A kind of handicraft and its preparation method

A technology of handicrafts and parts by weight, which is applied in the field of handicraft technology development, can solve problems such as narrow application range, and achieve the effects of simple preparation method, high tensile and compressive strength, and good shaping

Active Publication Date: 2018-11-16
ZHANGYE CIY DANXIA FENGYUN TOURISM & CULTURE DEV
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The scope of application of the handicraft is relatively narrow

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A handicraft, comprising the following raw materials in parts by weight: 50 parts of sepiolite powder, 60 parts of epoxy resin, 70 parts of peach gum, 25 parts of yellow clay, and 100 parts of natural latex.

[0019] The preparation method of above-mentioned handicraft is carried out according to the following steps:

[0020] (1) According to the parts by weight, take 70 parts of peach gum, heat to 80°C, add 50 parts of sepiolite powder, 25 parts of yellow clay, and stir evenly;

[0021] (2) Raise the temperature to 120°C, add 60 parts of epoxy resin, and stir evenly;

[0022] (3) The temperature is lowered to room temperature, 100 parts of natural latex is added, stirred evenly, poured into a mould, and dried naturally or dried.

Embodiment 2

[0024] A handicraft, comprising the following raw materials in parts by weight: 30 parts of pyrophyllite powder, 30 parts of acrylic resin, 50 parts of tragacanth gum, 20 parts of yellow clay, and 50 parts of polybutadiene latex.

[0025] The preparation method of above-mentioned handicraft is carried out according to the following steps:

[0026] (1) According to the parts by weight, take 50 parts of tragacanth gum, heat to 70°C, add 30 parts of pyrophyllite powder, 20 parts of yellow clay, and stir evenly;

[0027] (2) Raise the temperature to 110°C, add 30 parts of acrylic resin, and stir evenly;

[0028] (3) The temperature is lowered to room temperature, 50 parts of polybutadiene latex is added, stirred evenly, poured into a mould, and dried naturally or dried.

Embodiment 3

[0030] A handicraft, comprising the following raw materials in parts by weight: 80 parts of iron ore powder, 100 parts of styrene-butadiene-styrene block copolymer, 100 parts of gum ghatti, 30 parts of yellow clay, 200 parts of styrene-butadiene latex .

[0031] The preparation method of above-mentioned handicraft is carried out according to the following steps:

[0032] (1) According to the parts by weight, take 100 parts of gum ghatti, heat to 100°C, add 80 parts of iron ore powder, 30 parts of yellow clay, and stir evenly;

[0033] (2) Raise the temperature to 130°C, add 100 parts of styrene-butadiene-styrene block copolymer, and stir evenly;

[0034] (3) Lower the temperature to room temperature, add 200 parts of styrene-butadiene latex, stir evenly, pour it into a mold, and dry it naturally or dry it.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses artware and a preparation method thereof. The artware comprises the following raw materials in parts by weight: 30-80 parts of mineral powder, 30-100 parts of macromolecular resin, 50-100 parts of resin, 20-30 parts of yellow clay and 50-200 parts of latex. The artware prepared in the invention has the advantages of high waterproof and fireproof properties, high tensile strength and compressive strength, relatively good shaping property, rare deformation after shaping and simple preparation method and is suitable for large-scale industrial production.

Description

technical field [0001] The invention relates to the field of handicraft technology development, in particular to a handicraft and a preparation method thereof. Background technique [0002] Handicrafts are essential supplies in life. There are many kinds of modern handicrafts, including ceramic handicrafts, plastic handicrafts, vine handicrafts, metal handicrafts, etc. The preparation methods of various handicrafts are various, metal handicrafts are expensive, the preparation method is complicated, and the energy consumption of preparation is high. Manual weaving has high labor costs, plastic handicrafts produce unpleasant smells, which are not good for human health, ceramic handicrafts are difficult to prepare, and the yield is low, requiring firing and high energy consumption. [0003] Patent 201310001678.7 discloses a handicraft and its preparation method. , including the following raw materials in parts by weight: 1000 parts of resin, 2-7 parts of accelerator, and 3-10...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L7/02C08L5/00C08L63/00C08L9/10C08L33/00C08L9/08C08L53/02C08L13/02C08K3/34
CPCC08L5/00C08L7/02C08L9/08C08L9/10C08L2201/02C08L2205/03C08L63/00C08K3/34C08K3/346C08L33/00C08L53/02C08L13/02C08K3/36
Inventor 马爱忠
Owner ZHANGYE CIY DANXIA FENGYUN TOURISM & CULTURE DEV