A kind of hot-rolled steel strip for ct90 continuous pipe and its production method

Abstract

A hot-rolled steel strip for a CT90 level continuous pipe comprises chemical components including, by weight percent, 0.05%-0.10% of C, 0.10%-0.30% of Si, 0.40%-0.90% of Mn, smaller than or equal to 0.015% of P, smaller than or equal to 0.0020% of S, 0.25%-0.40% of Cu, 0.15%-0.35% of Ni, 0.50%-1.00% of Cr, 0.10%-0.20% of Mo, 0.020%-0.050% of Nb, smaller than or equal to 0.010% of V, 0.010%-0.030% of Ti, smaller than or equal to 0.0050% of N, 0.015%-0.060% of Al, 0.0008%-0.0025% of Ca and 0.0008%-0.0015% of B. A production method comprises the steps that a cast ingot is heated after smelting and ingot casting; rough rolling is conducted; finish rolling is conducted; cooling is conducted in three stages; and after a steel roll is rolled, the steel roll is placed in a thermal insulating wall to be subjected to slow cooling. Through adding of the B, the content of the C is reduced, structure segregation of the steel is improved, and it is ensured that the HIC resisting and SSCC resisting performance is qualified; through composite adding of the Cu and the Ni, the hot shortness of the Cu is improved; staging controlled cooling is conducted, regulation and control over a complex phase structure are achieved, and the yield ratio of the steel strip is reduced.

Description

technical field [0001] The invention relates to pipeline steel and a production method thereof, in particular to a hot-rolled steel strip for CT90 continuous pipe and a production method thereof. Background technique [0002] Coiled tubing is a new type of pipe used in the oil drilling and production industry. The flexible steel pipe with a length of several thousand meters to tens of thousands of meters is coiled on the coil. It is opened from the coil during operation and coiled on the coil again after the operation. use. Compared with traditional oil well tubing, coiled tubing operation is more flexible, and has the advantages of snubbing operation, continuous hoisting, small equipment volume, fast operation cycle and low cost. [0003] After searching, the Chinese patent application number is 200710168545.3, which discloses "a steel for high plastic coiled tubing and its manufacturing method". After analysis, its Cr content is relatively low, and the hardenability and c...

AI Technical Summary

Problems solved by technology

[0003] After searching, the Chinese patent application number is 200710168545.3, which discloses "a steel for high plastic coiled tubing and its manufacturing method". After analysis, its Cr content is relatively low, and the hardenability and corrosion resistance of coiled tubing are relatively low. Poor; due to the addition of 0.15-0.30% Cu without adding Ni at the same time, there is hot brittleness; its alloy content is relatively low, and the strength similar to this patent is achieved through a low cooling temperature, and its low-temperature toughness is relatively poor

[0004] The Chinese patent application number is 200810040895.6, which discloses "a CT90 steel for coiled tubing and its manufacturing method". Due to the high content of C and Mn, serious segregation will occur in the steel strip, and high-frequency resistance welding Hook-shaped crack defects also appear in the pipe-making process; at the same time, its composition design contains high V, which is unfavorable to the toughness and plasticity of the steel strip; its yield ratio is above 0.90, and the deformability is poor, which is not conducive to the fatigue performance of the steel pipe

Images