A smelting method, ultra-low carbon steel technology, applied in the manufacture of converters, etc., can solve the problems of reduced smelting efficiency, high energy consumption, and large consumption

Active Publication Date: 2017-07-07
PANGANG GRP XICHANG STEEL & VANADIUM CO LTD
View PDF6 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

During the smelting process of this kind of process, the temperature loss when the converter is released is relatively large, and a large amount of electric energy is required to raise the temperature of the molten steel to the processing requirements of the RH vacuum treatment furnace again, which not only consumes high energy, but also increases the smelting time. Reduce smelting efficiency

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0014] The core of the present invention is to provide a method for smelting ultra-low carbon steel, so as to effectively reduce energy consumption during smelting of ultra-low carbon steel, reduce smelting time, and improve smelting efficiency.

[0015] The technical solutions in the embodiments of the present invention will be clearly and completely described below. Obviously, the described embodiments are only some of the embodiments of the present invention, but not all of them. Based on the embodiments of the present invention, all other embodiments obtained by persons of ordinary skill in the art without making creative efforts belong to the protection scope of the present invention.

[0016] The smelting method of ultra-low carbon steel disclosed in the present invention, the basic process route is: iron desulfurization pretreatment-converter blowing-RH vacuum treatment-continuous casting, compared with the prior art, the improvement point is that the heating process is ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a method for smelting ultra-low carbon steel. The method comprises a desulfurization procedure, a converter blowing procedure, an RH vacuum treatment procedure and a continuous casting procedure. After converter blowing, the temperature of tapping is 1680 DEG C-1700 DEG C, then ferroaluminum is added into liquid steel so that the liquid steel is subjected to preliminary deoxygenation; then the temperature is measured, oxygen activity is determined, and the liquid steel is fed with an aluminium wire according to a determined oxygen activity result, so that the oxygen activity is fine-tuned, and it is ensured that the oxygen activity is at 550 ppm-650 ppm; and the liquid steel meeting conditions enters the RH vacuum treatment procedure directly. A high target temperature of the converter tapping, with the partial ferroaluminum deoxygenation conducted after the converter tapping, enables the liquid steel to be kept at a high temperature level, and the temperature level meets the requirement for the temperature when the liquid steel enters the RH vacuum treatment procedure, so that an existing electric heating procedure is omitted; and the liquid steel can enter the RH vacuum treatment procedure directly, so that energy consumption in the steel making process is reduced greatly, and steel making efficiency is enhanced effectively after the heating procedure is omitted.

Description

technical field [0001] The invention relates to the technical field of steelmaking, and more specifically, relates to a method for smelting ultra-low carbon steel. Background technique [0002] Ultra-low carbon steel refers to steel with a carbon content below 0.01%. At present, the process of desulfurization-converter blowing-LF treatment-RH vacuum treatment-CC (continuous casting) is generally used to smelt ultra-low carbon steel. [0003] At present, in this process, the temperature of the molten steel after converter blowing is relatively low. Before entering the RH vacuum treatment furnace, it needs to be heated by electric heating in the ladle furnace, and then sent to the RH vacuum treatment furnace for decarburization. Deoxidation alloying. During the smelting process of this kind of process, the temperature loss when the converter is released is relatively large, and a large amount of electric energy is required to raise the temperature of the molten steel to the p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C21C7/06C21C7/10C21C5/28C21C7/064C21C1/02
CPCC21C1/025C21C5/28C21C7/0006C21C7/06C21C7/0645C21C7/10
Inventor 郭振宇
Owner PANGANG GRP XICHANG STEEL & VANADIUM CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap