A kind of method for preparing polypropylene foam material by irradiation cross-linking technology

A technology for irradiating polypropylene and foaming materials, which is applied in the field of preparing polypropylene foaming materials, can solve the problems of poor foaming quality and high foaming temperature, and achieves easy foaming process, low foaming temperature, and avoidance of inconvenience. uniform effect

Active Publication Date: 2018-04-06
广州华大生物科技有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This invention belongs to the chemical foaming method, which also has the problems of high foaming temperature (above 160°C) and poor foaming quality

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] Prepare the polypropylene foam material according to the following steps:

[0046] (1) Add polypropylene to xylene, heat to 50°C and stir until completely dissolved, add N-hexadecyl borate diethanolamine with a mass ratio of 3:1:80, fluorosilicon surface An emulsifier aqueous solution mixed with active agent and water, the mass ratio of polypropylene, N-hexadecyl borate diethanolamine ester, and fluorosilicon surfactant is 50:3:1, stir and emulsify at 50°C for 4 hours, stop After stirring, it was allowed to stand at room temperature for 12 hours, and the xylene was evaporated under reduced pressure to obtain a polypropylene emulsion;

[0047] (2) Add PETA dropwise to the polypropylene emulsion obtained in step (1) under stirring, the mass ratio of PETA to polypropylene emulsion is 1:30, continue to stir for 1 hour after the dropwise addition, stop stirring and leave it at room temperature for 12 hour to get the mixed emulsion, put the mixed emulsion into the irradiatio...

Embodiment 2

[0050] Prepare the polypropylene foam material according to the following steps:

[0051] (1) Add polypropylene to xylene, heat to 50°C and stir until completely dissolved, add N-hexadecyl borate diethanolamine with a mass ratio of 3:1:80, fluorosilicon surface An emulsifier aqueous solution mixed with active agent and water, the mass ratio of polypropylene, N-hexadecyl borate diethanolamine ester, and fluorosilicon surfactant is 50:3:1, stir and emulsify at 50°C for 4 hours, stop After stirring, it was allowed to stand at room temperature for 12 hours, and the xylene was evaporated under reduced pressure to obtain a polypropylene emulsion;

[0052] (2) Add PETA dropwise to the polypropylene emulsion obtained in step (1) under stirring, the mass ratio of PETA to polypropylene emulsion is 1:30, continue to stir for 1 hour after the dropwise addition, stop stirring and leave it at room temperature for 12 hour to get the mixed emulsion, put the mixed emulsion into the irradiatio...

Embodiment 3

[0055] Prepare the polypropylene foam material according to the following steps:

[0056] (1) Add polypropylene to xylene, heat to 50°C and stir until completely dissolved, add N-hexadecyl borate diethanolamine with a mass ratio of 3:1:80, fluorosilicon surface An emulsifier aqueous solution mixed with active agent and water, the mass ratio of polypropylene, N-hexadecyl borate diethanolamine ester, and fluorosilicon surfactant is 50:3:1, stir and emulsify at 50°C for 4 hours, stop After stirring, it was allowed to stand at room temperature for 12 hours, and the xylene was evaporated under reduced pressure to obtain a polypropylene emulsion;

[0057] (2) Add PETA dropwise to the polypropylene emulsion obtained in step (1) under stirring, the mass ratio of PETA to polypropylene emulsion is 1:30, continue to stir for 1 hour after the dropwise addition, stop stirring and leave it at room temperature for 12 hour to get the mixed emulsion, put the mixed emulsion into the irradiatio...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a method for preparing polypropylene foam material by irradiation cross-linking technology, comprising the following steps: (1) adding polypropylene into xylene, heating and stirring until completely dissolved, adding an emulsifier aqueous solution dropwise, stirring and emulsifying , stand still at room temperature after stopping stirring, obtain polypropylene emulsion after decompressing to remove xylene; Put it into an irradiation tube, put it into a 60Co irradiation device for irradiation to obtain irradiated polypropylene; (3) melt and plasticize the irradiated polypropylene, and then transfer to co-rotating twin-screw extrusion In the feeding port of the extruder, carbon dioxide is added to the gas injection port of the co-rotating twin-screw extruder for continuous extrusion and foaming to obtain a polypropylene foam material. The invention can prepare polypropylene foam material with better foaming quality, and has the advantages of lower energy consumption and less pollution.

Description

technical field [0001] The invention relates to a method for preparing polypropylene foam material. Background technique [0002] my country is a developing country, facing huge development pressure, the continuous growth of population and economy and the improvement of people's living standards will inevitably lead to an increase in the growth rate of energy consumption. The reliance on high-carbon energy coal cannot be changed in the short term, coupled with the lack of technology and funds required for emission reduction, and the large scale of "transferred emissions" from developed countries as the "world factory" all determine China's Before 2020, reducing the total amount of greenhouse gas emissions is under enormous pressure, and developing a low-carbon economy with Chinese characteristics is the direction of my country's sustainable development strategy in the future. [0003] Future energy conservation and emission reduction will focus on the production of clean ene...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08J3/24C08J9/12C08J3/11C08J3/07C08L23/12C08K5/55
CPCC08J3/07C08J3/11C08J3/24C08J9/122C08J2203/08C08J2323/12C08K5/55C08K2201/017C08L2201/02C08L2201/04C08L23/12
Inventor 万利秀邹伟权辜英杰彭志刚
Owner 广州华大生物科技有限公司
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com