High-polymerization-degree polyvinyl chloride wear-resistant sole material

A polyvinyl chloride, high degree of polymerization technology, applied in the field of materials, can solve the problems of heavy weight and application restrictions, and achieve the effect of improving light weight and increasing wear resistance

Inactive Publication Date: 2017-02-22
WUXI CHANGAN SHUGUANG GLOVE FACTORY
View PDF8 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although alloy particles increase the wear resistance of the sole, their weight is relatively large, which is contrary to the goal of lightweighting the shoe, so its application is greatly restricted

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] High degree of polymerization polyvinyl chloride HPVC 100

[0020] Nitrile rubber 10

[0021] Dioctyl phthalate 40

[0022] Silica 10

[0023] Calcium carbonate filler 5

[0024] Graphene 5

[0025] Tungsten carbide-cobalt cemented carbide particles 2.

Embodiment 2

[0027] High degree of polymerization polyvinyl chloride HPVC 100

[0028] Nitrile rubber 20

[0029] Dioctyl phthalate 60

[0030] Silica 20

[0031] Calcium carbonate filler 15

[0032] Graphene 10

[0033] Tungsten carbide-cobalt cemented carbide particles 5.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Tensile strengthaaaaaaaaaa
Peel strengthaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-polymerization-degree polyvinyl chloride wear-resistant sole material. The sole material is prepared from, by weight, 100 parts of HPVC (high-polymerization-degree polyvinyl chloride), 10-20 parts of nitrile butadiene rubber, 40-60 parts of dioctyl phthalate, 10-20 parts of white carbon black, 5-15 parts of calcium carbonate filler, 5-10 parts of graphene and 2-5 parts of tungsten-cobalt carbide hard alloy particles. The high-polymerization-degree polyvinyl chloride wear-resistant sole material can improve wear resistance and can realize light weight, tensile strength is greater than 20MPa, elongation at break is greater than 370%, abrasion loss is smaller than 0.15cm<2> / 2km, stripping strength is greater than 4.8kN / m, and breaking strength is greater than 47kN / m.

Description

technical field [0001] The invention relates to the technical field of materials, in particular to a high-polymerization-degree polyvinyl chloride shoe sole material. Background technique [0002] The structure of the sole is quite complex. In a broad sense, it can include all the materials that make up the bottom, such as the outsole, midsole and heel. In a narrow sense, it only refers to the outsole. The common characteristics of general sole materials should be wear-resistant, water-resistant, oil-resistant, heat-resistant, pressure-resistant, impact-resistant, good elasticity, easy to fit the shape of the foot, and not easy to change after being shaped. Heat preservation, easy to absorb moisture, etc., and at the same time, it must cooperate with the midsole, which has a braking effect when walking and changing feet, so that it will not slip and is easy to stop. There are many types of sole materials, which can be divided into natural base materials and synthetic base m...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L27/06C08L9/02C08K13/02C08K3/36C08K3/26C08K3/04C08K3/14C08K3/08A43B13/04
CPCC08L27/06A43B13/04C08L9/02C08K13/02C08K3/36C08K2003/265C08K3/04C08K3/14C08K2003/0843
Inventor 缪建良
Owner WUXI CHANGAN SHUGUANG GLOVE FACTORY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com