Method for producing ultra-white polyvinyl chloride resin after suspension polymerization of vinyl chloride

A polyvinyl chloride resin, suspension polymerization technology, applied in the field of ultra-white polyvinyl chloride resin after vinyl chloride suspension polymerization, to achieve good fluidity, reduce processing costs, and eliminate the effect of resin yellowing

Active Publication Date: 2019-06-18
TANGSHAN SANYOU CHLOR ALKALI
View PDF2 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, there is no method of whitening through the principle of blue light-yellow light complementary optics after polyvinyl chloride is polymerized.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] A method for producing ultra-white polyvinyl chloride resin after suspension polymerization of vinyl chloride. According to the mass ratio, 15 parts of absolute ethanol, 2 parts of liquid carbolic acid, 4 parts of "acid blue 90" and 400 parts of water are used to prepare whitening aids ; In the range of 0-80°C, according to the volume ratio, dilute the whitening aids for dispersion, add each part of the whitening aids to 200 times the volume of deionized water, stir at a speed of 20-80r / min for 1 minute, and In the slurry of SG3 resin exiting the kettle, use 1.6L dilution aid / m 3 slurry, add dilution aid to the stripped slurry and stir evenly. After centrifugation at a speed of 1500-2000r / min and drying at 60°C for 10-15 minutes, the initial whiteness of the product was sampled and tested to be 93.2%, and the aging whiteness of the product tested according to the national standard GB5761 was 88.4%. The initial whiteness of the same batch of samples without post-treatme...

Embodiment 2

[0017] A method for producing ultra-white polyvinyl chloride resin after suspension polymerization of vinyl chloride. According to the mass ratio, 15 parts of absolute ethanol, 2 parts of liquid carbolic acid, 5 parts of "acid blue 74" and 500 parts of water are used to prepare whitening aids , dilute 200 times with deionized water to prepare dilution aid.

[0018] In the SG5 type resin slurry, dilute the auxiliary agent by 2L / m 3 slurry, add dilution aid to the stripped slurry and stir evenly. After centrifugation at a speed of 2000r / min and drying at 60°C for 15 minutes, the initial whiteness of the product was sampled and tested to be 94.2%, and the aging whiteness of the product tested according to the national standard GB5761 was 88.3%. The initial whiteness of the same batch of samples without post-treatment of whitening additives is 92.5%, and the aging whiteness of GB5761 is 86.5%.

Embodiment 3

[0020] A method for producing ultra-white polyvinyl chloride resin after suspension polymerization of vinyl chloride, comprising 15 parts of absolute ethanol, 2 parts of liquid carbolic acid, 6 parts of "acid blue 5", and 600 parts of water to configure whitening aids according to the mass ratio, Prepare dilution aid by diluting 200 times with deionized water.

[0021] In the SG8 type resin slurry, dilute the auxiliary agent at 2.4L / m 3 slurry, add dilution aid to the stripped slurry and stir evenly. After centrifugation and drying, the initial whiteness of the product is 93.8% according to the sampling test, and the aging whiteness of the product is 88.3% according to the national standard GB5761. The initial whiteness of the same batch of samples without post-treatment of whitening additives is 92.2%, and the aging whiteness of GB5761 is 86.7%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
whitenessaaaaaaaaaa
whitenessaaaaaaaaaa
whitenessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a production method of ultra-white polyvinyl chloride paste resin, in particular to a method for producing ultra-white polyvinyl chloride resin after suspension polymerization of vinyl chloride. Proceed as follows: 12 to 18 parts of ethanol, 1 to 3 parts of liquid carbolic acid, 4 to 8 parts of blue pigments, and 400 to 600 parts of deionized water are used to prepare whitening aids according to the mass ratio; The auxiliary agent is dispersed and diluted with deionized water, then added to the polyvinyl chloride slurry, stirred evenly, centrifuged, and dried to obtain a high whiteness polyvinyl chloride resin product. Compared with the existing technology, it has the following advantages: good whitening effect: 2), high whitening efficiency: because the whitening agent is a water-soluble high-dispersion solution, the blue pigment molecules are adsorbed by the folds of the resin particles, and in blue light- The phenomenon of yellowing of the resin is eliminated under the complementary effect of yellow light. Since the pigment molecules are fully dispersed in the slurry, the coloring efficiency is greatly improved; and the downstream processing cost of the later resin is reduced.

Description

technical field [0001] The invention relates to a production method of ultra-white polyvinyl chloride paste resin, in particular to a method for producing ultra-white polyvinyl chloride resin after suspension polymerization of vinyl chloride. Background technique [0002] Domestically produced general-purpose suspension-process polyvinyl chloride resin is widely used in building materials, industrial products, daily necessities, floor tiles, artificial leather, profiles, pipes, packaging, and so on. In most application fields, white polyvinyl chloride plastic products have higher requirements on the whiteness of the resin. For colored plastic products, the whiteness of the resin also affects the coloring performance in the later stage. Therefore, the polyvinyl chloride industry as a whole has higher requirements on the whiteness of the resin. [0003] At present, polyvinyl chloride production enterprises usually use steam stripping to reduce the residual vinyl chloride mon...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08J3/20C08L27/06
CPCC08J3/2056C08J2327/06
Inventor 赵琳刘宝东高悦周爱存陈福新桑兆虎苏永学杜建军赵丽颖刘黎王峰周云飞李德军刘洋李明徐建玲孔令媛乔梁吕彦玲赵亮张克强鲍雷雷刘思佳陈国超
Owner TANGSHAN SANYOU CHLOR ALKALI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com