Mixed mortar for stone-like coating and preparation method thereof

A technology of mixing mortar and real stone paint, applied in the field of real stone paint, to achieve the effect of improving the color effect, avoiding long-term drop, and improving the use effect

Inactive Publication Date: 2017-08-08
XIAOGAN CHUANGKE ELECTRONICS TECH
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But often in use, the color difference and sensory fidelity of real stone paint are what we need to improve and pursue. Improving the color and sensory degree of real stone paint is a problem we need to face

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A kind of mixed mortar for real stone paint, its raw materials are as follows by weight: 800 parts of colored stone sand, 960 parts of river sand, 20 parts of silica fume, 10 parts of preservative, 4 parts of thickener, 80 parts of pure acrylic acid, 20 parts of gypsum part, 250 parts of water.

[0022] The colored stone sand is obtained through high-temperature sintering, and the high-temperature sintering temperature is 1200°C. The river sand is made by mixing coarse river sand and fine river sand according to the weight component ratio of 2:1, the mesh number of the coarse river sand is 50 mesh, and the mesh number of the fine river sand is 30 mesh. The silica fume is 3000 mesh micro silica fume. The thickener is obtained from carboxymethyl cellulose and hydroxyethyl cellulose in a ratio of 3:1 by weight. The preservative is sodium benzoate. The mesh number of the colored stone sand is 60 mesh.

[0023] The present invention also provides a method for preparing a...

Embodiment 2

[0030] A kind of mixed mortar for real stone paint, its raw materials are as follows by weight: 1000 parts of colored stone sand, 1200 parts of river sand, 25 parts of silica fume, 15 parts of preservative, 5 parts of thickener, 90 parts of pure propanolactic acid, 25 parts of gypsum part, 300 parts of water.

[0031] The colored stone sand is obtained through high-temperature sintering, and the high-temperature sintering temperature is 1250°C. The river sand is made by mixing coarse river sand and fine river sand according to the weight component ratio of 2:1, the mesh number of the coarse river sand is 60 mesh, and the mesh number of the fine river sand is 40 mesh. The silica fume is 3000 mesh micro silica fume. The thickener is obtained from carboxymethyl cellulose and hydroxyethyl cellulose in a ratio of 3:1 by weight. The preservative is sodium benzoate. The mesh number of the colored stone sand is 70 mesh.

[0032] The present invention also provides a method for pre...

Embodiment 3

[0039] A kind of mixed mortar for real stone paint, its raw materials are as follows by weight: 1200 parts of colored stone sand, 1450 parts of river sand, 30 parts of silica fume, 20 parts of preservative, 6 parts of thickener, 100 parts of pure propanolactic acid, 30 parts of gypsum part, 350 parts of water.

[0040] The colored stone sand is obtained through high-temperature sintering, and the high-temperature sintering temperature is 1300°C. The river sand is prepared by mixing coarse river sand and fine river sand according to the weight component ratio of 2:1, the mesh number of the coarse river sand is 70 mesh, and the mesh number of the fine river sand is 50 mesh. The silica fume is 3000 mesh micro silica fume. The thickener is obtained from carboxymethyl cellulose and hydroxyethyl cellulose in a ratio of 3:1 by weight. The preservative is sodium benzoate. The mesh number of the colored stone sand is 80 mesh.

[0041] The present invention also provides a method fo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses mixed mortar for a stone-like coating. The mixed mortar is prepared from the following raw materials in parts by weight: 800 to 1,200 parts of colored stone sand, 960 to 1,450 parts of river sand, 20 to 30 parts of silicon ash, 10 to 20 parts of preservative, 4 to 6 parts of thickening agent, 80 to 100 parts of pure acrylic emulsion, 20 to 30 parts of gypsum and 250 to 350 parts of water. By adopting the mixed mortar, the colored stone sand and the river sand are mixed, so that the stone-like coating can achieve higher color fidelity; by adopting the colored stone sand, the color effect can be improved greatly, and meanwhile the situation of fading after a long time can be avoided; meanwhile, the perception fidelity of the stone-like coating can be improved greatly by the river sand; meanwhile, the river sand is prepared from coarse river sand and fine river sand, so that the stone-like coating has greater concave-convex sense, and the using effect of the stone-like coating is improved greatly.

Description

technical field [0001] The invention relates to the technical field of genuine stone paint, in particular to a mixed mortar for real stone paint and a preparation method thereof. Background technique [0002] Real stone paint is a kind of paint with a decorative effect similar to marble and granite. It is mainly made of natural stone powder of various colors, and it is applied to the imitation stone effect of building exterior walls, so it is also called liquid stone. The buildings decorated with real stone paint have natural and real natural color, which gives people elegant, harmonious and solemn aesthetic feeling. It is suitable for indoor and outdoor decoration of all kinds of buildings. Especially when it is decorated on curved buildings, it is vivid and lifelike, and has an effect of returning to nature. Real stone paint has fire protection, waterproof, acid and alkali resistance, and pollution resistance. Non-toxic, tasteless, strong adhesion, never fade and other ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B26/06
CPCC04B26/06C04B2111/00482
Inventor 张国保
Owner XIAOGAN CHUANGKE ELECTRONICS TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap