Flame-retardant reinforced polyurethane grouting material and preparation method thereof

A grouting material, polyurethane technology, applied in chemical instruments and methods, other chemical processes and other directions, can solve the problems of secondary combustion flame propagation speed, low melting point, etc., and achieve moderate curing speed, simple preparation method, and convenient construction.

Inactive Publication Date: 2017-04-26
江苏卓美聚氨酯科技有限公司
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing grouting materials have a low melting point and produce molten droplets when exposed to fire at high temperature, which is prone to secondary combustion and has an extremely fast flame propagation speed

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] A flame-retardant reinforced polyurethane grouting material proposed by the present invention comprises the following raw materials in parts by weight: 15 parts of polyether polyol, 23 parts of polyurethane reactive monomer, 15 parts of polyester, 3 parts of compatibilizer, and amine catalyst 1.2 parts, 0.5 parts of tin catalyst, 2.1 parts of flame retardant, 15 parts of isocyanate, 1 part of plasticizer, 12 parts of organic solvent, 16 parts of flame retardant polyol, 16 parts of chlorophosphate, 1.5 parts of antimony trioxide .

[0018] The present invention also proposes a method for preparing a flame-retardant reinforced polyurethane grouting material, comprising the following steps:

[0019] S1. Weigh polyether polyols, polyurethane reactive monomers, polyesters, isocyanates, flame-retardant polyols and chlorophosphates according to the proportions, and heat and stir them in a reactor with a stirrer for 11 minutes to obtain the first It is expected that the temper...

Embodiment 2

[0024] A flame-retardant reinforced polyurethane grouting material proposed by the present invention includes the following raw materials in parts by weight: 25 parts of polyether polyol, 30 parts of polyurethane reactive monomer, 25 parts of polyester, 7 parts of compatibilizer, and amine catalyst 2 parts, 1.5 parts of tin catalyst, 3.5 parts of flame retardant, 25 parts of isocyanate, 3.5 parts of plasticizer, 20 parts of organic solvent, 25 parts of flame retardant polyol, 25 parts of chlorophosphate, 3 parts of antimony trioxide .

[0025] The present invention also proposes a method for preparing a flame-retardant reinforced polyurethane grouting material, comprising the following steps:

[0026] S1. Weigh polyether polyols, polyurethane reactive monomers, polyesters, isocyanates, flame-retardant polyols and chlorophosphates according to the proportions, and heat and stir them in a reactor with a stirrer for 15 minutes to obtain the first It is expected that the temperat...

Embodiment 3

[0031] A flame-retardant reinforced polyurethane grouting material proposed by the present invention comprises the following raw materials in parts by weight: 28 parts of polyether polyol, 33 parts of polyurethane reactive monomer, 28 parts of polyester, 8 parts of compatibilizer, and amine catalyst 2.3 parts, 1.8 parts of tin catalyst, 4 parts of flame retardant, 28 parts of isocyanate, 4 parts of plasticizer, 23 parts of organic solvent, 28 parts of flame retardant polyol, 28 parts of chlorophosphate, 3.5 parts of antimony trioxide .

[0032] The present invention also proposes a method for preparing a flame-retardant reinforced polyurethane grouting material, comprising the following steps:

[0033] S1. Weigh polyether polyols, polyurethane reactive monomers, polyesters, isocyanates, flame-retardant polyols and chlorophosphates according to the proportions, and heat and stir them in a reactor with a stirrer for 18 minutes to obtain the first It is expected that the tempera...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a flame-retardant reinforced polyurethane grouting material comprising the following raw materials in parts by weight: 15-30 parts of polyether glycol, 20-35 parts of polyurethane reactive monomers, 15-30 parts of polyester, 2-10 parts of a compatilizer, 1-2.5 parts of an amine catalyst, 0-2 parts of a tin catalyst, 2-5 parts of a flame retardant, 15-30 parts of isocyanate, 1-5 parts of a plasticizer, 10-25 parts of an organic solvent, 15-30 parts of flame-retardant polyalcohol, 15-30 parts of halogenated phosphate and 1-4 parts of antimony trioxide. A preparation method of the flame-retardant reinforced polyurethane grouting material is simple, and the prepared grouting composition can be flame-retardant and is suitable for popularization.

Description

technical field [0001] The invention relates to the technical field of grouting materials, in particular to a flame-retardant reinforced polyurethane grouting material and a preparation method thereof. Background technique [0002] The grouting material is selected to achieve a certain engineering purpose, can exist in liquid form, and is convenient to use hydraulic pressure, air pressure or electrochemical principles to inject into the internal space of the corresponding medium, such as cracks, cracks, pores, etc., and has the ability to cement and solidify, so that the medium The general term for a class of engineering materials whose leakage channels are blocked and whose physical properties and mechanical properties are improved. However, the existing grouting materials have a low melting point and produce molten droplets when exposed to fire at a high temperature, which is prone to secondary combustion and has an extremely fast flame propagation speed. Therefore, we pr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08G18/42C08G18/48C08G18/66C08K3/22C08K5/521C08L75/06C08L75/08C09K3/10
CPCC08G18/4018C08G18/42C08G18/48C08G18/66C08K3/2279C08K5/521C08L75/06C08L75/08C08L2201/02C09K3/10
Inventor 杨帅杨承尧
Owner 江苏卓美聚氨酯科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com