A flame-retardant transparent plasticized PVC functional film and its preparation method

A technology of flame retardant plasticizer and PVC resin, applied in the field of PVC film and its preparation, can solve the problem of poor shielding effect, plasticized PVC functional film does not have flame retardant type, and transparent plasticized PVC functional film does not have flame retardant Type and other issues

Active Publication Date: 2019-07-02
JIANGSU MINGYANG POLYMER NEW MATERIAL
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The disadvantage of rigid transparent PVC film is poor flexibility and elasticity, which limits its use in some specific occasions
[0005] The Chinese patent with the publication number CN 103467888A and the patent name "Soft PVC functional film with solar spectrum selective transmission and its preparation method" discloses a soft transparent PVC functional film although the The inhibition rate is as high as 99.8%, and the transparent soft PVC functional film can only effectively shield the single function of ultraviolet light
The Chinese patent with the publication number CN 104693646A and the patent name "A Transparent Plasticized PVC Functional Film and Its Preparation Method" discloses a transparent plasticized PVC functional film that can effectively shield ultraviolet rays and effectively shield high-energy visible light-blue light and infrared rays. Among them, the average transmittance of 400-500nm high-energy visible light (blue light) is 24.3-76.2%, and the inhibition rate of blue light is not high; when the average transmittance of 400-500nm blue light reaches 24.3%, the average transmittance of visible light is only 35.3%. The practical application of occasions with high requirements for shielding blue light is limited. For example, in some occasions, the average transmittance of blue light is required to be below 1%.
The above two kinds of plasticized PVC functional films are not flame retardant, which further limits their application in related fields such as electronics and electrical appliances.
[0006] In summary, the transparent plasticized PVC functional films currently in use only have the functions and functions of effectively shielding ultraviolet rays and effective high-energy visible light (blue light), especially for high-energy visible light (blue light). Transparent plasticized PVC functional films are not flame retardant

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A flame-retardant transparent plasticized PVC functional film and its preparation method
  • A flame-retardant transparent plasticized PVC functional film and its preparation method
  • A flame-retardant transparent plasticized PVC functional film and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] The quality ratio of raw materials is: suspension PVC resin (S-1300) 100, polyester plasticizer 30, tris (1-chloro-2-propyl) phosphate flame retardant plasticizer 30, barium stearate 1.0, Calcium stearate 0.8, zinc stearate 0.2, benzotriazole ultraviolet light absorber UV 326 0.4, hindered amine light stabilizer C 944 0.1, ITO-g-PBA 0.5, functional yellow pigment 0.1.

[0043] Preparation:

[0044] ① Surface modification metal oxide modification: ITO is placed in toluene, ultrasonically dispersed for 20 minutes, and then transferred to a constant temperature magnetic stirring device. After stirring for 20 minutes, coupling agent KH-570 and triethylamine are added to the ITO-toluene dispersion. React at 70℃ for 4h, the whole reaction process is in dry N 2 The toluene and ITO are separated by a centrifuge, washed with alcohol for more than 3 times, dried at 80°C for 10 hours, and then ground for use. Using seed emulsion polymerization, first add a certain amount of distilled ...

Embodiment 2

[0048] The quality ratio of raw materials is: suspension PVC resin (S-1300) 100, polyester plasticizer 28, tris (1-chloro-2-propyl) phosphate flame retardant plasticizer 32, barium stearate 0.5, Calcium stearate 1.2, zinc stearate 0.3, benzotriazole ultraviolet light absorber UV 328 0.5, hindered amine light stabilizer C 944 0.5, ATO-g-PBA 0.5, functional yellow pigment 0.2

[0049] Preparation:

[0050] ①Surface modification of metal oxide modification: ATO is placed in toluene, ultrasonically dispersed for 30 minutes, and then transferred to a constant temperature magnetic stirring device. After stirring for 40 minutes, the coupling agent KH-570 and triethylamine are added to the ATO-toluene dispersion. React at 80℃ for 2h, the whole reaction process is in dry N 2 After separating toluene and ATO with a centrifuge, washing with alcohol for more than 3 times, drying at 80°C for 7 hours and then grinding for further use. Using seed emulsion polymerization, first add a certain amou...

Embodiment 3

[0054] The quality ratio of raw materials is: suspension PVC resin (S-1300) 100, polyester plasticizer 30, tris(1-chloro-2-propyl) phosphate flame retardant plasticizer 30, barium stearate 0.8, Calcium stearate 1.2, zinc stearate 0.2, benzotriazole ultraviolet light absorber UV P 0.6, hindered amine light stabilizer C 944 0.2, ITO-g-PBA 1.0, functional yellow pigment 0.3.

[0055] Preparation:

[0056] ① Surface modification metal oxide modification: ITO is placed in toluene, ultrasonically dispersed for 20 minutes and then transferred to a constant temperature magnetic stirring device. After stirring for 40 minutes, the coupling agent KH-570 and triethylamine are added to the ITO-toluene dispersion. React at 75℃ for 4h, the whole reaction process is in dry N 2 After separating toluene and inorganic non-metal compounds with a centrifuge, washing with alcohol for more than 3 times, drying at 80°C for 8 hours and then grinding for use. Using seed emulsion polymerization, first add a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
glass transition temperatureaaaaaaaaaa
glass transition temperatureaaaaaaaaaa
refractive indexaaaaaaaaaa
Login to View More

Abstract

The invention discloses an inflaming-retarding transparent plasticized PVC (Polyvinyl Chloride) functional thin film and a preparation method. The inflaming-retarding transparent plasticized PVC functional thin film has the characteristics of selectively transmitting and absorbing a solar spectrum and multiple functions of efficiently shielding ultraviolet rays, infrared rays, energetic visible light-blue light and the like. The inflaming-retarding transparent plasticized PVC functional thin film has an average shielding rate, which is up to 99 percent or above, in a 200nm to 400nm of ultraviolet waveband and an average inhibition rate, which is up to 99 percent or above, for 400nm to 500nm of the energetic visible light (blue light), and meanwhile, has a limit oxygen index which is more than 30 percent. The inflaming-retarding transparent plasticized PVC functional thin film provided by the invention is prepared from the following raw materials by mass: 100 parts of PVC resin, 60 to 70 parts of compound plasticizer, 2 parts of compound heat stabilizer, 0.1 to 1 part of compound light stabilizer, 0.1 to 0.5 part of functional pigment and 0.5 to 1 part of surface graft-modified metallic oxide.

Description

Technical field [0001] The invention relates to a PVC film and a preparation method thereof, more specifically to a flame-retardant transparent plasticized PVC functional film and a preparation method thereof. Background technique [0002] Polyvinyl chloride resin (PVC) is a typical amorphous polymer with excellent transparency and is especially suitable for making transparent films. At the same time, the structure of PVC resin only contains three atoms of carbon (C), hydrogen (H) and chlorine (Cl), and the content of chlorine atoms in the composition of PVC resin is as high as 56.8% by mass, which makes it have very good flame retardant properties. , Weather resistance and corrosion resistance, the literature reports that the limiting oxygen index (LOI) of PVC resin is more than 45%, and it is a flame-retardant polymer material in the air. The rigid transparent PVC film is made of PVC resin as the matrix material, compounded with a small amount of stabilizers, processing aids a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L27/06C08L67/02C08K13/06C08K5/521C08K5/098C08K9/08C08K3/22C08K5/3475
CPCC08J5/18C08J2327/06C08J2467/02C08K2201/014C08L27/06C08L2201/02C08L2201/10C08L2203/16C08L67/02C08K13/06C08K5/521C08K5/098C08K9/08C08K3/22C08K5/3475
Inventor 张军尹秀萍顾浦中吴淼袁益凯袁建吴俊英周贤刘云辉庄志磊徐斌浦海岗
Owner JIANGSU MINGYANG POLYMER NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com