing tube for uniform mixing to form a slurry;

[0047] (3) Sizing;

[0048] (4) Forming, spunlace;

[0049] (5) Drying;

[0050] (6) Slitting.

[0051] Wherein, in step (1), the concentration of viscose fiber after concentration adjustment is 0.7%, the concentration of tencel is ...

Embodiment 3

[0057] A flushable and fully degradable spunlace non-woven fabric is prepared from the following raw materials in weight percentage: 25% viscose fiber, 8% tencel, and the balance is wood pulp.

[0058] Among them, the viscose fiber is a zigzag flat viscose fiber with a length of 11mm; Tencel is a special short fiber produced by Lenzing Company with a length of 11mm; the length of wood pulp is 3mm.

[0059] The preparation method of the flushable and fully degradable spunlace nonwoven fabric of the present invention includes the following steps:

[0060] (1) Each raw material is separately dissolved and concentrated according to the feeding ratio;

[0061] (2) The concentrated raw materials are transported to the mixing tube for uniform mixing to form a slurry;

[0062] (3) Sizing;

[0063] (4) Forming, spunlace;

[0064] (5) Drying;

[0065] (6) Slitting.

[0066] Wherein, in step (1), the concentration of viscose fiber after concentration adjustment is 0.7%, the concentration of tencel is ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Lengthaaaaaaaaaa
Lengthaaaaaaaaaa
Login to view more

Abstract

The invention relates to a dispersible full-degradable spunlaced nonwoven fabric and a preparation method thereof, and belongs to the technical field of nonwoven fabric materials. The spunlaced nonwoven fabric is prepared from the following raw materials in percentage by weight: 15-30 percent of viscose, 5-10 percent of tencel and the balance of wood pulp. The dispersible full-degradable spunlaced nonwoven fabric has good dispersing performance and high strength, and the preparation method of the spunlaced nonwoven fabric has the advantages of short process flow, low defective percentage and high production efficiency; and the spunlaced nonwoven fabric is wide in raw material source, has various varieties, high yield and wide application range, and is environment-friendly.

Description

Technical field [0001] The invention relates to a flushable fully degradable spunlace non-woven fabric and a preparation method thereof, and belongs to the technical field of non-woven fabric materials. Background technique [0002] With the enhancement of environmental protection awareness, flushable fully degradable spunlace non-woven fabrics have appeared in the field of spunlace non-woven fabrics. However, the flushability of this kind of spunlace non-woven fabric currently on the market needs to be further improved, and its production process also needs to be further optimized. Summary of the invention [0003] The purpose of the present invention is to provide a flushable fully degradable spunlace nonwoven fabric and a preparation method thereof. The flushable fully degradable spunlace nonwoven fabric has good flushing performance and high strength, and the flushable fully degradable spunlace The preparation method of the thorn non-woven fabric has short process flow, low d...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D04H1/28D04H1/26D04H1/492D04H1/72
CPCD04H1/28D04H1/26D04H1/492D04H1/72
Inventor 韩旭厉伟
Owner 绍兴柯桥天圣无纺有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap