Surface paint for automobile production and preparation method thereof

A technology for surface coatings and automobiles, applied in coatings and other directions, can solve problems such as no antibacterial function, and achieve the effect of low production cost and simple process

Inactive Publication Date: 2017-04-26
CHONGQING BAISHIDE BUILDING MATERIALS
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The current industrialized products do not have antibacterial function

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] The surface coating for automobile production in this embodiment is composed of the following mass components: 6 parts of zinc oxide, 15 parts of conch shell powder, 8 parts of polyacrylamide, 10 parts of xylene, 8 parts of phthalic anhydride amine, nano 4 parts of aluminum dioxide, 12 parts of polyvinyl butyral, 0.5 part of vinyl acetate, 0.1 part of isophorone diisocyanate, 5 parts of dry powdered sucrose, and 1 part of zinc borate.

[0018] Above-mentioned automobile production surface coating preparation method comprises the steps:

[0019] (1) Add the above-mentioned conch shell powder into water, and then sequentially add the above-mentioned parts by mass of zinc oxide, polyacrylamide, phthalic anhydride amine, nano-alumina, polyvinyl butyral, iso Phorne diisocyanate, dry powdered sucrose, zinc borate, high-speed dispersion;

[0020] (2) Add the xylene in the above mass fraction, and disperse at high speed;

[0021] (3) Add the vinyl acetate in the above mass fr...

Embodiment 2

[0024] The surface coating for automobile production in this embodiment is composed of the following mass components: 10 parts of zinc oxide, 30 parts of conch shell powder, 16 parts of polyacrylamide, 25 parts of xylene, 10 parts of phthalic anhydride amine, nano 10 parts of aluminum dioxide, 20 parts of polyvinyl butyral, 1 part of vinyl acetate, 0.5 parts of isophorone diisocyanate, 15 parts of dry powdered sucrose, 3 parts of zinc borate.

[0025] Above-mentioned automobile production surface coating preparation method comprises the steps:

[0026] (1) Add the above-mentioned conch shell powder into water, and then sequentially add the above-mentioned parts by mass of zinc oxide, polyacrylamide, phthalic anhydride amine, nano-alumina, polyvinyl butyral, iso Phorne diisocyanate, dry powdered sucrose, zinc borate, high-speed dispersion;

[0027] (2) Add the xylene in the above mass fraction, and disperse at high speed;

[0028] (3) Add the vinyl acetate in the above mass f...

Embodiment 3

[0031] The surface coating for automobile production in this embodiment is composed of the following mass components: 8 parts of zinc oxide, 18 parts of conch shell powder, 12 parts of polyacrylamide, 13 parts of xylene, 9 parts of phthalic anhydride amine, nano 12 parts of aluminum dioxide, 16 parts of polyvinyl butyral, 0.75 parts of vinyl acetate, 0.3 parts of isophorone diisocyanate, 10 parts of dry powdered sucrose, and 2 parts of zinc borate.

[0032] Above-mentioned automobile production surface coating preparation method comprises the steps:

[0033] (1) Add the above-mentioned conch shell powder into water, and then sequentially add the above-mentioned parts by mass of zinc oxide, polyacrylamide, phthalic anhydride amine, nano-alumina, polyvinyl butyral, iso Phorne diisocyanate, dry powdered sucrose, zinc borate, high-speed dispersion;

[0034] (2) Add the xylene in the above mass fraction, and disperse at high speed;

[0035] (3) Add the vinyl acetate in the above ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to surface paint for automobile production. The surface paint comprises, by mass, 6-10 parts of zinc oxide, 15-30 parts of trumpet shell powder, 8-16 parts of polyacrylamide, 10-25 parts of xylene, 8-10 parts of o-phthalic anhydride amine, 4-10 parts of nano aluminum dioxide, 12-20 parts of polyvinyl butyral, 0.5-1 part of vinyl acetate, 0.1-0.5 part of isophorone diisocyanate, 5-15 parts of dry cane sugar powder and 1-3 parts of zinc borate. The preparation process of the surface paint for automobile production is conducted at normal temperature and normal pressure, new devices do not need to be added, the technology is simple, and the production cost is low.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to a surface coating for automobile production and a preparation method thereof. Background technique [0002] With the rapid development of the economy, people's living standards have been greatly improved, and people's awareness of health has been continuously enhanced, especially in recent years [0003] The outbreak and prevalence of various diseases have made people pay more and more attention to the serious harm caused by various infectious diseases and diseases caused by harmful bacteria to human health. This type of product of industrialization does not have antibacterial function at present. With the improvement of people's living standards and the strengthening of hygiene awareness, antibacterial products will inevitably be developed. In addition, some coatings have a good effect on flame retardant, which is convenient and better flame retardant, and improves the safety...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D4/00C09D4/06C09D7/12
Inventor 王杨崴
Owner CHONGQING BAISHIDE BUILDING MATERIALS