Economical H2S corrosion-resistant normalized pipeline steel and production method

An economical, pipeline steel technology, applied in economical H2S corrosion-resistant normalized pipeline steel and production fields, can solve the problems of insufficient economy, lack of economical features, lack of corrosion resistance, etc., to avoid excessive grain size growing effect

Active Publication Date: 2017-05-24
武汉钢铁有限公司
View PDF14 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] After searching, before the present invention, the Chinese patent application numbers are CN201010235925.6, CN201510297590.3, CN20160419909.X, CN2012101168133.0, CN201410233997.5 documents, the involved normalizing pipeline steel chemical composition is low C Or the composition system of medium C + medium Mn, and adding an appropriate amount of precious alloys such as Cr and Ni at the same time, is not economical and does not have corrosion resistance
[0006] Chinese patent application numbers are CN201210271608.9, CN201610025494.8, CN201310146465.3, CN201010130911.8, CN201410130811.3 documents, the involved normalizing pipeline steel adopts the composition system of Cu+Cr+Mo+Ni or high Cr, not economical

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Economical H2S corrosion-resistant normalized pipeline steel and production method
  • Economical H2S corrosion-resistant normalized pipeline steel and production method
  • Economical H2S corrosion-resistant normalized pipeline steel and production method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0033] The present invention is described in detail below:

[0034] Table 1 is the chemical composition list of each embodiment of the present invention and comparative example;

[0035] Table 2 is the main process parameter list of each embodiment of the present invention and comparative example;

[0036] Table 3 is each embodiment of the present invention and comparative example mechanical property and resistance to H 2 S corrosion performance list;

[0037] Table 4 is a comparison list of important alloy costs between the embodiment of the present invention and the similar patent embodiment.

[0038] Each embodiment of the present invention all produces according to the following steps:

[0039] 1) Heating the slab after continuous casting, and controlling the heating temperature at 1100~1150°C;

[0040] 2) Carry out rough rolling, and control the end temperature of rough rolling to 1030~1080°C;

[0041]3) Carry out finish rolling, and control its starting rolling temp...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses economical H2S corrosion-resistant normalized pipeline steel. The economical H2S corrosion-resistant normalized pipeline steel comprises the following chemical components in percentage by weight (wt%): 0.04-0.07% of C, 0.10-0.20% of Si, 0.7-0.9% of Mn, P not more than 0.01%, S not more than 0.002%, 0.06-0.12% of Nb, 0.04-0.07% of V, B not more than 0.0005, and RE not more than 0.0005. A production method comprises the production steps of casting blank heating, rough rolling, finish rolling, cooling, coiling and normalization. Besides of guaranteeing use mechanical performance and excellent weldability, the hydrogen sulfide corrosion resistance is excellent; cracks are not observed under the condition of the loading load being 0.80*actual yield strength load; the alloy cost is simple; and the cost can be reduced by 20% or above.

Description

technical field [0001] The invention relates to a pipeline steel and a production method, in particular to a H-resistant 2 A normalized pipeline steel with excellent corrosion performance and a production method thereof. Background technique [0002] Oil and natural gas are important energy sources for the development of the national economy, and their proportions in energy consumption are increasing day by day. At present, pipeline transportation is still the most economical, safe and efficient long-distance transportation method for oil and natural gas. However, with the depletion of easy-to-exploit oil and natural gas resources, H 2 The development of natural gas with high S content is increasing. [0003] h 2 S is one of the most corrosive and harmful media in oil and gas. When pipeline steel is exposed to moisture containing H 2 When in the conveying medium of S, the material is very prone to H 2 S acid corrosion, causing sudden failure of the delivery pipeline, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C38/04C22C38/02C22C38/12C21D8/02
CPCC21D8/0226C21D8/0263C22C38/02C22C38/04C22C38/12
Inventor 崔雷徐进桥李利巍邹航徐锋孔君华郎丰军王俊霖毛传军张扬
Owner 武汉钢铁有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products