Highly protective polyimide flame-retardant garment fabric and heat setting method thereof

A technology of polyimide and polyimide fiber, which is applied in the direction of fabric surface trimming, heating/cooling fabric, textile, etc., can solve the problem of not being able to meet the shaping requirements of polyimide fabric, the time is short, and the contact temperature is low and other problems, to achieve the effect of increasing the contact surface, small internal stress and stable structure

Inactive Publication Date: 2017-04-26
JIANGSU AOSHEN HI TECH MATERIALS CO LTD
View PDF2 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Polyimide fiber is a high-performance flame-retardant fiber with a limiting oxygen index of 38%. It is a non-combustible fiber, and the long-term use temperature of polyimide fiber is 260°C. Generally: guide cylinder→warping→drawing-in heald→on machine→weaving→finishing (washing, heat setting, etc.)→piece inspection→finished product, etc. In the traditional setting process, the setting temperature generally does not exceed 200°C. The time is about a few seconds. The time for the fabric to pass through the sizing machine is very short, and the contact temperature is relatively low, which cannot meet the sizing requirements of polyimide fabrics. Therefore, a new sizing process is designed, which is suitable for polyimide fabrics. The shaping process is an indispensable step, which has certain guiding significance for the development of polyimide downstream products in the future

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Highly protective polyimide flame-retardant garment fabric and heat setting method thereof
  • Highly protective polyimide flame-retardant garment fabric and heat setting method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A high-protection polyimide flame-retardant clothing fabric, which is sewn by a combination of inner and outer layers of fabrics, the inner layer is woven from polyimide fiber yarn and polyimide filaments, The outer layer is a cloth surface with raised grids woven from polyimide fiber yarn and polyimide filament, the specification of the polyimide fiber yarn is 40S, and the polyimide fiber yarn The specification of the filament is 300D.

[0021] The weaving method of the outer fabric of the high-protection polyimide flame-retardant clothing is: select polyimide fiber yarn 40S, polyimide filament 300D according to figure 1 Weaving into woven fabrics, in which area 1 is designed according to the satin weave, and a polyimide filament is incorporated in area 2, so that through yarns and filaments of different thicknesses, a lattice fabric with raised weave points is formed , increasing the contact surface of the fabric.

[0022] The heat-setting process of the high-protec...

Embodiment 2

[0024] A high-protection polyimide flame-retardant clothing fabric, which is sewn by a combination of inner and outer layers of fabrics, the inner layer is woven from polyimide fiber yarn and aramid filaments, the The outer layer is a cloth surface with raised lattice woven by polyimide fiber yarn and aramid filament, the specification of the polyimide fiber yarn is 36S, and the specification of the aramid filament is 300D .

[0025] The weaving method of the outer fabric of the high-protection polyimide flame-retardant clothing is: select polyimide fiber yarn 36S, aramid filament 300D according to figure 2 Woven into a woven fabric, wherein the area 3 is designed according to the satin weave, and a polyimide fiber yarn and an aramid filament are incorporated in the area 4. Through the yarns and filaments of different thicknesses, a convex pattern is formed. The lattice fabric with organized points increases the contact surface of the fabric and makes the fabric form a uniqu...

Embodiment 3

[0028] A high-protection polyimide flame-retardant clothing fabric, which is sewn by a combination of inner and outer layers of fabrics, the inner layer is woven from polyimide fiber yarn and aramid filaments, the The outer layer is a cloth surface with raised lattice woven by polyimide fiber yarn and aramid filament, the specification of the polyimide fiber yarn is 23S, and the specification of the aramid filament is 300D .

[0029] The weaving method of the outer fabric of the high-protection polyimide flame-retardant clothing is: select polyimide fiber yarn 23S, aramid filament 300D according to figure 2 Woven into woven fabrics, in which area 3 is designed according to the satin weave, and two aramid filaments are incorporated in area 4, and a lattice fabric with raised weave points is formed through yarns and filaments of different thicknesses, increasing the The contact surface of the fabric makes the fabric form a unique style.

[0030] The heat-setting process of th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a highly protective polyimide flame-retardant garment fabric and a heat setting method thereof and relates to the technical field of flame-retardant fabrics. The highly protective polyimide flame-retardant garment fabric is prepared from an inner layer and an outer layer through sewing. The inner layer is prepared from polyimide fiber yarn and flame-retardant filaments through weaving. The outer layer is a cloth surface with raised grids and is prepared from polyimide fiber yarn and flame-retardant filaments through weaving. The highly protective polyimide flame-retardant garment fabric has good fire resistance and heat-insulating functions, can be used at a high temperature for a long time, is comfortable, and reduces hair slip. Through heat setting, the fabric is smooth and flat and size stability.

Description

technical field [0001] The invention relates to the technical field of flame-retardant fabrics, in particular to a high-protection polyimide flame-retardant clothing fabric and a heat-setting process. Background technique [0002] With the progress of human society and the development of science and technology, people's living environment is surrounded by various high-rise buildings and high-tech products. In daily production and life, the form and frequency of fire are no longer single. The environment tests the rescuers, and the overweight fireproof clothing also limits the mobility of the rescuers, and the physical exertion of the rescuers is also relatively large. Therefore, it is of great value and significance to develop a fire-resistant clothing with high protective performance, comfortable wearing and light weight for the rescuers who shuttle on the front line of the fire scene. [0003] Polyimide fiber is a high-performance flame-retardant fiber with a limiting oxy...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B32B27/28B32B27/36B32B27/34B32B27/02B32B27/12B32B37/06B32B3/30D03D15/12D03D15/00D03D13/00D04B1/16D06C7/02D03D15/283D03D15/50D03D15/513D03D15/52
CPCD03D13/00D04B1/16D06C7/02B32B3/30B32B5/02B32B5/08B32B5/26D10B2331/04D10B2331/021D10B2331/02D10B2501/04B32B2250/20B32B2262/0276B32B2262/0261B32B2262/02B32B2262/14B32B2307/7145B32B2307/306B32B2307/3065B32B2307/304D03D15/43D03D15/513
Inventor 刘泽含
Owner JIANGSU AOSHEN HI TECH MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap