Precision casting method for metal objects

A technology of precision casting and utensils, applied in casting molding equipment, metal processing equipment, casting molds, etc., can solve problems such as insufficient density and hardness, trachoma, and inability to obtain high fineness

Inactive Publication Date: 2017-08-11
五星机械(镇江)有限公司
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Because of its very high ornamental value, copper crafts have been widely loved by people since ancient times, and the craftsmanship of copper crafts has also continued from ancient times to the present. Although the development of existing technologies, the craftsmanship of copper crafts has gradually improved. Improvement, the techniques used in different copper crafts are also varied. However, with the improvement of people's living standards, people's requirements for the exquisiteness and delicacy of copper crafts are also getting higher and higher. The existing copper crafts The art production process needs to be further improved. However, due to the defects in the specific process (such as baking and pouring) steps in the existing copper art production process, on the one hand, there will be cracks and blisters. On the other hand, the density and hardness are not enough, and it is easy to deform. On the other hand, the requirements of high fineness and fineness cannot be obtained.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0017] The investment casting method for metal utensils of the present invention will be further described in detail below in conjunction with specific embodiments.

[0018] The precision casting method of the metal utensil of the present invention comprises the following steps:

[0019] A. Model making

[0020] Use beeswax to make a casting model, and then spread mud on the outside of the model to make an outer mold. After the outer mold is made, it is divided into several pieces to remove the outer mold from the model. After the clay core is finally heated and baked, the wax film is completely melted and lost, so that the outer mold and the clay core are fitted together to form a cavity;

[0021] B. Preheating

[0022] Put the outer mold and the clay core together and heat it with a warm fire at 80-90°C, heat it for 1-2 hours and then cool it slowly for 30 minutes, then put it into the kiln and heat it at a high temperature of 300-400°C;

[0023] C. Pouring

[0024] Afte...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a precision casting method for metal objects. The method includes the following steps that A, model making is performed, beewax is used for making a casting model, and an outline and a clay core are combined in a sleeving mode to form a cavity; B, preheating is conducted, the outline and the clay core are combined in the sleeving mode to be heated with small fire at first, slow cooling is performed, and then the outline and the clay core are put into a furnace kiln to be heated at a high temperature; C, pouring is carried out, molten copper is poured into a pouring gate, and after the molten copper is solidified and cooled, the outline and the core can be removed to take out a copper billet casting; D, a copper billet is polished; and F, decorating and surface coloring are carried out, the polished product is decorated, surface coloring is conducted after the product is decorated, and accordingly a finished product can be obtained. By the adoption of the method, rupture and sand holes cannot happen to the casting formed through the outline and the clay core easily, molten copper mobility can be improved by preheating the outline and the clay core, and therefore the molten copper injected into the cavity can be evenly filled, and the density and hardness of the finished product are improved; and in addition, through the reasonable technology, manufactured copper ware is fine and smooth in surface, delicate in modeling, dainty and exquisite and good in ornamental value.

Description

technical field [0001] The invention relates to a manufacturing method of copper handicrafts, in particular to a precision casting method of metal utensils. Background technique [0002] Because of its very high ornamental value, copper crafts have been widely loved by people since ancient times, and the craftsmanship of copper crafts has also continued from ancient times to the present. Although the development of existing technologies, the craftsmanship of copper crafts has gradually improved. Improvement, the techniques used in different copper crafts are also varied. However, with the improvement of people's living standards, people's requirements for the exquisiteness and delicacy of copper crafts are also getting higher and higher. The existing copper crafts The art production process needs to be further improved. However, due to the defects in the specific process (such as baking and pouring) steps in the existing copper art production process, on the one hand, there ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B22C9/04B22C9/12
CPCB22C9/04B22C9/12
Inventor 赵平王自东
Owner 五星机械(镇江)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products