A liquid die forging aluminium alloy and a preparing method thereof

A technology of liquid die forging and aluminum alloy, which is applied in the field of liquid die forging aluminum alloy and its preparation, can solve problems such as waste of resources, achieve the effects of reducing production costs, improving use value, and broad application prospects

Active Publication Date: 2017-04-19
广州金邦液态模锻技术有限公司
View PDF4 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, most of the waste aluminum in my country is mainly used to regenerate cast aluminum alloys with low added value. The alloy elements such as silicon, copper, and magnesium contained in waste aluminum have not been effectively utilized, resulting in a huge waste of resources.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] The raw material composition of liquid die forging aluminum alloy is: 45% scrap aluminum wheels of automobiles (chemical composition and mass percentage are: Si 6.8%, Mg 0.6%, Cu 0.01%, Mn 0.4%, Fe 1.1%, Zn 0.01 %, Ti 0.1%, the balance is Al and unavoidable impurities), 25% of waste automobile aluminum gearbox housing (chemical composition and mass percentage: Si 9.9%, Mg0.79%, Cu 0.5%, Mn 1.1 %, Fe 0.5%, Zn 0.01%, Ti 0.02%, the balance is Al and unavoidable impurities), 10% waste aluminum cans (chemical composition and mass percentage: Mn 0.9%, Mg 0.2%, Si 0.3% , Cu 0.2%, Fe0.4%, Cr 0.2%, Zn 0.2%, Ti 0.05%, the balance is Al and unavoidable impurities), 5% waste aluminum wire and cable (chemical composition and mass percentage: Zr 0.5 %, Si 1.1%, Mg 0.5%, Cu 1.5%, Mn 1.0%, Ti 0.35%, Zn 0.2%, Fe 0.4%, the balance is Al and unavoidable impurities), 15% aluminum ingot (chemical composition And the mass percentage is: Si0.01%, Mg 0.01%, Cu 0.05%, Mn 0.01%, Zn 0.01%, Fe 0....

Embodiment 2

[0034]The composition of raw materials for liquid die forging aluminum alloy is: 50% scrap aluminum wheels of automobiles (chemical composition and mass percentage are: Si 7.5%, Mg 1.2%, Cu 0.05%, Mn 0.4%, Fe 1.2%, Zn 0.02%, Ti 0.15%, the balance is Al and unavoidable impurities), 30% waste automobile aluminum gearbox housing (chemical composition and mass percentage: Si10%, Mg 0.9%, Cu 1.0%, Mn 1.2% , Fe 0.6%, Zn 0.01%, Ti 0.02%, the balance is Al and unavoidable impurities), 11% waste aluminum cans (chemical composition and mass percentage: Mn 1.5%, Mg 0.4%, Si 0.5%, Cu 0.2%, Fe 0.4%, Cr 0.05%, Zn 0.1%, Ti 0.01%, the balance is Al and unavoidable impurities), 6% waste aluminum wire and cable (chemical composition and mass percentage: Zr 1.5%, Si 1.5%, Mg 1.4%, Cu 2.1%, Mn 0.9%, Ti 0.01%, Zn 0.1%, Fe 0.4%, the balance is Al and unavoidable impurities), 3% aluminum ingot (chemical composition and quality The percentages are: Si 0.01%, Mg 0.01%, Cu 0.02%, Mn 0.01%, Zn 0.02%, F...

Embodiment 3

[0043] The composition of the raw materials of liquid die forging aluminum alloy is: 47% scrap aluminum wheels of automobiles (chemical composition and mass percentage are: Si 7.1%, Mg 1.7%, Cu 0.04%, Mn 0.35%, Fe 0.8%, Zn 0.02%, Ti 0.15%, the balance is Al and unavoidable impurities), 26% of waste automobile aluminum gearbox housing (chemical composition and mass percentage: Si9.8%, Mg 0.7%, Cu 0.8%, Mn 1.1%, Fe 0.6%, Zn 0.01%, Ti 0.1%, the balance is Al and unavoidable impurities), 12% waste aluminum cans (chemical composition and mass percentage: Mn 1.4%, Mg 0.3%, Si 0.2 %, Cu 0.2%, Fe 0.4%, Cr 0.1%, Zn 0.1%, Ti 0.01%, the balance is Al and unavoidable impurities), 8% waste aluminum wire and cable (chemical composition and mass percentage: Zr 1.5 %, Si 0.5%, Mg 0.5%, Cu 1.5%, Mn 0.8%, Ti 0.15%, Zn 0.2%, Fe 0.1%, the balance is Al and unavoidable impurities), 7% aluminum ingot (chemical composition And the mass percentage is: Si0.01%, Mg 0.01%, Cu 0.01%, Mn 0.01%, Zn 0.02%,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
elongationaaaaaaaaaa
Login to view more

Abstract

A liquid die forging aluminium alloy and a preparing method thereof are disclosed. Raw materials of the aluminum alloy include 45-50% by mass of waste automobile aluminum wheels, 25-30% by mass of waste automobile aluminum gearbox shells, 10-12% by mass of waste aluminum pop cans and 5-8% by mass of waste aluminum electric wires and cables, with the balance being aluminium ingots. Waste aluminum is adopted as the main raw material. The liquid die forging aluminium alloy having high performance is directly regenerated through optimizing composition of the waste aluminum raw materials, thus increasing the using value of the waste aluminum and reducing the production cost of the liquid die forging aluminium alloy. The produced liquid die forging aluminium alloy has advantages of high strength and good plasticity, can be used as load-bearing structure parts of automobiles, electronic products, mechanical equipment, aviation and spaceflight, weapon equipment, and the like, and has a wide application prospect.

Description

technical field [0001] The invention belongs to the field of alloy preparation, and in particular relates to a liquid die forging aluminum alloy and a preparation method thereof. Background technique [0002] Liquid die forging technology is a metal forming process that has both casting characteristics and is similar to die forging. It directly pours a certain amount of molten metal into the mold cavity, and solidifies and forms under the action of continuous mechanical static pressure. Liquid die forging technology can eliminate the shrinkage cavity formed by solidification and shrinkage, and obtain high-strength parts with fine and uniform grains and dense structure. Liquid die forging technology is widely used in automobiles, electronic appliances, mechanical equipment, aerospace and weaponry and other fields. [0003] With the development and wide application of liquid die forging technology, the demand for high-performance liquid die forging aluminum alloys is also inc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C1/03C22C1/06C22C21/00C22F1/04B22D18/02
CPCB22D18/02C22C1/026C22C1/03C22C1/06C22C21/00C22F1/04
Inventor 黄毅王顺成吴春林裴连进郝勇凌筱燕
Owner 广州金邦液态模锻技术有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap