Nano diamond alkene containing novel aqueous varnish and preparation method thereof

A nanodiamondene and water-based technology, applied in the direction of coating, etc., can solve the problems of weather resistance, scratch resistance, poor image quality, poor aging resistance, poor dispersion uniformity of powder wall paint, and environmental pollution, and achieve UV resistance Strong ability, improved scratch resistance, and low VOC content

Inactive Publication Date: 2017-05-10
HENAN YUXING MICRON DIAMOND CO LTD
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, water-based varnishes mainly include solvent-based, water-soluble and powder-based. Although solvent-based varnishes are better in use, they contain a large amount of VOC (volatile organic compounds) and pollute the environment; powder-based wall paints have poor dispersion uniformity and are rarely used. ; Water-soluble varnish has good environmental protection performance, so it is loved by consumers
However, the existing water-based varnishes are poor in weather resistance, scratch resistance, distinctness of image, and aging resistance, and further improvement is needed

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Nano diamond alkene containing novel aqueous varnish and preparation method thereof
  • Nano diamond alkene containing novel aqueous varnish and preparation method thereof
  • Nano diamond alkene containing novel aqueous varnish and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] A novel water-based varnish containing nanodiamondene and a preparation method thereof, which are made of the following parts by weight:

[0036] The first component: 50 parts of hydroxy acrylate emulsion, 3.99 parts of nanodiamondene, 15 parts of deionized water, 0.6 parts of dispersant, 0.1 part of anti-settling agent, 0.01 part of defoaming agent, 0.2 part of leveling agent, film forming aid 4 parts of agent, 2 parts of thickener, 0.1 part of PH regulator;

[0037] The second component: 21 parts of curing agent, 3 parts of co-solvent;

[0038] The above-mentioned nanodiamondene is prepared by the following steps:

[0039] a. Ultrasonic alkaline cleaning: Put the nanodiamondene in the raw material into an ultrasonic cleaning machine equipped with lye, the ultrasonic frequency is 30KHz, the lye concentration is 8% NaOH solution, the lye temperature is controlled at 50 ℃, and the rotation is stirred , The stirring speed is 25rpm, and the cleaning is 25min;

[0040] b. Ultrasoni...

Embodiment 2

[0049] A novel water-based varnish containing nanodiamondene and a preparation method thereof, which are made of the following parts by weight:

[0050] The first component: 60 parts of hydroxy acrylate emulsion, 7 parts of nanodiamondene, 10 parts of deionized water, 0.39 parts of dispersant, 0.01 part of anti-settling agent, 0.1 part of defoaming agent, 1 part of leveling agent, film forming aid 3 parts of agent, 1.2 parts of thickener, 0.3 parts of PH regulator;

[0051] The second component curing agent: 15 parts, 2 parts co-solvent;

[0052] The above-mentioned nanodiamondene is prepared by the following steps:

[0053] a. Ultrasonic alkaline cleaning: Put the nanodiamondene in the raw material into an ultrasonic cleaning machine equipped with lye, the ultrasonic frequency is 30KHz, the lye concentration is 10% NaOH solution, the lye temperature is controlled at 55℃, and the rotating stirring , The stirring speed is 27rpm, and the cleaning is 27min;

[0054] b. Ultrasonic water w...

Embodiment 3

[0063] A novel water-based varnish containing nanodiamondene and a preparation method thereof, which are made of the following parts by weight:

[0064] The first component: 65.4 parts of hydroxy acrylate emulsion, 0.5 part of nanodiamondene, 5 parts of deionized water, 0.1 part of dispersant, 0.05 part of anti-settling agent, 0.05 part of defoaming agent, 0.4 part of leveling agent, film forming aid 2 parts, thickening agent 0.3, pH regulator 0.2;

[0065] The second component: 25 parts of curing agent, 1 part of co-solvent;

[0066] The above-mentioned nanodiamondene is prepared by the following steps:

[0067] a. Ultrasonic alkaline cleaning: Put the nanodiamondene in the raw material into an ultrasonic cleaning machine equipped with lye, the ultrasonic frequency is 30KHz, the lye concentration is 11% NaOH solution, the lye temperature is controlled at 57 ℃, and the rotating stirring , Stirring speed is 28rpm, cleaning 29min;

[0068] b. Ultrasonic water washing: Put the alkali-was...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the field of water varnish, and in particular relates to nano diamond alkene containing novel aqueous varnish and a preparation method thereof. The nano diamond alkene containing novel aqueous varnish is prepared from the following raw materials in parts by weight: a first component, including 50-70 parts of a hydroxied acrylate emulsion, 0.5-7 parts of nano diamond alkene, 5-15 parts of deionized water, 0.1-0.6 part of a dispersing agent, 0.01-0.1 part of an anti-settling agent, 0.01-0.1 part of a defoaming agent, 0.2-1 part of a leveling agent, 2-4 parts of a coalescing agent, 0.3-2 parts of a thickening agent and 0.1-0.3 part of a pH adjusting agent; a second component, 15-25 parts of a curing agent and 1-3 parts of a cosolvent. The nano diamond alkene containing novel aqueous varnish is capable of solving the problems that conventional water vanish is relatively poor in weather resistance, scratch resistance, distinctness of image, and the like, is greatly excellent in glossiness, hardness, impact resistance, flexibility and weather resistance when being compared with those of conventional vanish, and is relatively good in environmental friendliness.

Description

Technical field [0001] The invention belongs to the field of water-based varnish manufacturing, and specifically relates to a novel water-based varnish containing nanodiamondene and a preparation method thereof. Background technique [0002] With the rapid development of industry, people’s requirements for material quality continue to increase. As the outermost layer of coatings for automobiles and furniture, varnishes play a vital role in the beauty and service life of objects. Water-based varnishes are a A kind of paint that does not contain coloring substances. The traditional water-based varnish is a paint made of resin as the main film-forming substance and solvent, which can keep the original texture of the article and form a smooth film after drying. At present, water-based varnishes are mainly solvent-based, water-soluble and powder-based. Although solvent-based varnishes have good results, they contain a large amount of VOC (volatile organic compounds) and pollute the en...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D133/14C09D7/12
CPCC09D133/14C08K2201/014C08L2205/035C09D7/61C09D7/63C08L83/12C08L75/04C08L101/00C08K13/02C08K3/04C08K5/101C08K5/06
Inventor 张洪涛尹维召杨晋中武艳强李盟
Owner HENAN YUXING MICRON DIAMOND CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com