Gas-liquid separating membrane, gas-liquid separating membrane supporting material compound and application

A gas-liquid separation membrane and support material technology, which is applied in the manufacturing field of gas-liquid separation membrane, gas-liquid separation membrane support material composite, and composite material parts, can solve the problems of difficult manufacturing, high cost, and high cost, and achieve the preparation process Simple, accurate and stable control, cheap raw materials

Active Publication Date: 2017-02-22
周伟
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] In the prior art, gas-liquid separation membranes generally use gas-liquid separation membranes made of PTEF microporous membranes, which are difficult and expensive to manufacture, and the production of PTEF microporous membranes has stretching process, air permeability and pressure resistance. Quantitative control is difficult, and there are also problems such as difficult manufacturing process and high cost.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Gas-liquid separating membrane, gas-liquid separating membrane supporting material compound and application
  • Gas-liquid separating membrane, gas-liquid separating membrane supporting material compound and application
  • Gas-liquid separating membrane, gas-liquid separating membrane supporting material compound and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0053] This embodiment provides a gas-liquid separation membrane, which is manufactured by the following method:

[0054]

[0055] The resin base material is polyurethane modified acrylic resin TKM-980, and the manufacturer is Dongguan Yade Resin New Material Co., Ltd.; the crosslinking agent is analytically pure toluene diisocyanate; Produced by Dachao Micro Industry (Suzhou) Co., Ltd.; the diluent is analytically pure acetone. The four components are stirred and dispersed by a mixer at a speed of 500 rpm for 0.5 hours, and then stirred and dispersed at a speed of 200 rpm for 2 hours to obtain a liquid paste resin composition with a viscosity of 6500 cps. The mixer is Jiangyin High-speed dispersing machine IGF2.2 produced by City Aida Machinery Co., Ltd. The above-mentioned liquid paste resin composition is coated on a silicone oil release film with a thickness of 20um at a speed of 5 m / min and a coating amount of 30 g / m2 with a coating machine. The coating machine is Sha...

Embodiment 2

[0057] This embodiment provides a gas-liquid separation membrane, which is manufactured by the following method:

[0058]

[0059] The resin base material is polyurethane resin HDW-20, and the manufacturer is Shanghai Huide Chemical Co., Ltd.; the crosslinking agent is analytically pure toluene diisocyanate; the breathable additive is kaolin powder with D50 at 500 nanometers, and the manufacturer is Inner Mongolia Mengxi kaolin powder Ltd; the diluent was analytically pure DMF. The four components were stirred and dispersed by a mixer at a speed of 500 rpm for 0.5 hours, and then stirred and dispersed at a speed of 200 rpm for 2 hours to obtain a liquid paste resin composition with a viscosity of 6200 cps. The above-mentioned liquid pasty resin composition is coated on a silicone oil release film with a thickness of 20um at a coating amount of 25 g / square meter with a coating machine, and dried at 150 degrees Celsius for 20 minutes in an oven, and then The cured film was p...

Embodiment 3

[0061] This embodiment provides a gas-liquid separation membrane, which is manufactured by the following method:

[0062]

[0063]

[0064] The resin base material is polyurethane resin HDW-20; the crosslinking agent is analytically pure toluene diisocyanate; the breathable additive is kaolin powder with D50 at 500 nanometers; the diluent is analytically pure DMF. The four components were stirred and dispersed by a mixer at a speed of 500 rpm for 0.5 hours, and then stirred and dispersed at a speed of 200 rpm for 2 hours to obtain a liquid paste resin composition with a viscosity of 4000 cps. The above-mentioned liquid pasty resin composition is coated on a silicone oil release film with a thickness of 20um with a coating amount of 25 g / square meter by a coating machine, and the coated smear is placed in a temperature of 50 degrees Celsius. After soaking in water for 25 minutes, take it out and dry it in an oven at 110 degrees Celsius, and peel off the cured film from th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
thicknessaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a gas-liquid separating membrane, a gas-liquid separating membrane supporting material compound and an application. The gas-liquid separating membrane is prepared from, in weight percentage, 20%-89.9% of resin binders, 0.05%-10% of cross-linking agents, 0.05%-10% of breathable additives and 10%-60% of diluents. Raw materials selected for the gas-liquid separating membrane are inexpensive, the preparation process is simple, the prepared gas-liquid separating membrane has high hydraulic resistance and gas transmission rate, the prepared gas-liquid separating membrane supporting material compound is used for the field of composite components prepared by resin infusion curing molding, and the quality of cured finished products can be effectively ensured.

Description

technical field [0001] The invention relates to a gas-liquid separation membrane, a gas-liquid separation membrane support material composite and its application, and is specifically applied in the field of resin infusion solidification molding to manufacture composite material components, including wind turbine blades, aircraft wing bodies, ship shells, etc. Manufacture of composite parts. Background technique [0002] In the prior art, gas-liquid separation membranes are generally made of PTEF microporous membranes, which are difficult and expensive to manufacture, and the production of PTEF microporous membranes has stretching process, air permeability and pressure resistance. Quantitative control is difficult, and there are also problems such as difficult manufacturing process and high cost. Contents of the invention [0003] The technical problem to be solved by the present invention is to overcome the deficiencies of the prior art and provide a gas-liquid separation...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L75/14C08L75/04C08K3/26C08K5/29C08K3/34C08J5/04C08J5/18
CPCC08J5/043C08J5/18C08J2375/04C08J2375/14C08K3/26C08K3/346C08K5/29C08K2003/265C08K2201/003C08L75/14C08L75/04
Inventor 周伟
Owner 周伟
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com