Polishing rear treatment method for plastic rattan for rattan-weaved products

A post-processing and weaving technology, which is applied in the field of grinding and post-processing of plastic rattan for rattan weaving products, can solve the problems of insufficient smoothness, and achieve the effect of increasing smoothness and non-corrosiveness.

Inactive Publication Date: 2017-09-01
安徽持家汉家居工艺品有限公司
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The current plastic rattan will be polished before weaving to make its surface smoother and more beautiful. Because the surface of the polished plastic rattan will have many burrs more or less, making its smoothness not enough, so further processing is needed

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polishing rear treatment method for plastic rattan for rattan-weaved products
  • Polishing rear treatment method for plastic rattan for rattan-weaved products

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A method for post-polishing plastic rattan for rattan products, specifically comprising the following steps:

[0022] (1) Soak the plastic rattan in the soaking solution for 4-10 hours, then take out the plastic rattan and expose it to the sun for 1 day, then soak it in the soaking solution for 4-10 hours, and send it directly to the cold storage at -10°C after soaking Freeze for 10 hours;

[0023] The soaking solution is made from the following raw materials in parts by weight:

[0024] 4 parts of protocatechuic acid, 4 parts of β-terpinene, 2.5 parts of myristic acid, 8 parts of gallic acid, 1.5 parts of isoquercitrin, 1.5 parts of p-cymene, N-phenyl-2-naphthalene 6 parts of amine and 230 parts of water. The preparation method is to mix the raw materials and then stir them evenly in a mixer. The stirring speed is 2500r / min, the stirring temperature is 50-60°C, and the time is 10 minutes;

[0025] (2) Take out the plastic rattan and thaw it with a tea polyphenol solu...

Embodiment 2

[0031] A method for post-polishing plastic rattan for rattan products, specifically comprising the following steps:

[0032] (1) Soak the plastic rattan in the soaking solution for 4-10 hours, then take out the plastic rattan and expose it to the sun for 1 day, then soak it in the soaking solution for 4-10 hours, and send it directly to the cold storage at -10°C after soaking Freeze for 10 hours;

[0033] The soaking solution is made from the following raw materials in parts by weight:

[0034] 3 parts of protocatechuic acid, 3 parts of β-terpinene, 2 parts of myristic acid, 5 parts of gallic acid, 1 part of isoquercitrin, 1 part of p-cymene, N-phenyl-2-naphthalene 4 parts of amine and 200 parts of water. The preparation method is to mix the raw materials and then stir them evenly in a mixer. The stirring speed is 2500r / min, the stirring temperature is 50-60°C, and the time is 10 minutes;

[0035] (2) Take out the plastic rattan and thaw it with a tea polyphenol solution at ...

Embodiment 3

[0041] A method for post-polishing plastic rattan for rattan products, specifically comprising the following steps:

[0042] (1) Soak the plastic rattan in the soaking solution for 4-10 hours, then take out the plastic rattan and expose it to the sun for 1 day, then soak it in the soaking solution for 4-10 hours, and send it directly to the freezer at -10°C after soaking Freeze for 10 hours;

[0043] The soaking solution is made from the following raw materials in parts by weight:

[0044] 5 parts of protocatechuic acid, 5 parts of β-terpinene, 3 parts of myristic acid, 10 parts of gallic acid, 2 parts of isoquercitrin, 2 parts of p-cymene, N-phenyl-2-naphthalene 8 parts of amine and 260 parts of water. The preparation method is to mix the raw materials and then stir them evenly in a mixer. The stirring speed is 2500r / min, the stirring temperature is 50-60°C, and the time is 10 minutes;

[0045] (2) Take out the plastic rattan and thaw it with a tea polyphenol solution at 40...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a polishing rear treatment method for plastic rattan for rattan-weaved products. The method specifically comprises the following steps that the plastic rattan is immersed in immersing liquid for 4-10 h; the plastic rattan is taken out and unfrozen through a tea polyphenol solution with the temperature ranging from 40 DEG C to 50 DEG C, and then the plastic rattan is immersed in a potassium hydroxide solution with the concentration being 4.4%; the plastic rattan is taken out and completely washed through deionized water and is covered with vinasse to be placed in the environment with the temperature ranging from 25 DEG C to 30 DEG C and the relative humidity being 50%-60%, and the plastic rattan is completely washed through purified water after one month; and the plastic rattan is taken out, the surface of the plastic rattan is coated with tendril-leaved fritillary bulb loquat leaf extracts, after the tendril-leaved fritillary bulb loquat leaf extracts are dried, the plastic rattan is aired under the sun for 3-5 days, the plastic rattan is placed in water to be decocted, and the plastic rattan is taken out and is completely washed and dried. According to the treatment method, burrs on the surface of the plastic rattan can be removed, the smoothness of the plastic rattan is improved, the plastic rattan surface attaching force is small, and dirt adhering is not likely to happen; and plastic smells of the plastic rattan can be removed, meanwhile, corrosivity is avoided in the treatment process, and hazardous substances are not generated.

Description

technical field [0001] The invention relates to the technical field of plastic rattan treatment, in particular to a post-polishing treatment method of plastic rattan for rattan products. Background technique [0002] Rattan weaving generally goes through more than a dozen processes such as rattan cutting (removing knots and scars on rattan), picking rattan, washing rattan, drying rattan, pulling rattan, pulling rattan (planing rattan), cutting rattan, bleaching, dyeing, weaving, and painting. . Rattan weaving is mainly made of rattan branches, rattan core or bamboo as the skeleton, and then woven with rattan bark or young rattan core, giving full play to the characteristics of rattan which is soft and not easy to break. [0003] In terms of color, most of them use the light yellow of the original rattan, or process and bleach it to white or ivory, which looks soft and elegant, and some are matched with coffee and brown. Rattan furniture is made of thick rattan as the skele...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine