A kind of biofuel resistant rubber seal material and preparation method thereof

A rubber seal, bio-resistant technology, applied in the rubber field, can solve the problems of non-renewable fuel oil, long oil regeneration time, etc., and achieve the effects of resistance to swelling corrosion, good mechanical properties, bio-fuel resistance, and prevention of extraction corrosion

Active Publication Date: 2019-06-21
ANHUI ZHONGDING SEALING PARTS
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the regeneration time of petroleum is too long, and it takes tens of thousands of years to complete, so the fuel synthesized from petroleum is basically a non-renewable fuel.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of biofuel resistant rubber seal material and preparation method thereof
  • A kind of biofuel resistant rubber seal material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A bio-fuel-resistant rubber seal material, its raw materials include by weight: 100 parts of a mixture of nitrile rubber and polyvinyl chloride, 60 parts of quick extruded carbon black, 5.5 parts of zinc oxide by indirect method, 1.5 parts of stearic acid, 2 parts of 2,2,4-trimethyl-1,2-dihydroquinoline polymer, 2 parts of 4,4'-bis(α,α-dimethylbenzyl)diphenylamine, polyester plasticizer 7 parts, 5.5 parts of calcium hydroxide, 4 parts of ultra-high molecular weight polyethylene, 2 parts of paraffin, 1.5 parts of sulfur, 1 part of accelerator TMTD, and 2 parts of accelerator CBS.

[0021] The preparation method of the above-mentioned bio-fuel-resistant rubber seal material includes the following steps: taking the above-mentioned raw materials and mixing them, banburying to obtain synthetic rubber; taking the synthetic rubber, performing kneading and molding, then adding it into a mold, and vulcanizing to obtain bio-fuel-resistant rubber seals Material.

Embodiment 2

[0023] A kind of bio-fuel-resistant rubber seal material, its raw material comprises by weight: 100 parts of the mixture of nitrile rubber and polyvinyl chloride, 50 parts of quick extruded carbon black, 3 parts of indirect method zinc oxide, 1 part of stearic acid, 1 part of 2,2,4-trimethyl-1,2-dihydroquinoline polymer, 1 part of 4,4'-bis(α,α-dimethylbenzyl)diphenylamine, polyester plasticizer 10 parts, 3 parts of calcium hydroxide, 3 parts of 300 mesh ultra-high molecular weight polyethylene, 1 part of paraffin, 1 part of sulfur, 1.5 parts of accelerator TMTD, and 1 part of accelerator CBS;

[0024] Wherein, in the mixture of nitrile rubber and polyvinyl chloride, the content of polyvinyl chloride is 25wt%, and the content of acrylonitrile in nitrile rubber is 50wt%;

[0025] The molecular weight of ultra-high molecular weight polyethylene is 2 million.

[0026] The preparation method of the above-mentioned bio-fuel-resistant rubber seal material includes the following step...

Embodiment 3

[0028] A bio-fuel-resistant rubber seal material, its raw materials include by weight: 100 parts of a mixture of nitrile rubber and polyvinyl chloride, 60 parts of quick extruded carbon black, 5 parts of zinc oxide by indirect method, 1.5 parts of stearic acid, 2 parts of 2,2,4-trimethyl-1,2-dihydroquinoline polymer, 2 parts of 4,4'-bis(α,α-dimethylbenzyl)diphenylamine, polyester plasticizer 8 parts, 5 parts of calcium hydroxide, 4 parts of 600 mesh ultra-high molecular weight polyethylene, 2 parts of paraffin, 1.5 parts of sulfur, 1 part of accelerator TMTD, and 2 parts of accelerator CBS;

[0029] Wherein, in the mixture of nitrile rubber and polyvinyl chloride, the content of polyvinyl chloride is 30wt%, and the content of acrylonitrile in nitrile rubber is 45wt%;

[0030] The molecular weight of ultra-high molecular weight polyethylene is 3 million.

[0031]The preparation method of the above-mentioned bio-fuel-resistant rubber seal material includes the following steps: ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
hardnessaaaaaaaaaa
strengthaaaaaaaaaa
hardnessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a biological fuel oil-resistant rubber sealing element material, which is prepared from the following raw materials in parts by weight: 100 parts of a mixture of nitrile rubber and polyvinyl chloride, 50-70 parts of fast extruded carbon black, 3-8 parts of an indirect zinc oxide, 1-2 parts of stearic acid, 1-3 parts of 2,2,4-trimethyl-1,2-dihydroquinoline polymer, 1-3 parts of 4,4-bis(a,a-dimethyl benzyl)-diphenylamine, 5-10 parts of a polyester plasticizer, 3-8 parts of calcium hydroxide, 3-5 parts of ultra high molecular weight polyethylene, 1-3 parts of paraffin, 1-2 parts of sulphur, 0.5-1.5 parts of an accelerant TMTD and 1-3 parts of an accelerant CBS. The invention further discloses a preparation method of the biological fuel oil-resistant rubber sealing element material. The biological fuel oil-resistant rubber sealing element material is capable of effectively resisting expanding corrosion of biological fuel oil and preventing extracting corrosion of biological fuel oil, and has good biological fuel oil resistance.

Description

technical field [0001] The invention relates to the technical field of rubber, in particular to a biofuel-resistant rubber seal material and a preparation method thereof. Background technique [0002] Our current vehicle fuels are mainly gasoline and diesel, which are synthesized from petrochemicals. However, the regeneration time of petroleum is too long, and it takes tens of thousands of years to complete, so the fuel synthesized from petroleum is basically non-renewable fuel. At the same time, biofuel is a kind of energy produced based on vegetable oil. It is a renewable fuel. Biofuel is not limited by oil reserves. After the efforts of agriculture and biologists, its consumption will not be exhausted. At the same time, bio-fuel has no harmful elements such as sulfur and benzene in petroleum, and has less pollution to the atmosphere after combustion, so it is also called clean fuel. [0003] Biofuels are now partially replacing traditional gasoline and diesel. However,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L9/02C08L27/06C08L23/06C08L67/00C08K13/02C08K5/09C08K3/06C08K3/04C08K3/22C08K5/3437C08K5/18B29C35/02
CPCB29C35/02C08L9/02C08L2201/08C08L2205/035C08L2207/068C08L27/06C08L23/06C08L67/00C08K13/02C08K2003/2296C08K5/09C08K3/06C08K3/04C08K2003/2206C08K5/3437C08K5/18
Inventor 夏迎松李彬毛学斌方炳虎章维国
Owner ANHUI ZHONGDING SEALING PARTS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap