A high-gloss and wear-resistant screen printing process for glass products

A technology for glass products and screen printing, applied in printing, printing devices, inks, etc., can solve the problems of unsatisfactory brightness and wear resistance of polyacrylate films, improve brightness and wear resistance, and improve wear resistance. Grinding performance, brightness improvement effect

Active Publication Date: 2019-01-18
YIWU HUAHONG CULTURE CREATIVE CO LTD
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Aiming at the problem that the brightness and wear resistance of the current polyacrylate film are not ideal enough, the invention provides a high-gloss wear-resistant screen printing process for glass products

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A high-gloss and wear-resistant screen printing process for glass products
  • A high-gloss and wear-resistant screen printing process for glass products
  • A high-gloss and wear-resistant screen printing process for glass products

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] This embodiment is a high-gloss wear-resistant screen printing process for glass products, including glass cleaning and drying, screen plate production, high-gloss wear-resistant ink preparation, printing and curing, and post-processing. The specific operations are as follows:

[0033] 1) Glass cleaning and drying: use industrial cleaning agent solution (commercially available, 5wt%) to 1m 2 The glass products to be printed are cleaned, and then the cleaned glass products to be printed are dried at 80°C for use;

[0034] 2) Screen plate production: select 60-mesh nylon screen to tighten on the screen frame, the thickness of the screen is 70 μm; attach the photosensitive film to the screen, the thickness of the photosensitive film is 25 μm, and use the method of exposure and development to transfer the image and text Put it into the photosensitive film, rinse and develop, dry, and apply glue to get the screen plate, which is ready for use;

[0035] 3) Preparation of com...

Embodiment 2

[0042] This embodiment is a high-gloss wear-resistant screen printing process for glass products, including glass cleaning and drying, screen plate production, high-gloss wear-resistant ink preparation, printing and curing, and post-processing. The specific operations are as follows:

[0043] 1) Glass cleaning and drying: use industrial cleaning agent solution (commercially available, 5wt%) to 1m 2 The glass products to be printed are cleaned, and then the cleaned glass products to be printed are dried at 80°C for use;

[0044] 2) Screen plate production: select 100-mesh nylon screen to tighten on the screen frame, the thickness of the screen is 80 μm; attach the photosensitive film to the screen, the thickness of the photosensitive film is 45 μm, and use the method of exposure and development to transfer the image and text Put it into the photosensitive film, rinse and develop, dry, and apply glue to get the screen plate, which is ready for use;

[0045] 3) Preparation of co...

Embodiment 3

[0051] This embodiment is a high-gloss wear-resistant screen printing process for glass products, including glass cleaning and drying, screen plate production, high-gloss wear-resistant ink preparation, printing and curing, and post-processing. The specific operations are as follows:

[0052] 1) Glass cleaning and drying: use industrial cleaning agent solution (commercially available, 5wt%) to 1m 2 The glass products to be printed are cleaned, and then the cleaned glass products to be printed are dried at 80°C for use;

[0053] 2) Screen plate production: Select 80-mesh nylon screen to tighten on the screen frame, the thickness of the screen is 75 μm; attach the photosensitive film to the screen, the thickness of the photosensitive film is 30 μm, and use the method of exposure and development to transfer the image and text Put it into the photosensitive film, rinse and develop, dry, and apply glue to get the screen plate, which is ready for use;

[0054] 3) Preparation of com...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a glasswork high-bright wear-resistant screen printing technology which comprises the following steps: 1) glass cleaning and drying are carried out; 2) a screen printing plate is manufactured; 3) high-bright wear-resistant printing ink is blended; 4) printing and solidification are carried out; and 5) post treatment is carried out. By adding nano silver nitrate powder, aminopropyl triethyl silicane, and polycarbonate diol or polycarbonate to polyacrylate printing ink, the radiance, the toughness and the wear-proof property of a polyacrylate film are improved. In addition, glasswork after the printing is completed is put in an environment at 60-80 DEG C, is subjected to heat preservation for 10-30min, and then is subjected to natural cooling, the polyacrylate film having higher crystallinity can be obtained, positive effects are exerted in improving the radiance and the wear-proof property of the polyacrylate film.

Description

technical field [0001] The invention belongs to the technical field of screen printing, and in particular relates to a high-gloss wear-resistant screen printing process for glass products. Background technique [0002] Glass screen printing refers to the screen printing method used for glass plates or glass containers as the main product. The use of glass has a long history in our country, even in today's modernization, glass still plays an important role in our life. The screen printing process can endow the glass with a beautiful appearance pattern, which greatly meets people's life and aesthetic needs. [0003] The polyacrylate ink developed in the 1960s has been valued in the screen printing process because of its clear and light color, water resistance, corrosion resistance, good discoloration resistance, easy performance adjustment, convenient use, and abundant raw materials. . The disadvantage of polyacrylate ink is that the brightness of the formed polyacrylate fi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More