Paper based friction material with carbon fibers enhanced and its preparation method

A paper-based friction material and a technology for friction materials, applied in chemical instruments and methods, other chemical processes, etc., can solve the problems of inappropriateness, inability to disperse scraps of friction material base paper, low strength, etc., and achieve the effect of reducing production costs.

Inactive Publication Date: 2003-10-08
陕西航沣新材料有限公司
View PDF3 Cites 48 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, before the base paper of this kind of paper-based friction material is impregnated with adhesive, its strength is too low, and the stamping operation is easily deformed. After the impregnated resin binder is cured, the scraps of the base paper of friction material that are punched out cannot be dispersed in water and cannot be reused.
[0003] Chinese patent 99114959.9 discloses a paper-based friction material with bamboo fiber or / and wood fiber as the substrate and its manufacturing method. This process is obviously not suitable for high-performance fibers such as carbon fibers

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Paper based friction material with carbon fibers enhanced and its preparation method
  • Paper based friction material with carbon fibers enhanced and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] Embodiment 1: a carbon fiber reinforced paper-based friction material, containing carbon fiber, Kevlar fiber, barite, kaolin, molybdenum disulfide, alumina, graphite powder, phenolic resin and cashew nut shell liquid modified phenolic resin, and its mass percentage group It becomes: carbon fiber 5-35%, Kevlar fiber 2-15%, barite 3-20%, kaolin 7-15%, molybdenum disulfide 1-10%, aluminum oxide 2-15%, graphite powder 2- 25%, 2-15% of phenolic resin, 25-55% of phenolic resin modified by cashew nut shell liquid.

[0020] The reinforcing fibers are any one or more of carbon fibers or carbon fibers and Kevlar fibers, glass fibers, polyacrylonitrile fibers, ceramic fibers, phenolic resin fibers, and carbon fiber pre-oxygen filaments.

[0021] The friction performance modifier can be any one or several of molybdenum disulfide, alumina and graphite powder.

[0022] The filler can be any one or several of barite and kaolin.

[0023] The adhesive is cashew nut shell liquid-modifi...

Embodiment 2

[0029] Embodiment 2: a carbon fiber reinforced paper-based friction material, comprising the friction material scraps, carbon fiber, Kevlar fiber, barium sulfate, kaolin, molybdenum disulfide, alumina, graphite powder, phenolic resin and modified phenolic resin of Example 1, Its mass percentage composition is: scrap 15-60%, carbon fiber 2-20%, Kevlar fiber 1-8%, barite 1-10%, kaolin 3-8%, molybdenum disulfide 0.5-5%, dioxide trioxide Aluminum 1-7%, graphite powder 1-15%, phenolic resin 1-12%, cashew nut shell liquid modified phenolic resin 25-55%.

[0030] The preparation method is the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

A carbon fibre reinforced paper-base friction material is prepared from reinforcing fibres (7-40 mass%), friction performance regulator (5-35 mass%), filler (11-35 mass%) raw paper reinforcing agnt (2-15 mass%), and adhesive (25-55 mass%) through adding them to water, beating, shaping, baking mechanical punching, immersing in adhesive, hot pressing, solidifying and machining to obtain friction disk. Its advantage is high utilization rate of raw materials.

Description

technical field [0001] The invention relates to a carbon fiber reinforced paper-based friction material and a preparation method thereof, in particular to a carbon fiber-reinforced paper-based friction material for friction plates and a preparation method thereof. Background technique [0002] Paper-based friction material is a wet friction material produced by a papermaking process. It is the basic material for preparing friction plates and is widely used in automatic transmissions and wet braking devices to transmit torque, decelerate and brake. US patent [Kitahara Shun, Umezawa, Shigeki.Wet friction material USP 6,130,177] describes the method of preparing single-layer paper-based friction material using mixed fibers of carbon fiber and aramid fiber, literature [Andrew Kears, Dagobert Wagner.Carbon fiber for wet friction applications .SAE Paper 972754] and U.S. Patent [Yesnik, M.A..USP 6,194,059] introduced a method for preparing double-layer paper-based friction material...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09K3/14
Inventor 李贺军付业伟李克智张秀莲
Owner 陕西航沣新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com